Ni0.6Co0.2Mn0.2(OH)2合成条件对物化性能的影响研究
|
Abstract:
利用硫酸镍、硫酸钴、硫酸锰、氨碱、氨水为原料，采用共沉淀法制备镍钴锰三元锂电池前驱体。分析了合成过程中氨水浓度、pH、温度、陈化时长、陈化后洗水量等因素对Ni0.6Co0.2Mn0.2(OH)2粒径、形貌等指标的影响，最终选出较优的工艺条件。
Using nickel sulfate, cobalt sulfate, manganese sulfate, ammonia base and ammonia water as raw materials, the precursor of nickel cobalt manganese ternary lithium battery was prepared by coprecipitation method. The influences of ammonia concentration, pH, temperature, aging time, and washing water amount on Ni0.6Co0.2Mn0.2(OH)2 particle size and morphology were analyzed in the synthesis process, and the optimal process conditions were finally selected.
| [1] | 王勇. ECFA下两岸新兴产业投资合作成效与提升路径探讨[J]. 国际经济合作, 2016, 32(2): 57-62. |
| [2] | 张淑静, 钟盛文, 张骞, 匡敬忠, 钟国雄. 镍酸锂前驱体-球形Ni(OH)2的制备工艺研究[J]. 江西有色金属, 2005, 19(4): 40-42. |
| [3] | 李尚津. 锂离子电池三元正极材料LiNi0.5Co0.2Mn0.3O2的制备与改性[D]: [硕士学位论文]. 南宁: 广西大学, 2017. |
| [4] | Choi, J. and Manthiram, A. (2015) Comparison of the Electrochemical Behaviors of Stoichiometric LiNi1/3Co1/3Mn1/3O2 and Lithium Li1.03(Ni1/3Co1/3Mn1/3)(0.97)O2. Electrochemical & Solid State Letters, 7, A365-A368. |
| [5] | Hou, P.Y., Wang, X.Q. and Song, D.W. (2014) Design, Synthesis, and Performances of Dou-ble-Shelled LiNi0.5Co0.2Mn0.3O2 as Cathode for Long-Life and Safe Li-Ion Battery. Journal of Power Sources, 45, A174-A181.
https://doi.org/10.1016/j.jpowsour.2014.04.107 |
| [6] | Lu, Y. and Zeng, X.F. (2019) Ultrathin LiV2O4 Layers Mod-ified LiNi0.5Co0.2Mn0.3O2 Single-Crystal Cathodes with Enhanced Activity and Stability. Advanced Materials Interfaces, 6, A33-A36. https://doi.org/10.1002/admi.201901368 |
| [7] | 朱飞, 倪华良. 锂离子电池正极材料的研究进展[J]. 通信电源技术, 2012, 29(5): 74-78. |
| [8] | 贺晓书. 层状正极材料锂镍钴铝氧化物的制备与包覆改性研究[D]: [博士学位论文]. 哈尔滨: 哈尔滨工业大学, 2019. |
| [9] | 刘彦龙. 前驱体制备对三元材料的影响及研究进展概述[J]. 电源技术, 2019, 43(12): 7-12. |
| [10] | 元莎. LiNi0.8Co0.15Al0.05O2(NCA)正极材料的合成与电化学性能研究[D]: [硕士学位论文]. 昆明: 昆明理工大学, 2016. |
| [11] | Noh, M. and Cho, J. (2012) Optimized Synthetic Conditions of LiNi0.5Co0.2Mn0.3O2 Cathode Materials for High Rate Lithium Batteries via Co-Precipitation Method. Journal of the Electrochemical Society, 64, A105-A111.
https://doi.org/10.1149/2.004302jes |
| [12] | 李沛荣, 李沃颖. pH值与反应釜转速对三元材料前驱体物理性能的影响[J]. 广东化工, 2019, 46(11): 79-80. |
| [13] | 王昭. 锂离子电池富锂锰基三元正极材料的研究[D]: [博士学位论文]. 北京: 北京理工大学, 2015. |
| [14] | 黄可龙, 王兆翔, 刘素琴. 锂离子电池原理与关键技术[M]. 北京: 化学工业出版社, 2008: 60-62. |
| [15] | 胡伟, 钟盛文, 李晓艳, 等. LiNi0.55Co0.15Mn0.3O2三元正极材料的合成及电化学性能研究[J]. 有色金属科学与工程, 2019, 10(3): 54-57. |
| [16] | 杨利. 三元正极材料LiNi1/3Co1/3Mn1/3O2的制备及低温性能研究[D]: [硕士学位论文]. 兰州: 西北师范大学, 2015. |
| [17] | 张晨, 郑江峰, 冉建军, 等. 陈化时间对Ni0.60Co0.20Mn0.20(OH)2性能的影响[J]. 世界有色金属, 2019, 35(8): 221-223. |
| [18] | 饶睦敏. 锂电池纳米硫正极与凝胶聚合物电解质的研究[D]: [博士学位论文]. 广州: 华南理工大学, 2012. |