氯化聚乙烯电缆料的配方优化

通过正交试验对氯化聚乙烯（CPE）电缆料配方进行优化，以CPE/三元乙丙橡胶（EPDM）为基相，硫化剂DCP/助交联剂TAIC为硫化体系、炭黑为补强剂，并配以适量的阻燃剂和增塑剂，制备阻燃型电缆料。结果表明：电缆料的最佳配方为CPE　70，EPDM　30，炭黑　10，氧化镁　5，抗氧剂　2，增塑剂DOP　5，硫化剂DCP　4，助交联剂TAIC　2.5，胶料综合性能较优，且满足电缆料要求。;The formulation of chlorinated polyethylene（CPE） cable compound was optimized through the orthogonal experiment test，the flame retardant cable compound was prepared with CPE/EPDM as based resin，DCP/TAIC as curing system，carbon black as reinforcing agent，and proper amount of flame retardant and plasticizer.The results showed that，the optimized formulation of cable compound was CPE　70，EPDM　30，carbon black　10，MgO　5，antioxidant　2，DOP　5，DCP　4，TAIC　2.5.The comprehensive properties of the optimized formulation compound were excellent and met the requirements of the cable compound