Structural and magnetic characterization of (Ba,Sr)-hexaferrite Powders

Results on magnetic and structural characterization of ferrimagnetic compounds of BaxSr1-xFe12O19 (x=0.0, 0.25, 0.50, 0.75 and 1.0) prepared by the conventional ceramic method are reported. The samples were systematically examined using atomic force microscopy (AFM), X-ray diffraction and vibrating sample magnetometer. Structural and magnetic differences among the specimens were observed. The relations between structural features and magnetic properties are discussed. The presintering temperatures of the samples were 800°C and 1,000°C. The specimens were sintered at 1,200°C for one hour. Se presentan resultados de la caracterización estructural y magnética de compuestos ferrimagnéticos BaxSr1-xFe12O19 (x=0,0, 0,25, 0,50, 0,75 y 1,0) preparados por el método cerámico convencional. Las muestras fueron examinadas por microscopía de fuerza atómica, difracción de rayos X y magnetometría de muestra vibrante. Se observaron diferencias tanto estructurales como magnéticas en las muestras analizadas. Se discuten las relaciones entre los aspectos estructurales y los parámetros magnéticos medidos. Las temperaturas de presinterización de las muestras fueron de 800°C y 1.000°C y fueron sinterizadas a 1.200°C durante una hora.