Abstract:
针对含铜低合金钢轧制钢板表面裂纹，经统计分析，通过优化关键工艺控制参数，板坯入炉温度控制小于690℃、钢水[S]含量小于0.012%，[N]含量小于0.0070%，合理控制板坯加热时间和温度，将避免含铜低合金钢轧制钢板表面裂纹，轧制钢卷表面质量良好。
The surface crack of the rolled steel plate containing copper was studied by statistical analysis. The results show that reasonable control of the slab heating time and temperature will avoid the surface crack of the rolled steel plate containing copper and low alloy steel, and the surface quality of the rolled steel coil is well. The key process control parameters are slab temperature controlled below 690？C, liquid steel [S] content less than 0.012%, liquid steel [n] content less than 0.0070%.
| [1] | 李振明. 连铸坯热装热送技术在炼轧厂的应用[J]. 酒钢科技, 2012(3): 228-233. |
| [2] | 汪永国, 谷海容, 霍俊, 等. 热装热送工艺技术的生产实践[J]. 安徽冶金, 2016(3): 46-48. |
| [3] | 王洁, 骆正荣. 梅钢热装热送工艺[J]. 梅山科技, 2010(1): 63-64. |
| [4] | 陈红雨, 于长春, 张建方. 宁波钢铁连铸坯热装热送生产实践[J]. 山东冶金, 2012, 34(1): 57-58. |
| [5] | 孙成礼, 林健. 热轧板坯热装热送技术的应用[J]. 新疆钢铁, 2014(1): 9-13. |
| [6] | 王志刚. 直装工艺造成的表面缺陷机理研究[D]: [硕士学位论文]. 武汉: 武汉科技大学, 2010. |
| [7] | 程秀英, 刘宇. 热装热送板坯加热炉模型参数优化[J]. 特钢技术, 2012, 18(1): 44-45. |
| [8] | 邓新跃. 2250热装热送问题及改造方案研究[J]. 涟钢科技与管理, 2018(2): 37-39. |
| [9] | 万潇, 白松莲, 白学军. 连铸坯热装热送技术的应用[J]. 河北冶金, 2016(10): 54-56. |
| [10] | 李卓. 热装热送对82B成品表面质量影响浅析[J]. 酒钢科技, 2012(3): 177-180. |
| [11] | 陈小龙, 余轶峰, 董苑华. 柳钢热送热装技术应用浅析[J]. 柳钢科技, 2014(6): 23-26. |
| [12] | 喻云龙. 热送热装技术在中小型钢厂的应用[J]. 钢铁研究, 2010, 38(4): 36-38. |
| [13] | 刘钊. 热送热装过程的温度场应力场数值模拟及二次开发[D]: [硕士学位论文]. 武汉: 武汉科技大学, 2010. |