Aleación superficial de superaleaciones base níquel mediante láser

Ni based superalloys present a high oxidation resistance at high temperature as well as good mechanical properties. But new tecnhology developments forcé to research in this materials to improve their properties at high temperature. In this work, two Ni based superalloys (Nimonic 80A and Inconel 600) were surface alloyed with aluminium using a high power laser. SEM and EDX were used to study the microstructure of the obtained coatings. Alloyed specimens were tested at 1.273 K between 24 and 250 h. Results showed the generation of a protective and continuous coating of alumina on the laser treated specimens surface that can improve oxidation resistance. Las superaleaciones base níquel presentan una elevada resistencia a la oxidación a alta temperatura, así como excelentes propiedades mecánicas. Los nuevos desarrollos tecnológicos (condiciones cada vez más agresivas) obligan a una casi continua modificación de dichas aleaciones. En el presente trabajo, dos superaleaciones base níquel (Nimonic 80A e Inconel 600) se alean superficialmente con aluminio utilizando un láser de alta potencia. Se estudia la microestructura de la capas obtenidas mediante SEM y EDX. Se realizan ensayos de oxidación a 1.273 K sobre las probetas aleadas y sobre el material base durante tiempos variables entre 24 y 250 h. Los resultados indican la formación de una capa protectora de alúmina sobre las probetas aleadas que puede incrementar la resistencia a la oxidación.