酸蚀Al粉对Al-聚氨酯复合涂层光泽度与红外发射率的影响
Effects of acid-etched Al powders on glossiness and infrared emissivity of Al-polyurethane composite coatings

DOI: 10.13801/j.cnki.fhclxb.20170117.003

Keywords: 复合涂层,酸蚀,光泽度,红外发射率,力学性能
composite coatings,acid etching,glossiness,infrared emissivity,mechanical properties

Full-Text   Cite this paper   Add to My Lib

Abstract:

References

[1]	MAO Z P, YU X L, ZHANG L P, et al. Novel infrared stealth property of cotton fabrics coated with nano ZnO∶(Al, La) particles[J]. Vacuum, 2014, 104(2): 111-115.
[2]	张伟钢, 徐国跃, 乔加亮, 等. Al-Sm2O3/聚氨酯复合涂层的近红外低反射与8~14 μm低发射率性能[J]. 复合材料学报, 2014, 31(2): 436-440. ZHANG W G, XU G Y, QIAO J L, et al. Low emissivity at 8-14 μm and low near-infrared reflective properties of Al-Sm2O3/polyurethane composite coatings[J]. Acta Materiae Compositae Sinica, 2014, 31(2): 436-440 (in Chinese).
[3]	HU C, XU G Y, SHEN X M. Preparation and characteristics of thermal resistance polysiloxane/Al composite coatings with low infrared emissivity[J]. Journal of Alloys and Compounds, 2009, 486(1-2): 371-375.
[4]	肖圣荣, 张桐, 王智勇, 等. 一种水性聚氨酯涂层红外发射率的研究[J]. 红外技术, 2016, 38(2): 107-111. XIAO S R, ZHANG T, WANG Z Y, et al. The research on the infrared emissivity of water-borne polyurethane coatings[J]. Infrared Technology, 2016, 38(2): 107-111 (in Chinese).
[5]	FANG S J, WANG W, YU X L, et al. Preparation of ZnO∶(Al, La)/polyacrylonitrile (PAN) nonwovens with low infrared emissivity via electrospinning[J]. Materials Letters, 2015, 143: 120-123.
[6]	SOLOVYEV A A, RABOTKIN S V, KOVSHAROV N F. Polymer films with multilayer low-E coatings[J]. Materials Science in Semiconductor Processing, 2015, 38: 373-380.
[7]	CHEN J, ZHOU Y M, NAN Q L, et al. Synthesis, characterization and infrared emissivity study of Polyurethne/TiO2 nanocomposites[J]. Applied Surface Science, 2007, 253(23): 9154-9158.
[8]	李叶, 张志毅, 寿金泉, 等. 低红外发射率涂层的制备及耐高温性能研究[J]. 中国胶黏剂, 2015, 24(9): 37-40. LI Y, ZHANG Z Y, SHOU J Q, et al. Study on preparation and high temperature resistance of low infrared emissivity coating[J]. China Adhesives, 2015, 24(9): 37-40 (in Chinese).
[9]	ZHANG W G, XU G Y, DING R Y, et al. Nacre biomimetic design-A possible approach to prepare low infrared emissivity composite coatings[J]. Materials Science and Engineering: C, 2013, 33(1): 99-102.
[10]	石枭, 徐国跃, 张伟钢, 等. 不同固化剂对红外低发射率涂层力学性能的影响[J]. 兵器材料科学与工程, 2015, 38(3): 5-7. SHI X, XU G Y, ZHANG W G, et al. Influence of different curing agent on mechanical properties of low infrared emissivity coatings[J]. Ordnance Material Science and Engineering, 2015, 38(3): 5-7 (in Chinese).
[11]	TAN W M, WANG L F, YU F, et al. Preparation and characterization of a greenish yellow lackluster coating with low infrared emissivity based on Prussian blue modified aluminum[J]. Progress in Organic Coatings, 2014, 77(7): 1163-1168.
[12]	刘凯, 谭淑娟, 徐国跃, 等. 酞青蓝对红外低发射率涂层色泽的影响[J]. 南京航空航天大学学报, 2016, 48(1): 53-57. LIU K, TAN S J, XU G Y, et al. Influence of phthalocyanine blue on chromaticity of low infrared emissivity coatings[J]. Journal of Nanjing University of Aeronautics and Astronautics, 2016, 48(1): 53-57 (in Chinese).
[13]	徐飞凤, 徐国跃, 谭淑娟. 8~14 μm波段低红外发射率与低光泽度兼容涂层的制备方法初探[J]. 兵器材料科学与工程, 2011, 34(4): 5-9. XU F F, XU G Y, TAN S J. Preparation methods of low infrared emissivity and low glossiness coatings for 8-14 μm wave band[J]. Ordnance Material Science and Engineering, 2011, 34(4): 5-9 (in Chinese).
[14]	WU G W, YU D M. Preparation and characterization of a new low infrared-emissivity coating based on modified aluminum[J]. Progress in Organic Coatings, 2013, 76(1): 107-112.
[15]	YUAN L, WENG X L, XIE J L, et al. Solvothermal synthesis and visible/infrared optical properties of Al/Fe3O4 core-shell magnetic composite pigments[J]. Journal of Alloys and Compounds, 2013, 580(32): 108-113.
[16]	袁乐, 翁小龙, 卢虎, 等. Al/Cr2O3复合粉体的制备及红外反射特性研究[J]. 复合材料学报, 2013, 30(5): 545-550. YUAN L, WENG X L, LU H, et al. Preparation and infrared reflection performance of Al/Cr2O3 composite particles[J]. Journal of Inorganic Materials, 2013, 30(5): 545-550 (in Chinese).
[17]	中华人民共和国化学工业部. 色漆和清漆-铅笔法测定漆膜硬度: GB/T 6739-2006[S]. 北京: 中国标准出版社, 2006. Ministry of Chemical Industry of the People's Republic of China. Paints and varnishes-Determination of film hardness by pencil test: GB/T 6739-2006[S]. Beijing: Standards Press of China, 2006 (in Chinese).
[18]	中华人民共和国化学工业部. 漆膜附着力测定法: GB 1720-79[S]. 北京: 中国标准出版社, 1979. Ministry of Chemical Industry of the People's Republic of China. Ministry of Chemical Industry of the People's Republic of China. Determination of adhesion of paint film: GB 1720-79[S]. Beijing: Standards Press of China, 1979 (in Chinese).
[19]	中华人民共和国化学工业部. 漆膜耐冲击测定法: GB/T 1732-93[S]. 北京: 中国标准出版社, 1993. Ministry of Chemical Industry of the People's Republic of China. Ministry of Chemical Industry of the People's Republic of China. Determination of resistance to impact of paint film: GB/T 1732-93[S]. Beijing: Standards Press of China, 1993 (in Chinese).

Full-Text