稀土永磁材料基体与镀锌层结合力的研究
|
Abstract:
改善镀层与基体结合力的方法报道很多，多数通过优化前处理工艺来达到结合力要求。本文先采用硫酸盐镀锌工艺在永磁材料表面电镀一层底锌，然后采用钾盐镀锌工艺再电镀一层表锌。本方法得到的镀层结合力良好，满足了实际生产的要求。
While a large number of methods have been reported to improve the bonding force of coating and substrate, most of which can be achieved by optimizing the pretreatment process. In this paper, the surface of permanent magnetic material was electroplated with a layer of zinc base by sulfate galvanizing process, and then a layer of surface zinc was electroplated by potassium salt galvanizing process. The coating adhesion obtained by this method is good, which meets the requirements of actual production.
| [1] | 邓志伟, 张友亮, 张守华. 钕铁硼产品研磨倒角工艺优化[J]. 当代化工研究, 2022(15): 180-182. |
| [2] | 谢连刚, 孔令凯, 张健. 酸洗液酸洗能力控制方法的研究[J]. 广东化工, 2022, 49(13): 37-39. |
| [3] | 邓志伟, 张守华, 张友亮. 原子发射光谱法测定草酸稀土沉淀中的钕含量[J]. 当代化工研究, 2021(13): 42-43. |
| [4] | 覃奇贤, 刘淑兰. 镀层与基体的结合力[J]. 电镀与精饰, 2010, 32(1): 34-36. |
| [5] | 曲敬信, 汪泓宏. 表面工程手册[M]. 北京: 化学工业出版社, 1998: 873, 885. |
| [6] | 沈品华, 屠振密. 锌及锌合金[M]. 北京: 机械工业出版社, 2001: 15. |
| [7] | 张友亮, 李滨, 张蒙, 等. 钕铁硼永磁材料沙镍工艺研究[J]. 信息记录材料, 2021, 22(7): 23-25. |
| [8] | 张宏杰, 温茂远, 侯振, 等. 测定结晶器涂镀层结合力的探讨[C]//2013年连铸新技术及关键耐材长寿化学术研讨会. 2013年连铸新技术及关键耐材长寿化学术研讨会论文集. 青岛: 中国金属学会, 2013: 84-90. |
| [9] | 朱峰, 伍超群, 唐维学. 金相分析系统在金相定量分析中的应用[J]. 材料研究与应用, 2007, 4(4): 318-320. |