%T Structural and magnetic characterization of (Ba,Sr)-hexaferrite Powders
%A Palomares-S¨¢nchez
%A S.
%A Ponce-Casta£¿eda
%A S.
%A Ruiz
%A F.
%A Mirabal-Garc¨ªa
%A M.
%J Revista de Metalurgia
%D 1999
%I Consejo Superior de Investigaciones Cient¨ªficas
%X Results on magnetic and structural characterization of ferrimagnetic compounds of BaxSr1-xFe12O19 (x=0.0, 0.25, 0.50, 0.75 and 1.0) prepared by the conventional ceramic method are reported. The samples were systematically examined using atomic force microscopy (AFM), X-ray diffraction and vibrating sample magnetometer. Structural and magnetic differences among the specimens were observed. The relations between structural features and magnetic properties are discussed. The presintering temperatures of the samples were 800¡ãC and 1,000¡ãC. The specimens were sintered at 1,200¡ãC for one hour. Se presentan resultados de la caracterizaci¨®n estructural y magn¨¦tica de compuestos ferrimagn¨¦ticos BaxSr1-xFe12O19 (x=0,0, 0,25, 0,50, 0,75 y 1,0) preparados por el m¨¦todo cer¨¢mico convencional. Las muestras fueron examinadas por microscop¨ªa de fuerza at¨®mica, difracci¨®n de rayos X y magnetometr¨ªa de muestra vibrante. Se observaron diferencias tanto estructurales como magn¨¦ticas en las muestras analizadas. Se discuten las relaciones entre los aspectos estructurales y los par¨¢metros magn¨¦ticos medidos. Las temperaturas de presinterizaci¨®n de las muestras fueron de 800¡ãC y 1.000¡ãC y fueron sinterizadas a 1.200¡ãC durante una hora.
%K Ferrites
%K Ceramics
%K Magnetic properties
%K Atomic force microscopy
%K Ferritas
%K Cer¨¢micos
%K Propiedades magn¨¦ticas
%K Microscop¨ªa de fuerza at¨®mica
%U http://revistademetalurgia.revistas.csic.es/index.php/revistademetalurgia/article/view/617/627