帘线钢生产工艺的研究进展
Research Progress of Cord Steel Production Technology

DOI: 10.12677/MEng.2019.64035, PP. 251-259

Keywords: 帘线钢，铅浴淬火，水浴淬火，电镀工艺
Cord Steel, Lead Bath Quenching, Water Bath Quenching, Electroplating Process

Full-Text   Cite this paper   Add to My Lib

Abstract:

帘线钢具有弹性好、强度高、抗冲击等优异的力学性能，是超洁净钢的代表性产品，具有极高的技术工艺难度。本文简要介绍了钢帘线的拉丝过程、盘条的处理、钢帘线的铅浴淬火，水浴淬火和电镀工艺的最新研究进展。重点介绍了铅浴淬火和镀铜的工艺参数。
Cord steel has excellent mechanical properties such as good elasticity, high strength, and impact resistance. It is a representative product of ultra-clean steel and has extremely high technical dif-ficulties. This article briefly introduces the latest research progress of steel cord drawing process, wire rod processing, lead bath quenching of steel cord, water bath quenching and plating process. The process parameters of lead bath quenching and copper plating were introduced.

References

[1]	Parusov, V.V., Derevyanchenko, I.V., Sychkov, A.B., et al. (2005) Ensuring High Quality Indices for the Wire Rod Used to Make Metal Cord. Metallurgist, 49, 439-448. https://doi.org/10.1007/s11015-006-0020-y
[2]	Lee, S.K., Ko, D.C. and Kim, B.M. (2009) Pass Schedule of Wire Drawing Process to Prevent Delamination for High Strength Steel Cord Wire. Materials and Design, 30, 2919-2927. https://doi.org/10.1016/j.matdes.2009.01.007
[3]	康昕. 我国钢帘线的生产情况及国内外钢帘线生产技术[J]. 钢铁技术, 2006(6): 1-4.
[4]	雷家柳, 薛正良, 朱航宇, 等. 子午线轮胎用帘线钢非金属夹杂物的研究进展[J]. 钢铁研究学报, 2018, 30(11): 847-856.
[5]	萧忠敏. 武钢炼钢生产技术进步概况[M]. 北京: 冶金工业出版社, 2003.
[6]	邹峰. 帘线钢精炼相关问题的研究[D]: [硕士学位论文]. 武汉: 武汉科技大学, 2015.
[7]	张炜. 帘线钢的塑性夹杂物热力学计算[D]: [硕士学位论文]. 昆明: 昆明理工大学, 2008.
[8]	王勇. 钢帘线表面和性能质量控制工艺的研究[D]: [硕士学位论文]. 武汉: 武汉科技大学, 2007.
[9]	赵方实, 汤小雷. 钢帘线生产中不同淬火方式的探讨[J]. 金属制品, 2008, 34(1): 7-10.
[10]	魏泽民. 钢丝索氏体微观组织尺寸控制及相变条件研究[D]: [硕士学位论文]. 贵阳: 贵州大学, 2015.
[11]	曹秀岭, 翟振华. 帘线钢丝铅浴淬火与水浴淬火组织性能对比[J]. 金属制品, 2010, 36(4): 39-42.
[12]	宋清华, 王伯健, 刘世锋. 胎圈钢丝的生产现状[J]. 金属制品, 2006, 32(4): 12-13+16.
[13]	李宗科. KSC72A钢丝水浴淬火工艺及性能研究[D]: [硕士学位论文]. 镇江: 江苏大学, 2016.
[14]	Languillaume, J., Kapelski, G. and Baudelet, B. (1997) Evolution of the Tensile Strength in Heavily Cold Drawn and Annealed Pearlitic Steel Wires. Materials Letters, 33, 241-245. https://doi.org/10.1016/S0167-577X(97)00109-2
[15]	邵红红, 李宗科, 孙杰, 等. 水浴淬火工艺对φ0.8 mm KSC72A钢丝组织与性能影响[J]. 材料热处理学报, 2015, 36(S2): 112-116.
[16]	俞国峰. 明火炉铅淬火连续热处理工艺性能探讨[J]. 金属制品, 2002, 28(6): 12-14.
[17]	吴志娟. 引起钢丝铅淬火强度偏差的原因分析[J]. 金属制品, 2004, 30(6): 11-13.
[18]	肖英龙. 提高轮胎钢帘线的强度[J]. 金属制品, 2007, 33(5): 49-52.
[19]	孙金茂. 钢丝生产[M]. 北京: 冶金工业出版社, 1985.
[20]	于克勇. 钢丝铅淬火在炉加热时间的控制[J]. 天津冶金, 2005(S1): 61-62+76.
[21]	张雄菲. 电接触加热条件下的控制冷却对碳素钢丝组织与性能的影响[D]: [硕士学位论文]. 贵阳: 贵州大学, 2019.
[22]	宋维锡. 金属学[M]. 北京: 冶金工业出版社, 1989.
[23]	董述峰, 赵刚, 叶传龙, 等. 铅浴淬火工艺对70钢丝组织和性能的影响[J]. 特殊钢, 2011, 32(2): 60-62.
[24]	于同仁, 宋强, 王伟, 等. 一种1960MPa级海洋工程用镀锌钢丝绳及其生产方法[P]. 中国专利, CN108486478B. 2019-07-02.
[25]	Seppala, J., Koskel, S., Melanen, M. and Palperi, M. (2002) The Finish Metals Industry and The Environment. Resources, Conservation and Recycling, 35, 61-76. https://doi.org/10.1016/S0921-3449(01)00122-7
[26]	吴荣桂. 铅中毒诊断标准及铅卫生标准对铅接触者健康保护意义的探讨[J]. 广西医科大学学报, 2003, 20(1): 52-54.
[27]	王宝玉, 陈卫东. 金属制品行业的节能与清洁生产[J]. 金属制品, 2008, 34(6): 38-40.
[28]	刘永铨, 高庆安, 崔文暄, 等. 钢的热处理[M]. 北京: 冶金工业出版社, 1981.
[29]	赵丽. 70#高碳钢丝水浴淬火工艺及其对组织性能的影响[D]: [硕士学位论文]. 哈尔滨: 哈尔滨工业大学, 2016.
[30]	陈红献, 王宝玉, 宋为, 等. 一种钢丝感应加热水浴淬火热处理工艺[P]. 中国专利, CN106435099A. 2017-02-22.
[31]	高文顺, 张同轩, 高源远. 国内钢丝电镀铜工艺评述[J]. 内蒙古科技与经济, 2006(20): 102-104.
[32]	杨巍峰, 钱庆生, 杨小芹. 钢帘线用热浸镀黄铜钢丝的微观组织及力学性能[J]. 电镀与涂饰, 2019, 38(7): 305-310.
[33]	张学辉. 轮胎用钢帘线生产工艺[J]. 科技资讯, 2019, 17(10): 57-58+60.
[34]	吕伟刚, 王一男. 提高轮胎用钢帘线强度的方法探索[J]. 产业与科技论坛, 2016, 15(17): 70-71.
[35]	程沪生. 热扩散法镀黄铜丝[J]. 材料保护, 2004, 37(9): 53-54+61.
[36]	宋为. 国产电镀黄铜生产线技术研发[J]. 金属制品, 2011, 37(1): 41-44+60.
[37]	陈全晟, 宋为, 王宝玉. 镀黄铜高压胶管钢丝生产线[J]. 金属制品, 2001, 27(1): 9-10+17.
[38]	田栋, 周长利, 夏方诠, 等. 钢帘线无氰亚铜电镀黄铜及黄铜镀层的钝化方法[P]. 中国专利, CN104120462A. 2014-10-29.

Full-Text