三维正交机织玄武岩/环氧树脂复合材料高温老化后低速冲击性质
|
Abstract:
研究了三维正交机织玄武岩/环氧树脂复合材料在180℃高温环境下老化不同时间后的低速冲击力学性能,测试得到了不同老化时间的试样在低速冲击过程中的载荷-位移曲线。研究发现:随着老化时间增加,三维正交机织玄武岩/环氧树脂复合材料能承受的最大载荷下降,位移逐渐增加,载荷-位移曲线斜率逐渐下降;随着冲击能量增加,老化条件相同的三维正交机织玄武岩/环氧树脂复合材料试样最大承受载荷增大,位移和曲线斜率增加。对高温老化后三维正交机织玄武岩/环氧树脂复合材料试样进行SEM观察,发现纤维与树脂基体脱粘有裂纹产生,且裂纹数目和面积随着老化时间延长而增加。 We presents the low velocity impact mechanical behaviors of 3D orthogonal woven basalt/epoxy woven composites after exposure to 180℃ high temperature environment for different aging time. The load-displacement curves of specimens in process of low velocity impact for different aging time have been obtained. The research indicates that the peak load and the slope of load-displacement curves of 3D orthogonal woven basalt/epoxy composites monotonically decrease with the increase of aging time, while the deflection gradually increases. While with the increasing of impact energy, the peak load, the deflection and the slope of curves for 3D orthogonal woven basalt/epoxy composite specimens with the same aging condition also raise. The SEM observations for the high temperature aged 3D orthogonal woven basalt/epoxy composite specimens indicate the presence of fiber/resin matrix debonding crack, the amount and size of crack increase with increasing aging time. 国家自然科学基金(11272087)
| [1] | 杜善义. 先进复合材料与航空航天[J]. 复合材料学报, 2007, 24(1):1-12. DU S Y. Advanced composite materials and aerospace engineering[J]. Acta Materiae Compositae Sinica, 2007, 24(1):1-12(in Chinese). |
| [2] | SUN B Z, GU B H. Shear behavior of 3D orthogonal woven fabric composites under high strain rates[J]. Journal of Reinforced Plastics and Composites, 2006, 25(17):1833-1845. |
| [3] | TAN P, TONG L Y, STEVEN G P, et al. Behavior of 3D orthogonal woven CFRP composites. Part I. Experimental investigation[J]. Composites Part A:Applied Science and Manufacturing, 2000, 31(3):259-271. |
| [4] | 冯青, 李敏, 顾轶卓, 等. 不同湿热条件下碳纤维/环氧复合材料湿热性能实验研究[J]. 复合材料学报, 2010, 27(6):16-20. FENG Q, LI M, GU Y Z, et al. Experimental research on hygrothermal properties of carbon fiber/epoxy resin composite under different hygrothermal conditions[J]. Acta Materiae Compositae Sinica, 2010, 27(6):16-20(in Chinese). |
| [5] | American Society for Testing and Materials International. Standard test method for measuring damage resistance of fiber-reinforced polymer matrix composite to a drop-weight impact event:ASTM D7136-05[S]. West Conshohocken:ASTM International, 2005. |
| [6] | BOWLES K J, JAYNE D, LEONHARDT T A. Isothermal aging effects on pmr-15 resin[J]. Sampe Quarterly-Society for the Advancement of Material and Process Engineering, 1993, 24(2):2-9. |
| [7] | GIGLIOTTI M, GRANDIDIER J C, LAFARIE-FRENOT M C. The employment of 0/90 unsymmetric samples for the characterisation of the thermo-oxidation behaviour of composite materials at high temperatures[J]. Composite Structures, 2011, 93(8):2109-2119. |
| [8] | MISHRA R, MILITKY J, BEHERA B K, et al. Modelling and simulation of 3D orthogonal fabrics for composite applications[J]. Journal of the Textile Institute, 2012, 103(11):1255-1261. |
| [9] | HUANG G, ZHONG Z L. Tensile behavior of 3D woven composites by using different fabric structures[J]. Materials & Design, 2002, 23(7):671-674. |
| [10] | HANCOX N L. Thermal effects on polymer matrix composites:Part 2. Thermal degradation[J]. Materials & Design, 1998, 19(3):93-97. |
| [11] | HANCOX N L. Thermal effects on polymer matrix composites:Part 1. Thermal cycling[J]. Materials & Design, 1998, 19(3):85-91. |
| [12] | BARJASTEH E, BOSZE E J, TSAI Y I, et al. Thermal aging of fiberglass/carbon-fiber hybrid composites[J]. Composites Part A:Applied Science and Manufacturing, 2009, 40(12):2038-2045. |
| [13] | MINERVINO M, GIGLIOTTI M, LAFARIE-FRENOT M C, et al. The effect of thermo-oxidation on the mechanical behaviour of polymer epoxy materials[J]. Polymer Testing, 2013, 32(6):1020-1028. |
| [14] | VU D Q, GIGLIOTTI M, LAFARIE-FRENOT M C. Experimental characterization of thermo-oxidation-induced shrinkage and damage in polymer-matrix composites[J]. Composites Part A:Applied Science and Manufacturing, 2012, 43(4):577-586. |
| [15] | American Society for Testing and Materials International. Standard practice for heat aging of plastics without load:ASTM D3045-92[S]. West Conshohocken:ASTM International, 1992. |
| [16] | TAN P, TONG L Y, Steven G P. Behavior of 3D orthogonal woven CFRP composites. Part II. FEA and analytical modeling approache[J]. Composites Part A:Applied Science and Manufacturing, 2000, 31(3):273-281. |