紫外光吸收剂插层蒙脱土改性沥青的流变性能
|
Abstract:
本文通过对钠基蒙脱土(Na-MMT)进行处理得到有机蒙脱土(OMMT);选用不同紫外光吸收剂(UV326、UV328、UV531和UV770),采用插层复合的方法制备得到紫外光吸收剂插层有机蒙脱土(UVA/OMMT);以UVA/OMMT为改性剂对沥青进行改性,并评价了UVA/OMMT改性沥青的动态剪切流变性能。结果表明,不同类型UVA/OMMT的加入均使沥青的复数剪切模量(G*)和车辙因子增大,而相位角(δ)减小。UVA/OMMT可显著提高沥青抵抗高温变形的能力。
The organic montmorillonite (OMMT) was prepared by intercalation of Na-montmorillonite (Na-MMT) and organic intercalator. Then the ultraviolet absorber (UVA) intercalated organic montmorillonite (UVA/OMMT) was designed with different UVAs (UV326, UV328, UV531 and UV770) and OMMT. The UVA/OMMT modified asphalt was then prepared via melt blending. The rheological properties of different UVA/OMMT modified asphalt were studied by the dynamic shear rheometer (DSR). Results show that the complex shear modulus and the rutting factor of asphalt were increased, while the phase angle was decreased with the addition of UVA/OMMT. The high temperature stability of asphalt was improved by adding different types of UVA/OMMT.
[1] | [1]J.Y., Liang, Y.S. and Feng, Z.G. (2011) Investigation of Ultraviolet Aging on Rheological Characteristics of Bitumen. Applied Mechanics and Materials, 71-78, 1954-1957. |
[2] | https://doi.org/10.4028/www.scientific.net/AMM.71-78.1954 |
[3] | 栗培龙. 道路沥青老化行为与机理研究[D]: [硕士学位论文]. 西安: 长安大学, 2007. |
[4] | 曾文博. 沥青紫外老化机理及其表征方法研究[D]: [博士学位论文]. 武汉: 武汉理工大学, 2017. |
[5] | 万淼. 沥青老化及基于组分调和的再生机制研究[D]: [硕士学位论文]. 武汉: 武汉理工大学, 2017. |
[6] | 冯振刚. 紫外光吸收剂对沥青性能的影响及其作用机理研究[D]: [博士学位论文]. 武汉: 武汉理工大学, 2013. |
[7] | 时敬涛, 王子立, 李永振, 等. 紫外光吸收剂对苯乙烯-丁二烯-苯乙烯三嵌段共聚物改性沥青光老化的影响[J]. 化工新型材料, 2018, 46(5): 148-150+153. |
[8] | 洪岭岭, 刘朝晖, 冯国杰, 等. 紫外光吸收剂对不同嵌段比SBS改性沥青性能的影响[J]. 武汉理工大学学报, 2017, 39(1): 28-36. |
[9] | 化高伟. 抗紫外光添加剂对改善沥青及沥青混合料路用性能的对比研究[D]: [硕士学位论文]. 西安: 西安建筑科技大学, 2015. |
[10] | Zhang, Z.P., Jia, M., Jiao, W.X., et al. (2018) Physical Properties and Microstructures of Organic Rectorites and Their Modified Asphalts. Construction and Building Materials, 171, 33-43. |
[11] | https://doi.org/10.1016/j.conbuildmat.2018.01.163 |
[12] | Vargas, M.A., Moreno, L., Montiel, R., et al. (2017) Effects of Montmorillonite (Mt) and Two Different Organo-Mt Additives on the Performance of Asphalt. Applied Clay Science, 139, 20-27. https://doi.org/10.1016/j.clay.2017.01.009 |
[13] | 刘涛. 纳米蒙脱土改性沥青老化自愈合性能及机理研究[D]: [硕士学位论文]. 呼和浩特: 内蒙古工业大学, 2018. |
[14] | 肖新颜, 张登科. 异佛尔酮二异氰酸酯改性蒙脱土改性沥青的性能[J]. 华南理工大学学报(自然科学版), 2017, 45(2): 116-121. |
[15] | 朱明广, 王迎春, 李志文, 等.有机蒙脱土对沥青抗紫外光老化性能影响的研究[J]. 中国建筑防水, 2017, 33(1): 6-9. |
[16] | 王华才. 沥青/有机化蒙脱土复合材料的结构及紫外老化研究[D]: [硕士学位论文]. 武汉: 武汉理工大学, 2010. |
[17] | 冯振刚, 张沛, 孙思敖, 等. 紫外光吸收剂插层蒙脱土对沥青老化性能的影响[J]. 建筑材料学报, 2020, 22(5): 1-7+12. |