%X Ni based superalloys present a high oxidation resistance at high temperature as well as good mechanical properties. But new tecnhology developments forc谷 to research in this materials to improve their properties at high temperature. In this work, two Ni based superalloys (Nimonic 80A and Inconel 600) were surface alloyed with aluminium using a high power laser. SEM and EDX were used to study the microstructure of the obtained coatings. Alloyed specimens were tested at 1.273 K between 24 and 250 h. Results showed the generation of a protective and continuous coating of alumina on the laser treated specimens surface that can improve oxidation resistance. Las superaleaciones base n赤quel presentan una elevada resistencia a la oxidaci車n a alta temperatura, as赤 como excelentes propiedades mec芍nicas. Los nuevos desarrollos tecnol車gicos (condiciones cada vez m芍s agresivas) obligan a una casi continua modificaci車n de dichas aleaciones. En el presente trabajo, dos superaleaciones base n赤quel (Nimonic 80A e Inconel 600) se alean superficialmente con aluminio utilizando un l芍ser de alta potencia. Se estudia la microestructura de la capas obtenidas mediante SEM y EDX. Se realizan ensayos de oxidaci車n a 1.273 K sobre las probetas aleadas y sobre el material base durante tiempos variables entre 24 y 250 h. Los resultados indican la formaci車n de una capa protectora de al迆mina sobre las probetas aleadas que puede incrementar la resistencia a la oxidaci車n.
%K Laser treatments
%K Oxidation
%K Superalloys
%K Aleaci車n l芍ser
%K Oxidaci車n
%K Superaleaciones
%U http://revistademetalurgia.revistas.csic.es/index.php/revistademetalurgia/article/view/684/696