The brittle fracture mode close to the surface of Inconel 718 subsea bolts is closely related to their nanostructure. When the bolts are used subsea under cathodic protection, hydrogen evolves. Intergranular precipitates and points of intersection of slip lines always held responsible for hydrogen enhanced decohesion. However, thus far, little attention has been paid to the bolts manufacturing method and to the characterization of the role of subsurface oversized nanoprecipitates on transgranular surface cracking. As-received subsea bolts were analyzed using multi-scale observation techniques such as focused ion beam milling, scanning electron microscopy, transmission electron microscopy, and in-air strain rate tensile tests. The results further demonstrated that under identical API aging, there was a difference in the morphological precipitation and strength of 718 as a bolt and rectangular billet. For the 718 rectangular billets, discrete intergranular stable δ/MC carbides precipitate and only γ' of 10 - 20 nm was observed for the bulk and subsurface. Whereas, for the CRA subsea bolt, γ' was approximately 30 nm, γ\" was 30 - 50 nm for the bulk (370 HV); γ' was approximately 50 nm and γ\" was 50 - 100 nm at subsurface (400 HV). As-received subsea bolts were investigated at subsurface (10 μm from the surface) at the thread and shank region, which revealed transgranular sheared oversized ~50 nm γ' (with dislocation networks) and metastable γ\" > 100 nm particles, respectively. Thus, an effort was made to develop the hydrogen-assisted surface cracking theory for bolts.
References
[1]
DeBarbadillo, J.J. and Mannan, S.K. (2012) Alloy 718 for Oilfield Applications. JOM, 64, 265-270. https://doi.org/10.1007/s11837-012-0238-z
[2]
Rorvik, G., Kirkemo, F. and Haaland, B.O. (2014) Fasteners in Subsea Applications: End User Experiences and Requirements. Proceedings of the ASME 2014 33rd International Conference on Ocean, Offshore and Arctic Engineering, San Francisco, California, 8-13 June 2014, Paper No: OMAE2014-24520. https://doi.org/10.1115/OMAE2014-24520
[3]
Ferreira, P.J., Robertson, I.M. and Birnbaum, H.K. (1998) Hydrogen Effects on the Interaction between Dislocations. Acta Materialia, 46, 1749-1757. https://doi.org/10.1016/S1359-6454(97)00349-2
[4]
Sofronis, P. and Robertson, I.M. (2002) Transmission Electron Microscopy Observations and Micromechanical/Continuum Models for the Effect of Hydrogen on the Mechanical Behaviour of Metals. Philosophical Magazine A, 82, 3405-3413. https://doi.org/10.1080/01418610208240451
[5]
Oriani, R.A. (1972) A Mechanistic Theory of Hydrogen Embrittlement of Steels. Berichte der Bunsengesellschaft für physikalische Chemie, 76, 848-857.
[6]
Troiano, A.R. (1960) The Role of Hydrogen and Other Interstitials in the Mechanical Behavior of Metals. Transactions of the American Society of Metals, 52, 54-80.
[7]
API (2004) Specification of Nickel Base Alloy 718 (UNS N07718) for Oil and Gas Drilling and Production Equipment. American Petroleum Institute, Washington DC.
[8]
Rezende, M.C., Araujo, L.S., Gabriel, S.B., Dos Santos, D.S. and De Almeida, L.H. (2015) Hydrogen Embrittlement in Nickel-Based Superalloy 718: Relationship between γ’+ γ” Precipitation and the Fracture Mode. International Journal of Hydrogen Energy, 40, 17075-17083. https://doi.org/10.1016/j.ijhydene.2015.07.053
[9]
Liu, L., Tanaka, K., Hirose, A. and Kobayashi, K.F. (2002) Effects of Precipitation Phases on the Hydrogen Embrittlement Sensitivity of Inconel 718. Science and Technology of Advanced Materials, 3, 335-344. https://doi.org/10.1016/S1468-6996(02)00039-6
[10]
Nice, P., Strong, R., Bailey, W.M., Rorvik, G., Olsen, J.H. and Mobberley, T.G. (2014) Hydrogen Embrittlement Failure of a Precipitation Hardened Nickel Alloy Subsurface Safety Valve Component Installed in a North Sea Seawater Injection Well. NACE International, San Antonio.
[11]
Shademan, S.S., Martin, J.W. and Davis, A.P. (2012) UNS N07725 Nickel Alloy Connection Failure. NACE International, Houston.
[12]
Cassagne, T., Bonis, M., Hillis D. and Duret, C. (2008) Understanding Field Failure of Alloy 718 Forging Materials in HP/HT Wells. Proc. of EuroCorr, Edinburgh, European Federation of Corrosion, 7-11 September 2008, 1-13.
[13]
Oradei-Basile, A. and Radavich, J.F. (1991) A Current T-T-T Diagram for Wrought Alloy 718. In: Loria, E.A., Ed., Superalloys 718,625 and Various Derivatives, The Minerals, Metals, and Materials Society, Warrendale, 325-335. https://doi.org/10.7449/1991/Superalloys_1991_325_335
[14]
Saunders, N., Fahrmann, M. and Small, C.J. (2000) The Application of Calphad Calculations to Ni-Based Superalloys. In: Green, K.A., Pollock, T.M. and Kissinger, R.D., Eds., Superalloys 2000, TMS, Warrendale, 803.
[15]
Zhang, Z.B., Obasi, G., Morana, R. and Preuss, M. (2016) Hydrogen Assisted Crack Initiation and Propagation in a Nickel-Based Superalloy. Acta Materialia, 113, 272-283. https://doi.org/10.1016/j.actamat.2016.05.003
[16]
Tarzimoghadam, Z., Ponge, D., Klower, J. and Raabe, D. (2017) Hydrogen-Assisted Failure in Ni-based Superalloy 718 Studied Under in Situ Hydrogen Charging: The Role of Localized Deformation in Crack Propagation. Acta Materialia, 128, 365-374. https://doi.org/10.1016/j.actamat.2017.02.059
[17]
Demetriou, V., Robson, J.D., Preuss, M. and Morana, R. (2017) Study of the Effect of Hydrogen Charging on the tensile Properties and Microstructure of Four Variant Heat Treatments of Nickel Alloy 718. International Journal of Hydrogen Energy, 42, 23856-23870. https://doi.org/10.1016/j.ijhydene.2017.02.149
[18]
Mehl, M.E. and Lippold, J.C. (1997) Effect of δ Phase Precipitation on the Repair Weldability of Alloy 718. In: Loria, E.A., Ed., Superalloys 718,625, 706 and Various Derivatives, The Minerals, Metals, & Materials Society, Pittsburgh, 731-741. https://doi.org/10.7449/1997/Superalloys_1997_731_741
[19]
Cozar, R. and Pineau, A. (1973) Morphology of y’ and y” Precipitates and Thermal Stability of Inconel 718 Type Alloys. Metallurgical Transactions, 4, 47-59. https://doi.org/10.1007/BF02649604
[20]
Saleem, B., Dong, H.B. and Patel, V. (2019) Effect of Aging on the Strength of Corrosion-Resistant Incoloy Alloys 945 and 945X: A Microstructural Perspective. Materials Science and Engineering: A, 748, 327-336. https://doi.org/10.1016/j.msea.2019.01.114
[21]
Meng, C.G., Guo, J.T. and Hu, Z.Q. (1996) Relationship between Bonding Characteristics and Mechanical Properties of L12 Intermetallics. Journal of Alloys and Compounds, 237, 139-143. https://doi.org/10.1016/0925-8388(95)02027-6
[22]
Hagel, W.C. and Beattie, H.J. (1964) Iron and Steel Institute Special Report. Iron and Steel Institute, London, 98.
[23]
Niang, A., Viguier, B. and Lacaze, J. (2010) Some Features of an Isothermal Solid-State Transformations in Alloy 718. Materials Characterization, 61, 525-534. https://doi.org/10.1016/j.matchar.2010.02.011
[24]
Dehmas, M., Lacaze, J., Niang, A. and Viguier, B. (2011) TEM Study of High Temperature Precipitation of Delta Phase in Inconel 718 Alloy. Advances in Materials Science and Engineering, 2011, Article ID: 940634. https://doi.org/10.1155/2011/940634
[25]
Ramaswamy, V., Swann, P.R. and West, D.R.F. (1972) Observations on Intermetallic Compound and Carbide Precipitation in Two Commercial Nickel-Base Superalloys. Journal of the Less Common Metals, 27, 17-26. https://doi.org/10.1016/0022-5088(72)90100-2
[26]
Ghosh, S., Yadav, S. and Das, G. (2008) Study of Standard Heat Treatment on Mechanical Properties of Inconel 718 Using Ball Indentation Technique. Materials Letters, 62, 2619-2622. https://doi.org/10.1016/j.matlet.2008.01.001
[27]
Sims, C.T., Stoloff, N.S. and Hagel, W.C. (1987) Superalloys II. John Wiley & Sons, New York.
[28]
Fournier, L., Delafosse, D. and Magnin, T. (1999) Cathodic Hydrogen Embrittlement in Alloy 718. Materials Science and Engineering: A, 269, 111-119. https://doi.org/10.1016/S0921-5093(99)00167-7
[29]
Liu, L., Zhai, C., Lu, C., Ding, W., Hirose, A. and Kobayashi, K.F. (2005) Study of the Effect of δ Phase on Hydrogen Embrittlement of Inconel 718 by Notch Tensile Tests. Corrosion Science, 47, 355-367.
[30]
Azadian, S., Wei, L.Y. and Warren, R. (2004) Delta Phase Precipitation in Inconel 718. Materials Characterization, 53, 7-16. https://doi.org/10.1016/j.matchar.2004.07.004
Sundararaman, M., Mukhopadhyay, P. and Banerjee, S. (1988) Deformation Behaviour of γ” Strengthened Inconel 718. Acta Metallurgica, 36, 847-864. https://doi.org/10.1016/0001-6160(88)90139-3
[33]
Oblak, J.M., Paulonis, D.F. and Duvall, D.S. (1974) Coherency Strengthening in Ni Base Alloys Hardened by DO 22 γ’ Precipitates. Metallurgical Transactions, 5, Article No. 143.
[34]
Radavich, J.F. (1989) The Physical Metallurgy of Cast and Wrought Alloy 718. In: Loria, E.A., Ed., Superalloy 718 Metallurgy and Applications, The Minerals, Metals & Materials Society, Warrendale, 229-240.
[35]
Jothi, S., Merzlikin, S.V., Croft, T.N., Andersson, J. and Brown, S.G.R. (2016) An Investigation of Micro-Mechanisms in Hydrogen Induced Cracking in Nickel-Based Superalloy 718. Journal of Alloys and Compounds, 664, 664-681. https://doi.org/10.1016/j.jallcom.2016.01.033
[36]
LaCoursiere, M.P. Aidun, D.K. and Morrison, D.J. (2017) Slow Strain Rate Testing for Hydrogen Embrittlement Susceptibility of Alloy 718 in Substitute Ocean Water. Journal of Materials Engineering and Performance, 26, 2337-2345. https://doi.org/10.1007/s11665-017-2675-x
[37]
Obasi, G., Zhang, Z., Sampath, D., Morana, R., Akid, R. and Preuss, M. (2018) Effect of Microstructure and Alloy Chemistry on Hydrogen Embrittlement of Precipitation-Hardened Ni-Base Alloys. Metallurgical and Materials Transactions A, 49, 167-1181. https://doi.org/10.1007/s11661-018-4483-9
[38]
ASTM E112-96 (2004) Standard Test Methods for Determining Average Grain Size, ASTM International, West Conshohocken, PA.
[39]
Whitmore, L., Leitner, H., Povoden-Karadeniz, E., Radis, R. and Stockinger, M. (2012) Transmission Electron Microscopy of Single and Double Aged 718Plus Superalloy. Materials Science and Engineering: A, 534, 413-423. https://doi.org/10.1016/j.msea.2011.11.089
[40]
Ding, R. (2010) Grain Boundary Segregation in Ni-Base (718 Plus) Superalloy. Materials Science and Technology, 26, 36-40. https://doi.org/10.1179/174328408X385836
[41]
Turnbull, A., Ballinger, R.G., Hwang, I.S., Morra, M.M., Psaila-Dombrowsik, M. and Gates, R.M. (1992) Hydrogen Transport in Nickel-Base Alloys. Metallurgical Transactions A, 23, 3231-3244. https://doi.org/10.1007/BF02663432
[42]
Pressouyre, G.M. and Bernstein, I.M. (1979) A Kinetic Trapping Model for Hydrogen-Induced Cracking. Acta Metallurgica, 27, 89-100. https://doi.org/10.1016/0001-6160(79)90059-2
[43]
Dai, S. and Liu, W. (2010) First-Principles Study on the Structural, Mechanical and Electronic Properties of δ and γ” Phases in Inconel 718. Computational Materials Science, 49, 414-418. https://doi.org/10.1016/j.commatsci.2010.05.031
[44]
Lu, X., Wang, D., Wan, D., Zhang, Z.B., Kheradmand, N. and Barnoush, A. (2019) Effect of Electrochemical Charging on the Hydrogen Embrittlement Susceptibility of Alloy 718. Acta Materialia, 179, 36-48. https://doi.org/10.1016/j.actamat.2019.08.020
Palumbo, G. and Aust, K.T. (1995) Solute Effects in Grain-Boundary Engineering. Canadian Metallurgical Quarterly, 34, 165-173. https://doi.org/10.1179/cmq.1995.34.3.165
[47]
Seita, M., Hanson, J.P., Gradecak, S. and Demkowicz, M.J. (2015) The Dual Role of Coherent Twin Boundaries in Hydrogen Embrittlement. Nature Communications, 6, Article No. 6164. https://doi.org/10.1038/ncomms7164
[48]
Kagay, B., Findley, K., Coryell, S. and Nissan, A.B. (2016) Effects of Alloy 718 Microstructure on Hydrogen Embrittlement Susceptibility for Oil and Gas Environments. Materials Science and Technology, 32, 697-707. https://doi.org/10.1080/02670836.2016.1139225
[49]
Li, X., Zhang, J., Akiyama, E., Fu, Q. and Li, Q. (2019) Hydrogen Embrittlement Behavior of Inconel 718 Alloy at Room Temperature. Journal of Materials Science & Technology, 35, 499-502. https://doi.org/10.1016/j.jmst.2018.10.002
[50]
Kou, S. (2003) Welding Metallurgy. 2nd Edition, John Wiley and Sons, New York.