基于裂纹开裂角度的夹层板层间开裂
|
Abstract:
以聚氨酯弹性体钢夹层板为研究对象，对黏弹性夹芯夹层结构三点弯曲实验卸载后裂纹会沿层间方向继续扩展这一现象进行研究。开展了不同硬度夹芯的双悬臂梁（Double Cantilever Beam，DCB）实验和单悬臂梁（SLB）实验，测得了临界应变能释放率。在假设裂纹张开角度在开裂过程中不变的前提下，推导了临界应变能释放率的计算公式。并计算了软夹芯试件和硬夹芯试件的临界破坏的裂纹长度。结果表明，虽然存有一定的局限性，但是裂纹张开角度能够描述黏弹性夹层结构的层间裂纹扩展，获得的结果能够描述聚氨酯弹性体钢夹层板的层间延迟破坏的特点。 Specimens of sandwich plate with viscoelastic core for 3-points bending test appear delay debonding at interface after unloading. Theoretical and experimental approaches for sandwich plate with steel faceplates and polyurethane elastomer core were utilized here to study this phenomenon. Double Cantilever Beam(DCB) and Single Cantilever Beam(SLB) tests were conducted here to obtain strain energy release rate (SERR) between face plates and core. And the expression of critical SERR was deduced on condition of unchanged crack tip opening angle. Furthermore, critical crack length for two types of sandwich plate with different core was calculated. The results show that despite of some limitations, crack tip opening angle can illustrate the propagation of interface crack and reveal the characteristic of delay debonding of sandwich plate with polyurethane core and steel faceplate. 国家自然科学基金（51409056）；黑龙江省自然科学基金（E2015047；E2015045）；中央高校基本科研业务费专项基金（HEU20160202）
| [1] | PRASAD S, CARLSSON L A. Debonding and crack kinking in foam core sandwich beams—I. Analysis of fracture specimens[J]. Engineering Fracture Mechanics, 1994, 47(6): 813-824. |
| [2] | 王振清, 梁文彦, 吕红庆. 双材料界面Ⅰ型扩展裂纹尖端的弹黏塑性场[J]. 力学学报, 2011, 43(02): 417-422. WANG Zhenqing, LIANG Wenyan, LV Hongqing. The elastic-viscoplastic field near the mode I dynamic propagating crack-tip of interface in double dissimilar materials[J]. Chinese Journal of Theoretical and Applied Mechanics, 2011, 43(02): 417-422 (in Chinese). |
| [3] | 张淳源, 张为民. 求解一类非线性粘弹性问题的弹性回复对应原理[J]. 工程力学, 2002, 19(1): 139-146. ZHANG Chunyuan, ZHANG Weimin. Elasticity recovery correspondence principle for solving a class of nonlinear viscoelastic problems[J]. Engineering Mechanics, 2002, 19(1): 139-146 (in Chinese). |
| [4] | ROTHWELL B. Recent developments in design for crack arrest using the crack-tip opening angle (CTOA)[J]. Journal of Pipeline Engineering, 2015, 4th quarter(MA): 241. |
| [5] | 余同希. 塑性弯曲理论及其应用[M]. 北京: 科学出版社, 1992: 25-47. YU Tongxi. The application of plastic bending theory[M].Beijing: The Science Publishing Company, 1992: 25-47 (in Chinese). |
| [6] | 薛启超. 聚氨酯弹性体钢夹层板的力学性能研究[D]. 哈尔滨:哈尔滨工程大学, 2013. XUE Qichao. Mechanical properties study for sandwich plate system[D]. Harbin: Harbin Engineering University, 2013 (in Chinese). |
| [7] | 张淳源. 裂纹的延迟失稳[J]. 湘潭大学自然科学学报, 1987(4): 49-54. ZHANG Chunyuan. Delayed instability of cracks[J]. Journal of Xiangtan University, 1987(4): 49-54 (in Chinese). |
| [8] | 李佳. SPS复合钢板的屈曲性能和面/芯粘结属性研究[D]. 哈尔滨:哈尔滨工程大学, 2012. LI Jia. An investigation on buckling behavior and surface/core disbonds problem for SPS composite plate[D]. Harbin: Harbin Engineering University, 2012 (in Chinese). |
| [9] | 丁大钧, 刘忠德. 关于弹性地基梁的若干问题计算[J]. 沈阳建筑大学学报自然科学版, 1986, 2(1): 1-10 (in Chinese). DING Dajun, LIU Zhongde. On the calculation of some problems of elastic foundation beams[J]. Journal of Shenyang Architectural Engineering College, 1986, 2(1): 1-10 (in Chinese). |
| [10] | BROOKING M A. The performance, safety and production benefits of sps structures for double hull tankers[J/OL]. [2004-01-01]https://www.researchgate.net/publication/267683334_The_Performance_Safety_and_Production_Benefits_of_SPS_Structures_for_Double_Hull_Tankers |
| [11] | PRASAD S, CARLSSON L A. Debonding and crack kinking in foam core sandwich beams. Ⅱ—Experimental investigation[J]. Engineering Fracture Mechanics, 1994, 47(6): 825-841. |
| [12] | PAPANICOLAOU G C, BAKOS D. Interlaminar fracture behaviour of sandwich structures[J]. Composites Part A: Applied Science & Manufacturing, 1996, 27(3): 165-173. |
| [13] | 刘玉岚, 王彪, 王殿富. 含有界面裂纹的粘弹性层合板应变能释放率的计算[J]. 应用数学和力学, 2003, 24(1): 12-18. LIU Yulan, WANG Biao, WANG Dianfu. On the calculation of energy release rate for visoelastic cracked laminates[J]. Applied Mathematics and Mechanics, 2003, 24(1): 12-18 (in Chinese). |
| [14] | PAN Shidong, FENG Jicai, WU Linzhi. Analysis of pre-crack kinking and delamination in terms of SLB test of honeycomb sandwich structure[J]. Journal of Harbin Institute of Technology(New Series), 2009, 16(04): 445-452. |
| [15] | 泮世东, 吴林志, 孙雨果. 蜂窝夹芯试件破坏行为分析[J]. 力学学报, 2007, 39(5): 610-617. PAN Shidong, WU Linzhi, SUN Yuguo. Analysis of fracture behavior of honeycomb sandwich specimens[J]. Chinese Journal of Theoretical and Applied Mechanics, 2007, 39(5): 610-617 (in Chinese). |
| [16] | RINKER M, JOHN M, ZAHLEN P C, et al. Face sheet debonding in CFRP/PMI sandwich structures under quasi-static and fatigue loading considering residual thermal stress[J]. Engineering Fracture Mechanics, 2011, 78(17): 2835-2847. |
| [17] | 梁文彦, 王振清, 吕红庆. 双材料界面Ⅱ型扩展裂纹尖端的弹粘塑性场[J]. 哈尔滨工业大学学报, 2011(s1): 188-191. LIANG Wenyan, WANG Zhenqing, LV Hongqing. The elastic-viscoplastic field near the mode 2 dynamic propagating interface creak-tip of double dissimilar materials[J]. Journal of Harbin Institute of Technology, 2011, 43(s1): 188-191 (in Chinese). |