缝合式三维编织C/SiC复合材料拉伸加卸载力学行为
|
Abstract:
本文通过开展缝合式三维编织C/SiC复合材料的准静态单轴拉伸及循环加卸载试验，研究加卸载行为对复合材料的损伤及材料内部能量耗散的影响。通过对材料的断口分析，探究加卸载对材料破坏强度的影响规律。结果表明，加卸载行为会消耗材料内部的能量，对纤维束与基体之间的界面造成损伤，进而降低材料的承载能力；材料滞回曲线的面积随着卸载点应力的增大而增大；材料的整体失效属于脆性破坏，复合材料断口表现出明显的分层现象，且单轴拉伸时断口相对于循环加卸载更整齐。 Quasi-static uniaxial tension and cyclic loading/unloading tests of the sutured 3D-C/SiC braided composites were carried out to research the effects of cycle loading/unloading behavior on the damage and inner energy dissipation. Through the fractography analysis of this material, the effect law of the strength change caused by cycle loading/unloading has been explored. The results show that the behavior of cycle loading/unloading will consume energy of interface between matrix and fiber bundle inside the material, resulting in damage to it, which reduces the load-bearing capacity of the material, and the area of hysteresis loop increases as the stress of each unloading point increases. The overall failure of this material is brittle failure, but the fracture of the sample shows obvious delamination under monotonous loading and cycle loading, while the fracture of the uniaxial tensile specimen is more uniform. 国家自然科学基金（11802059）；江苏省自然科学基金（BK20170656
| [1] | KRENKEL W, BERNDT F. C/C-SiC composites for space applications and advanced friction systems[J]. Materials Science and Engineering:A, 2005, 412(1-2):177-181. |
| [2] | ZHOU Y, HANG X, WU S, et al. Frequency-dependent random fatigue of panel-type structures made of ceramic matrix composites[J]. Acta Mechanica Solida Sinica, 2017, 30(2):165-173. |
| [3] | 赵卫, 乔玲, 韩晓林, 等. C/C-SiC复合材料的表面烧蚀模型及数值模拟[J]. 东南大学学报(自然科学版), 2011, 41(2):365-369. ZHAO Wei, QIAO Ling, HAN Xiaolin, et al. Surface ablation model and numerical simulation of C/C-SiC composites[J]. Journal of Southeast University (Natural Science Edition), 2011, 41(2):365-369(in Chinese). |
| [4] | 郭飞, 费庆国, 李彦斌, 等. 基于Weibull模型的C/C销钉剪切强度分布及本构关系[J]. 复合材料学报, 2019, 36(2):461-468.GUO Fei, FEI Qingguo, LI Yanbin, et al. Shear strength distribution and constitutive model of C/C composite pins based on Weibull model[J]. Acta Materiae Compositae Sinica, 2019, 36(2):461-468(in Chinese). |
| [5] | 杨成鹏, 矫桂琼, 王波. D-C/SiC复合材料的单轴拉伸力学行为及其强度[J]. 力学学报, 2011, 43(2):330-337.YANG Chengpeng, JIAO Guiqiong, WANG Bo, et al. Uniaxial tensile stress-strain behavior and strength of plain woven C/SiC composite[J]. Chinese Journal of Theoretical and Applied Mechanics, 2011, 43(2):330-337(in Chinese). |
| [6] | XU Y, CHENG L, ZHANG L, et al. Mechanical properties of 3D fiber reinforced C/SiC composites[J]. Materials Science and Engineering:A, 2001, 300(1-2):196-202. |
| [7] | YAN K F, ZHANG C Y, QIAO S R, et al. Failure and strength of 2D-C/SiC composite under in-plane shear loading at elevated temperatures[J]. Materials & Design, 2011, 32(6):3504-3508. |
| [8] | LI J, JIAO G, WANG B, et al. Damage characteristics and constitutive modeling of the 2D C/SiC composite:Part II-Material model and numerical implementation[J]. Chinese Journal of Aeronautics, 2015, 28(1):314-326. |
| [9] | BOUAZZAOUI R E, STéPHANE B, GéRALD C. Development of damage in a 2D woven C/SiC composite under mechanical loading:II. Ultrasonic characterization[J]. Composites Science and Technology, 1996, 56(96):1373-1382. |
| [10] | MORVAN J M, BASTE S. Effect of the opening/closure of microcracks on the nonlinear behavior of a 2D C-SiC compo-site under cyclic loading[J]. International Journal of Damage Mechanics, 1998, 7(4):381-402. |
| [11] | STéPHANE Baste. Inelastic behaviour of ceramic-matrix composites[J]. Composites Science and Technology, 2001, 61(15):2285-2297. |
| [12] | CAMUS G, GUILLAUMAT L, BASTE S. Development of damage in a 2D woven C/SiC composite under mechanical loading:I. Mechanical characterization[J]. Composites Science and Technology, 1996, 56(12):1363-1372. |
| [13] | LI Y, XIAO P, LUO H, et al. Fatigue behavior and residual strength evolution of 2.5D C/C-SiC composites[J]. Journal of the European Ceramic Society, 2016, 36(16):3977-3985. |
| [14] | ZHOU Y, FEI Q. Evaluation of opening-hole shapes for rivet connection of a composite plate[J]. Proceedings of the Institution of Mechanical Engineers Part C:Journal of Mechanical Engineering Science, 2017, 231(20):3810-3817. |
| [15] | 陈素芳, 谭志勇, 姜东, 等. 高温环境下纤维增强复合材料等效参数预测[J]. 振动与冲击, 2018, 37(11):216-224.CHEN Sufang, TAN Zhiyong, JIANG Dong, et al. Equivalent parametric prediction for fiber reinforced composites under high temperature condition[J]. Journal of Vibration and Shock, 2018, 37(11):216-224(in Chinese). |
| [16] | 陈飞, 李彦斌, 费庆国, 等. 正交各向异性C/SiC复合材料板的模态密度辨识[J]. 东南大学学报(自然科学版), 2015, 45(6):1135-1139.CHEN Fei, LI Yanbin, FEI Qingguo, et al. Modal density identification of orthotropic C/SiC composite plate[J]. Journal of Southeast University(Natural Science Edition), 2015, 45(6):1135-1139(in Chinese). |
| [17] | 姜东, 陆韬, 吴邵庆, 等. 2.5维C/SiC复合材料弹性参数不确定性识别方法研究[J]. 振动工程学报, 2014, 27(3):318-325.JIANG Dong, LU Tao, WU Shaoqin, et al. An elastic moduli identification method of 2.5 dimensional C/SiC composite with uncertainty[J]. Journal of Vibration Engineering, 2014, 27(3):318-325(in Chinese). |
| [18] | 管国阳, 矫桂琼, 张增光. 2D-C/SiC复合材料的宏观拉压特性和失效模式[J]. 复合材料学报, 2005, 22(4):81-85.GUAN Guoyang, JIAO Guiqiong, ZHANG Zengguang, et al. Uniaxial macro-mechanical property and failure mode of a 2D-woven C/SiC composite[J]. Acta Materiae Compositae Sinica, 2005, 22(4):81-85(in Chinese). |
| [19] | BORKOWSKI L, CHATTOPADHYAY A. Multiscale model of woven ceramic matrix composites considering manufacturing induced damage[J]. Composite Structures, 2015, 126:62-71. |
| [20] | YANG C P, ZHANG L, WANG B, et al. Tensile behavior of 2D-C/SiC composites at elevated temperatures:Experiment and modeling[J]. Journal of the European Ceramic Society, 2017, 37(4):1281-1290. |
| [21] | CHABOCHE J L, MAIRE J F. New progress in micromechanics-based CDM models and their application to CMCs[J]. Composites Science and Technology, 2001, 61(15):2239-2246. |
| [22] | CHABOCHE J L, MAIRE J F. A new micromechanics based CDM model and its application to CMC's[J]. Aerospace Science and Technology, 2002, 6(2):131-145. |
| [23] | LI J, JIAO G, WANG B, et al. Damage characteristics and constitutive modeling of the 2D C/SiC composite:Part I-Experiment and analysis[J]. Chinese Journal of Aeronautics, 2014, 27(6):1586-1597. |
| [24] | LI L B. Cyclic loading/unloading hysteresis behavior of fiber-reinforced ceramic-matrix composites at room and elevated temperatures[J]. Materials Science and Engineering A, 2015, 648:235-242. |
| [25] | American Society for Testing Materials. Standard test method for monotonic tensile behavior of continuous fiber-reinforced advanced ceramics with solid rectangular cross-section test specimens at ambient temperature:C1275-18[S]. West Conshohocken:ASTM International, 2018, |
| [26] | KOTIL T, HOLMES J W, COMNINOU M. Origin of hysteresis observed during fatigue of ceramic-matrix composites[J]. Journal of the American Ceramic Society, 2010, 73(7):1879-1883. |
| [27] | GOODMAN L E, KLUMPP J H. Analysis of slip damping with reference to turbine blade vibration[J]. Journal of Applied Mechanics, 1956, 23(2):421-429. |