一步法制备含扩散阻挡层的多层体系及其界面结合强度
DOI: DOI:10.3724/SP.J.1037.2009.00472, PP. 561-568
Keywords: 扩散阻挡层,涂层,抗氧化,结合强度,一步沉积法
Abstract:
为抑制合金元素的互扩散,在Ni-Cr-Al-Y-Si涂层和DSM11基体间通过电弧离子镀技术一步制备了含扩散阻挡层(DB)和黏结层(BC)的多层体系Ni-Cr-Al-Y-Si/DB/BC/DSM11.由恒温氧化、循环氧化和粘胶拉伸实验考察了涂层的抗氧化性、DB阻挡元素扩散能力和体系的界面结合强度.结果表明,含扩散阻挡层的多层能很好地保护基体材料,经过1050℃恒温氧化100h后,试样表面形成连续致密的Al2O3膜,外层中仅检测到微量的来自基体的合金元素;经过1050℃？室温(RT)循环氧化100cyc后,DB与两侧材料的结合保持良好.退火多层体系的界面结合强度达到63.6MPa,比不连续法制备的Ni-Cr-Al-Y/Cr-O-N/DSM11体系提高了约20MPa.一步法制备能提高含扩散阻挡层多层体系的界面结合强度,DB在恒温和循环氧化过程中能保持很好的抑制元素扩散的能力.
| [1] | Knotek O, Loffler F, Beele W. Surf Coat Technol, 1993; 61: 6
|
| [2] | Li S S, Song J X, Zhou C G, Gong S K, Han Y F. Intermetallics, 2005; 13: 309
|
| [3] | Sloof W G. Self Healing in Coating at High Temperatures: Self Healing Materials. Netherlands: Springer, 2007: 309
|
| [4] | Nicholls J R. MRS Bull, 2003; 28: 659
|
| [5] | Wang Q M,Wu Y N, Ji A L, Ke P L, Sun C, Huang R F, Wen L S. Acta Metall Sin, 2004; 40: 83
|
| [6] | (王启民, 武颖娜, 纪爱玲, 柯培玲, 孙超, 黄荣芳, 闻立时. 金属学报, 2004; 40: 83)
|
| [7] | Li W Z, Yao Y, Wang Q M, Bao Z B, Gong J, Sun C, Jiang X. J Mater Res, 2008; 23: 341
|
| [8] | Li W Z, Yao Y, Li Y Q, Li J B, Gong J, Sun C, Jiang X. Mater Sci Eng, 2009; A512: 117
|
| [9] | Yao Y, Li W Z, Wang Q M, Gong J, Sun C, Li J B. Acta Metall Sin, 2008; 44: 876
|
| [10] | (姚勇, 李伟洲, 王启民, 宫骏, 孙 超, 李家宝. 金属学报, 2008; 44: 876)
|
| [11] | Zhang K, Wang Q M, Sun C, Wang F H. Corros Sci, 2008; 50: 1707
|
| [12] | Sun C, Wang Q M, Tang Y J, Guan Q F, Gong J, Wen L S. Acta Metall Sin, 2005; 41: 1167
|
| [13] | (孙超, 王启民, 唐永吉, 关庆丰, 宫 骏, 闻立时. 金属学报. 2005; 41: 1167)
|
| [14] | Ren X, Wang F H. Surf Coat Technol, 2006; 201: 30
|
| [15] | Yao Y. Master Dissertation. Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 2008
|
| [16] | (姚勇. 中国科学院金属研究所硕士学位论文, 沈阳, 2008)
|
| [17] | Peng X, Wang F H, Clark D K. Acta Metall Sin, 2003; 39: 1055
|
| [18] | (彭 晓, 王福会, Clarke D R. 金属学报. 2003; 39: 1055)
|
| [19] | Cremer R, Witthaut M, Reichert K, Schierling M, Neuschutz D. Surf Coat Technol, 1998; 108-109: 48
|
| [20] | Xie L, Sohn Y, Jordan E H, Gell M. Surf Coat Technol, 2003; 176: 57
|
| [21] | Evans A G, Mumm D R, Hutchinson J W, Meier G H, Pettit F S. Prog Mater Sci, 2001; 46: 505
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|