铝镇静钢LF低氟精炼渣系的脱硫实验研究
Experiment Study on Desulfurization of Low-Fluoride LF Refining Slag for Aluminum Killed Steel

DOI: 10.12677/MEng.2015.21007, PP. 42-48

Keywords: LF精炼，脱硫，粘度，铝镇静钢，Li₂O
LF Refining, Desulphurization, Viscosity, Aluminum Killed Steel, Li₂O

Full-Text   Cite this paper   Add to My Lib

Abstract:

本文采用CaO-Al₂O₃-SiO₂-MgO-CaF₂基础渣系，以Li₂O替代CaF₂，进行铝镇静钢LF脱硫实验。研究结果表明：渣中CaF₂经Li₂O替代后，在1500℃时，CaO (55.8%)-Al₂O₃ (20%)-SiO₂ (11.2%)-MgO (10%)-Li₂O (3%)渣的粘度低于0.3 Pa？s，渣的流动性能良好；温度1600℃、渣金比1:10时，该渣脱硫率77.14% (脱硫之前采用铝脱氧)，钢水硫含量能降到0.008%。随着渣中Li₂O含量的增加，脱硫率升高，最高可达80%。
Desulfurization efficiency of CaO-Al₂O₃-SiO₂-MgO-CaF₂ slag for Al-killed steel was studied with Li₂O replacing CaF₂. Experimental results show that at 1500？C, the viscosity of CaO (55.8%)-Al₂O₃ (20%)-SiO₂ (11.2%)-MgO (10%)-Li₂O (3%) slag is lower than 0.3 Pa？s, having good flow properties; at 1600？C, under the condition of slag-metal ratio of 1:10, desulfurization rate of the slag can reach 77.14%, and sulfur content in steel decreases to 0.008%. Desulfurization rate can even reach to 80% with Li₂O content increasing in slag after composition optimization.

References

[1]	杨叠, 王新华, 秦颐鸣, 邓小旋, 杨文 (2003) BOF-LF-CSP工艺低碳铝镇静钢精炼过程的夹杂物变化. 北京科技大学学报, 6, 580-581.
[2]	高泽平 (2001) 炉外精炼教程. 冶金工业出版社, 北京, 116-117.
[3]	Mizukami, H., Ishikawa, M. and Hirat, T. (2004) Dissolution mechanism of fluorine in aqueous solution from fluorine containing synthetic slag. ISIJ International, 44, 623-629.
[4]	黄希祜 (2002) 钢铁冶金原理. 冶金工业出版社, 北京, 380-383.
[5]	祝贞学, 王宏明, 李桂荣, 戴起勋, 黄成兵 (2006) Li2O和B2O3对精炼渣脱硫性能影响的实验研究. 上海金属, 1, 19-23.
[6]	Shahbazian, F., Sichen, D. and Seetharaman, S. (2002) The effect of adition of Al2O3 on the viscosity of CaO-FeO-SiO2- CaF2 slags. ISIJ International, 42, 155-162.
[7]	Behera, R.C. and Monhanty, U.K. (2001) Vsicosity of molten Al2O3-Cr2O3-CaO-CaF2 slags at various Al2O3/CaO ratios. ISIJ Internationa, 41, 834-839.

Full-Text