磨细钢渣粉和矿渣粉复掺对C60高性能混凝土性能的影响
|
Abstract:
使用磨细钢渣粉和矿渣粉复掺制备C60高性能混凝土，研究磨细钢渣粉和矿渣粉两者复掺或单掺对C60高性能混凝土抗压强度和抗渗性能的影响。试验结果：与单掺磨细钢渣粉相比、与单掺矿渣粉相比，磨细钢渣粉和矿渣粉两者复掺时，其C60高性能混凝土的抗压强度和抗渗性能最佳，单掺矿渣粉的次之，单掺磨细钢渣粉的最差。
C60 high-performance concrete was prepared by mixing fine steel slag powder and slag powder, and the effects of compound or single doping of ground steel slag powder and slag powder on the compressive strength and impermeability of C60 high-performance concrete were studied. Test re-sults: Compared with single-doped fine steel slag powder and single-doped slag powder, when the grinding fine steel slag powder and slag powder are mixed together, the compressive strength and impermeability of C60 high-performance concrete are the best, followed by single-doped slag pow-der, and the single-doped fine steel slag powder is the worst.
| [1] | 朱训国, 王利芬, 赵双, 王兆毅, 何传琪, 刘星池. 钢渣混凝抗冻与抗渗性能研究[J]. 四川建筑科学研究, 2019, 45(3): 106-109. |
| [2] | 高志扬, 王圣文, 吕兴栋, 李响, 蒋科. 钢渣粉-水泥复合体系水化热及动力学研究[J]. 长江科学院院报, 2018, 35(12): 138-142. |
| [3] | 张孜孜. 安定性良好的高活性钢渣制备及其性能研究[D]: [硕士学位论文]. 唐山: 华北理工大学, 2018. |
| [4] | 宋凯强, 刘福田. 钢渣微粉与矿渣粉对混凝土性能及水化机理的影响研究[J]. 水泥工程, 2015(4): 76-80. |
| [5] | 李志军, 侍克斌, 努尔开力.依孜特罗甫. 锂渣、钢渣高性能混凝土早期抗裂性能试验研究[J]. 混凝土, 2013(2): 25-27. |
| [6] | 周白露, 丁华柱, 陈乔, 刘围. 磨细钢渣粉对混凝土力学性能的影响[J]. 粉煤灰, 2016(6): 13-15. |
| [7] | 王戎. 钢渣粉对混凝土性能的影响[J]. 山东农业大学学报, 2019, 6(2): 221-224. |
| [8] | 刘智伟. 电炉钢渣铁组分回收及尾泥制备水泥材料的技术基础研究[D]: [博士学位论文]. 北京: 北京科技大学, 2016. |
| [9] | 程岚. 双掺秸秆灰钢渣绿色混凝土配合比设计及性能研究[D]: [硕士学位论文]. 张家口: 河北建筑工程学院, 2019. |
| [10] | 张朝晖, 廖杰龙, 巨建涛, 等. 钢渣处理工艺与国内外钢渣利用技术[J]. 钢铁研究学报, 2013, 25(7): 1-4. |
| [11] | 李鹏冠, 赵风清. 保持高胶凝活性的钢渣安定性处理工艺[J]. 钢铁研究学报, 2016, 28(7): 26-31. |