盐冻条件下水泥砂浆受风沙冲蚀磨损性能及损伤机制
Erosion-wear performance and mechanism of cement mortar subjected to freeze-thaw cycles in salts solution

DOI: 10.13801/j.cnki.fhclxb.20170417.002

Keywords: 冲蚀磨损,水泥砂浆,复合盐,冻融循环,损伤机制
erosion-wear,cement mortar,compound salt,freeze-thaw cycle,damage mechanism

Full-Text   Cite this paper   Add to My Lib

Abstract:

References

[1]	LIU Z, HANSEN W. Freeze-thaw durability of high strength concrete under deicer salt exposure[J]. Construction & Building Materials, 2016, 102(Part 1):478-485.
[2]	陈爱玖, 王静, 马莹. 钢纤维橡胶再生混凝土的抗冻性试验[J]. 复合材料学报, 2015, 32(4):933-941. CHEN A J, WANG J, MA Y. Test of frost resistance for steel fiber rubber recycled concrete[J]. Acta Materiae Compositae Sinica, 2015, 32(4):933-941(in Chinese).
[3]	尹延国, 朱元吉, 胡献国. 水工混凝土冲蚀磨损试验方法的研究[J]. 水利水电技术, 2001, 32(3):15-18. YIN Y G, ZHU Y J, HU X G. Study on method of erosion-wear experiment of hydraulic concrete[J]. Water Resources and Hydropower Engineering, 2001, 32(3):15-18(in Chinese).
[4]	高欣欣, 蔡跃波, 丁建彤. 磨粒形态对水工抗冲磨混凝土磨损程度的影响[J]. 混凝土, 2012(4):77-79. GAO X X, CAI Y B, DING J T. Study on the influence of form factor of abrasion particles on concrete[J]. Concrete, 2012(4):77-79(in Chinese).
[5]	尹延国, 胡献国, 崔德密, 等. 水工混凝土小角度冲蚀磨损特性的研究[J]. 摩擦学学报, 2001, 21(2):126-130. YIN Y G, HU X G, CUI D M, et al. Wear behaviors of hydraulic concrete impacted by water jet with sand at little angle[J]. Tribology, 2001, 21(2):126-130(in Chinese).
[6]	HU X G, MOMBER A W, YIN Y. High-speed hydrodynamic wear of steel-fibre reinforced hydraulic concrete[J]. Wear, 2004, 257(5-6):441-450.
[7]	GRDIC Z J, CURCIC G A T, RISTIC N S, et al. Abrasion resistance of concrete micro-reinforced with polypropylene fibers[J]. Construction & Building Materials, 2012, 27(1):305-312.
[8]	郝贠洪, 冯玉江, 段国龙, 等. 风沙环境下钢结构涂层的冲蚀摩擦学性能[J]. 北京工业大学学报, 2015, 41(4):558-565. HAO Y H, FENG Y J, DUAN G L, et al. Erosion tribological performance of steel-structure coating in sandstorm[J]. Journal of Beijing University of Technology, 2015, 41(4):558-565(in Chinese).
[9]	郝贠洪, 邢永明, 赵燕茹, 等. 风沙环境下钢结构涂层侵蚀机制及评价方法[J]. 建筑材料学报, 2011, 14(3):345-361. HAO Y H, XING Y M, ZHAO Y R, et al. Erosion mechanism and evaluation method of steel structure coating eroded under sandstorm environment[J]. Journal of Building Materials, 2011, 14(3):345-361(in Chinese).
[10]	PAUL C P, MISHRA S K, TIWARI P, et al. Solid-particle erosion behaviour of WC/Ni composite clad layers with different contents of WC particles[J]. Optics & Laser Technology, 2013, 50(2):155-162.
[11]	王彦平, 居春常, 王起才. 风沙环境下混凝土、砂浆和水泥石的固体颗粒冲蚀磨损试验研究[J]. 中国铁道科学, 2013, 34(5):21-26. WANG Y P, JU C C, WANG Q C. Experimental study on the solid particle erosion of concrete, mortar and cement paste under blown sand environment[J]. China Railway Science, 2013, 34(5):21-26(in Chinese).
[12]	郝贠洪, 冯玉江, 樊金承, 等. 混凝土受气固两相流冲蚀损伤机制与评价研究[J]. 建筑材料学报, 2016, 19(4):642-646. HAO Y H, FENG Y J, FAN J C, et al. Damage mechanism and evaluation of concrete under the erosion of gas-solid two phase flow[J]. Journal of Building Materials, 2016, 19(4):642-646(in Chinese).
[13]	SHIPWAY P H, HUTCHINGS I M. A method for optimizing the particle flux in erosion testing with a gas-blast apparatus[J]. Wear, 1994, 174(1-2):169-175.
[14]	CHEN J K, JIANG M Q, ZHU J. Damage evolution in cement mortar due to erosion of sulphate[J]. Corrosion Science, 2008, 50(9):2478-2483.
[15]	HORSZCZARUK E. The model of abrasive wear of concrete in hydraulic structures[J]. Wear, 2004, 256(7-8):787-796.
[16]	何真, 胡曙光, 梁文泉, 等. 水工混凝土磨蚀磨损的研究[J]. 硅酸盐学报, 2000, 28(s1):81-83. HE Z, HU S G, LIANG W Q, et al. Research of concrete abrasion erosion in hydraulic structure[J]. Journal of the Chinese Ceramic Society, 2000, 28(s1):81-83(in Chinese).
[17]	KULU P, HUSSAINOVA I, VEINTHAL R. Solid particle erosion of thermal sprayed coatings[J]. Wear, 2005, 258(1-4):488-496.
[18]	宿晓萍. 吉林省西部地区盐渍土环境下混凝土耐久性研究[D]. 长春:吉林大学, 2013. SU X P. Research on the concrete durability due to salinized soil in the western region of Jilin province[D]. Changchun:Jilin University, 2013(in Chinese).
[19]	杨礼明, 余红发, 麻海燕, 等. 混凝土在碳化和干湿循环作用下的抗硫酸盐腐蚀性能[J]. 复合材料学报, 2012, 29(5):127-133. YANG M L, YU H F, MA H Y, et al. Resistance of concrete to magnesium sulfate attack under combined action of carbonation and dry-wet cycles[J]. Acta Materiae Compositae Sinica, 2012, 29(5):127-133(in Chinese).
[20]	GORETTA K C, BURDT M L, CUBER M M, et al. Solid-particle erosion of Portland cement and concrete[J]. Wear, 1999, 224(1):106-112.
[21]	中华人民共和国建设部. 建筑砂浆基本性能试验方法标准:JGJ/T 70-2009[S]. 北京:中国标准出版社, 2009. Ministry of Construction of the People's Republic of China. Standard for test method of performance on building mortar:JGJ/T 70-2009[S]. Beijing:China Standards Press, 2009(in Chinese).

Full-Text