新型高固含量乳化沥青制备研究
Study on New Emulsified Asphalt with High Solid Content

DOI: 10.12677/OJTT.2019.83020, PP. 166-173

Keywords: 乳化沥青，阳离子乳化剂，阴离子乳化剂，裹附，强度
Emulsified Asphalt, Cationic Emulsifier, Anionic Emulsifier, Wrapping, Strength

Full-Text   Cite this paper   Add to My Lib

Abstract:

本论文共采用两种方法配制乳化沥青，方式一通过阳离子乳化，配制沥青占比65%的水包油(O/W)型乳液；方式二是通过煤油稀释沥青后非离子乳化，提高沥青含量，配制沥青占比70%的油包水(W/O)型乳液。最后在拌和沥青混合料的时候，通过三层裹附工艺提升沥青混合料的强度。
In this paper, two methods are used to prepare emulsified asphalt. The first method is to prepare water-oil (O/W) emulsion with a proportion of 65% by cation emulsification. The second method is to increase the content of asphalt by non-ionic emulsification after paraffin is diluted, and prepare water-in-oil (W/O) emulsion with 70% asphalt. Finally, when mixing asphalt mixture, the strength of asphalt mixture is improved by three-layer wrapping process.

References

[1]	王红亮, 李其祥, 丁浩, 等. 国内外乳化沥青的应用及发展趋势[J]. 炭素, 2013(4): 45-47, 25.
[2]	陈晓光, 丁朴, 熊杰. 乳化沥青冷再生技术分析公路与汽运[J]. 公路与汽运, 2006(2): 105-107.
[3]	王长安, 吴育良, 许凯, 等. 影响乳化沥青稳定性的主要因素[J]. 新型建筑材料, 2005(1): 52-54.
[4]	张紫红. 厂拌冷再生用乳化沥青性能及应用技术研究[D]: [硕士学位论文]. 西安: 西安科技大学, 2017.
[5]	刘尚乐. 乳化沥青及其在道路、建筑工程中的应用[M]. 北京: 中国建材工业出版社, 2008: 4-5.
[6]	张兰. 乳化沥青稳定剂的确定[J]. 安徽职业技术学报, 2009, 8(4): 13-15.
[7]	赵晓帆. 沥青碎石封层技术的施工工艺与施工装备应用[D]: [硕士学位论文]. 重庆: 重庆交通大学, 2009.
[8]	虎增福. 乳化沥青及稀浆封层技术[M]. 北京: 人民交通出版社, 2001.
[9]	田静, 沙爱民. 低能耗沥青路面混合料选型与施工工艺研究[D]: [硕士学位论文]. 西安: 长安大学, 2010.
[10]	胡凯, 王为标. 乳化沥青应用于水工沥青混凝土的探索性研究[D]: [硕士学位论文]. 西安: 西安理工大学, 2013.
[11]	郭晨昊, 韩森. 粘层用环氧树脂改性乳化沥青关键技术研究[D]: [硕士学位论文]. 西安: 长安大学, 2012.
[12]	侯伟林, 刘宝举. 水泥沥青砂浆用SBS改性沥青储存稳定性的影响[D]: [硕士学位论文]. 长沙: 中南大学, 2011.
[13]	龚陶然, 刘其城, 李海斌. 稳定剂对季铵盐阳离子型乳化沥青储存稳定性的影响[J]. 交通科学与工程, 2011, 27(1): 41-45.
[14]	韩春来. SBS改性乳化沥青研制及路用性能室内试验研究[D]: [硕士学位论文]. 长沙: 长沙理工大学, 2011.
[15]	彭煜, 蔺习雄, 杨克红, 等. 新微表处混合料可拌和时间的影响因素分析[J]. 石油沥青, 2007, 21(3): 14-18.
[16]	常玉艳, 裴建军, 姚德宏. 两种乳化沥青蒸发残留物含量测定法的比较[J]. 石油沥青, 2004, 18(6): 49-52.

Full-Text