表面处理玄武岩纤维增强水泥基复合材料力学性能
|
Abstract:
为提高玄武岩纤维（BF）与水泥基体的界面结合力和桥接作用，分别采用HCl溶液（0~2.0 mol/L）和NaOH溶液（0~2.0 mol/L）对BF表面进行刻蚀糙化处理，研究纤维表面处理对BF增强水泥基复合材料的力学性能影响规律。结果表明：随着HCl溶液浓度增加，BF/水泥复合材料抗折强度与弯曲强度均先增加后降低，挠度呈现缓慢增加趋势，而抗压强度变化幅度较小；当HCl溶液浓度为1 mol/L时，BF/水泥复合材料的强度与韧性最佳；碱处理BF后，BF/水泥复合材料的力学性能随NaOH浓度增加而显著降低，且复合材料韧性无明显改善；BF经HCl溶液腐蚀后的质量保留率变化规律与NaOH溶液腐蚀后的变化规律接近，而经HCl溶液腐蚀后BF强度保留率大于NaOH溶液腐蚀后的BF强度保留率。 For enhancing the interface bonding and the bringing effect of the basalt fibers (BF) to the cement matrix, the BF was treated with different concentrations of HCl solution (0-2.0 mol/L) and NaOH solution (0-2.0 mol/L), respectively. The mechanical properties of BF reinforced cement composites were studied. The results indicate that with the increase of the concentration of HCl solution, the flexural strength and bending strength increase firstly and then decrease, midspan deflection increases slowly and the change of compressive strength of BF/cement composite is not obvious. The strength and toughness of BF/cement composite are the highest as the concentration of HCl solution is 1 mol/L. The strength of BF/cement composite decreases significantly when BF is treated with NaOH solution, and the toughness of the composite is not improved obviously. Mass ratio variation trend of BF corroded HCl solution is similar to that of BF corroded with NaOH solution while strength ratio of BF corroded HCl solution is more than that of BF corroded with the same concentrate of NaOH solution. 国家自然科学基金（51402098）
| [1] | 陈润锋, 张国防, 顾国芳, 等. 我国合成纤维混凝土研究与应用现状[J]. 建筑材料学报, 2001, 4(2):167-173. CHEN R F, ZHANG G F, GU G F, et al. State of study and application of synthetic fibers reinforced concrete in China[J]. Journal of Building Materials, 2001, 4(2):167-173 (in Chinese). |
| [2] | VAJIHOLLAH A, ABBAS T, REZA G, et al. Effect of composition and length of PP and polyester fibers on mechanical properties of cement based composites[J]. Construction and Building Materials, 2012, 36:534-537. |
| [3] | 史建丽, 田砾, 赵铁军, 等. 天然纤维增强水泥基材料轴拉性能试验研究[J]. 混凝土与水泥制品, 2015(3):55-57. SHI J L, TIAN L, ZHAO T J, et al. Study on axial tension performance of natural fiber reinforced concrete[J]. China Concrete and Cement Products, 2015(3):55-57 (in Chinese). |
| [4] | FERNANDO P T, SAID J. Cementitious building materials reinforced with vegetable fibers:A review[J]. Construction and Building Materials, 2011, 25(2):575-581. |
| [5] | 赵晶, 李晓民, 宋学富, 等. 耐碱玻璃纤维混凝土的配合比设计[J]. 哈尔滨工业大学学报, 2005, 37(6):766-768. ZHAO J, LI X M, SONG X F, et al. Mix design of alkali-resistance glass fiber concrete[J]. Journal of Harbin Institute of Technology, 2005, 37(6):766-768 (in Chinese). |
| [6] | LUIGI F, DANIELE F, EZIO C. Dynamic behaviour of cement mortars reinforced with glass and basalt fibers[J]. Composites Part B:Engineering, 2016, 92:142-150. |
| [7] | KUNAL S. A short review on basalt fiber[J]. International Journal of Textile Science, 2012, 1(4):19-28. |
| [8] | FIORE V, SCALICI T, BELLA G D, et al. A review on basalt fibre and its composites[J]. Composites Part B:Engineering, 2015, 74:74-94. |
| [9] | 叶邦土, 蒋金洋, 王文灏, 等. 玄武岩纤维及其增强水泥基材料的研究进展[J]. 材料导报, 2013, 27 (19):102-108. YE B T, JIANG J Y, WANG W H, et al. Research progress on basalt fiber and its reinforced cement-based materials[J]. Materials Review, 2013, 27(19):102-108 (in Chinese). |
| [10] | KAMILE T F, FELEKOGLU B, RANADE R, et al. The role of flaw size and fibre distribution on tensile ductility of PVA-ECC[J]. Composites Part B:Engineering, 2014, 56:536-545. |
| [11] | 李忠良. 玄武岩纤维增强机场道面混凝土的力学性能研究[D]. 沈阳:沈阳工业大学, 2014. LI Z L. Study on mechanical properties of basalt fiber reinforced concrete for airport pavament[D]. Shengyang:Shenyang University of Technology, 2014 (in Chinese). |
| [12] | 吴钊贤, 袁海庆, 卢哲安, 等. 玄武岩纤维混凝土力学性能试验研究[J]. 混凝土, 2009(9):67-68+78. WU Z X, YUAN H Q, LU Z A, et al. Experimental research on mechanical properties of basalt fiber reinforced concrete[J]. Concrete, 2009(9):67-68 +78 (in Chinese). |
| [13] | SIM J, PARK C, MOON D Y. Characteristics of basalt fiber as a strengthening material for concrete structures[J]. Composites Part B:Engineering, 2005, 36(6-7):504-512. |
| [14] | 全国水泥标准化技术委员会. 水泥胶砂强度检验方法:GB/T 17671-1999[S]. 北京:中国标准出版社, 1999. National Cement Standardzation Technical Committee. Method of testing cements-determination of strength:GB/T 17671-1999[S]. Beijing:China Standards Press, 1999 (in Chinese). |
| [15] | JIAN Z, QIAN S Z, BELTRAN M G S, et al. Development of engineered cementitious composites with limestone powder and blast furnace slag[J]. Materials and Structures, 2010, 43(6):803-814. |
| [16] | 霍文静, 张佐光, 王明超, 等. 复合材料用玄武岩纤维耐酸碱性实验研究[J]. 复合材料学报, 2007, 24(6):77-82. HUO W J, ZHANG Z G. Experimental study on acid and alkali resistance of basalt fiber used for composites[J]. Acta Materiae Compositae Sinica, 2007, 24(6):77-82 (in Chinese). |
| [17] | SHAFIQ N, AYUB T, KHANB S U. Investigating the performance of PVA and basalt fibre reinforced beams subjected to flexural action[J]. Composite Structures, 2016, 153:30-41. |
| [18] | LIPATOV YA V, GUTNIKOV S I, MANYLOV M S, et al. High alkali-resistant basalt fiber for reinforcing concrete[J]. Materials and Design, 2015(73):60-66. |
| [19] | BRANDT A M. Fibre reinforced cement-based (FRC) composites after over 40 years of development in building and civil engineering[J]. Composite Structures, 2008, 86(1-3):3-9. |
| [20] | 何东明, 李丽娟, 朱江, 等. 钢纤维高强混凝土研究与应用进展[J]. 混凝土, 2009(4):17-19. HE D M, LI L J, ZHU J, et al. On the study and application of steel fiber reinforced high strength concrete[J]. Concrete, 2009(4):17-19 (in Chinese). |
| [21] | 佟钰, 田鑫, 朱长军, 等. 短切碳纤维混凝土的力学强度实验与分析[J]. 硅酸盐通报, 2015, 34(8):2281-2285+2297. TONG Y, TIAN X, ZHU C J, et al. Experiments and analysis on mechanical strength of carbon fiber reinforced concrete[J]. Bulletin of the Chinese Ceramic Society, 2015, 34(8):2281-2285+2297 (in Chinese). |