不同抛光工具对氧化锆抛光效果的比较研究
|
Abstract:
摘要 目的:研究不同抛光工具对氧化锆抛光后表面性能的影响。方法:制作氧化锆标准试件(13 mm×10 mm×3 mm),随机选取40个分成5组(n=8):A组(空白对照组)、B组(阴性对照组)、C组(松风组)、D组(固美组)、E组(EVE组)。测试各组试件每级处理后的Ra值及每组试件的维氏硬度值,扫描电镜下观察每组试件处理后的表面形态。结果:氧化锆试件经表面处理后各组Ra值之间不完全相同,差异有统计学意义(F=273.200,P=0.000);各组Ra值从低到高依次为:E
| [1] | 郭彬, 谢伟丽, 刘一志,等.不同形态的氧化锆陶瓷桩对牙本质应力的三维有限元分析[J].口腔医学研究,2015,31 (11)∶1104-1107 |
| [2] | Subasi MG,Demir N,Kara O,et al. Mechanical properties of zirconia after different surface treatments and repeated firings [J].J Adv Prosthodont,2014,6(6)∶462-467 |
| [3] | Awad D,Stawarczyk B,Liebermann A,et al.Translucency of esthetic dental restorative CAD/CAM materials and composite resins with respect to thickness and surface roughness [J]. J Prosthet Dent,2015,113(6)∶534-540 |
| [4] | Kawai K,Urano M,Ebisu S.Effect of surface roughness of porcelain on adhesion of bacteria and their synthesizing glucans [J]. J Prosthet Dent,2000,83(6)∶664-667 |
| [5] | Han GJ,Kim JH,Lee MA,et al.Performance of a novel polishing rubber wheel in improving surface roughness of feldspathic porcelain [J]. Dent Master J,2014,33(6)∶739-748 |
| [6] | 张凯, 吴凤鸣.表面抛光和上釉对Y-TZP全瓷表面粗糙度及磨耗性能的影响[J].口腔医学,2017,37(10)∶914-917 |
| [7] | 李新,苏乃川,廖运茂.不同条件的表面喷砂对牙科氧化锆材料表面丧失的影响[J].口腔医学,2016,36(1)∶28-32 |
| [8] | 王萍,马骏驰,胡建.椅旁CAD/CAM(CEREC ACTM)全瓷修复的临床回顾性研究[J].口腔医学,2016,36(12)∶1098-1103 |
| [9] | 郭震威. 不同抛光工具对e.max CAD玻璃陶瓷抛光效果的比较研究[D].郑州大学, 2017 |
| [10] | Kim MJ,Oh SH,Kim JH,et al.Wear evaluation of the human enamel opposing different Y-TZP dental ceramics and other porcelains [J]. J Dent,2012,40(11)∶979-988 |
| [11] | General Administration of Quality Supervision, Inspection and Quarantine of the People’s Republic of China, Standardization Administration of the People’s Republic of China.Geometrical product specifi cations (GPS)-surface texture:profile method-surface roughness parameters and their values. GB/T 1031-2009 [S]. Beijing: China Standards Press, 2009∶2-5 |
| [12] | 赵鑫. 牙科陶瓷磨抛后表面性状的实验研究[D].第四军医大学,2007 |
| [13] | Huang SZ, Ding B,Zou FP,et al.Influence of test loads on errors of vickers-hardness test [J]. Physical Testing & Chemical Analysis,2014,50(2)∶127-130 |
| [14] | Traini T, Gherlone E, Parabita SF, et al. Fracture toughness and hardness of a Y-TZP dental ceramic after mechanical surface treatments [J]. Clin Oral Investig, 2014, 18(3)∶707-714 |
| [15] | Maerten A, Zaslansky P, Mochales C, et al. Characterizing the transformation near indents and cracks in clinically used dental yttria-stabilized zirconium oxide constructs [J]. Dent Mater, 2013, 29(2)∶241-251 |