单向竹原纤维表面改性对其增强不饱和聚酯树脂复合材料性能的影响
|
Abstract:
采用碱处理、碱-偶联剂联合处理对竹原纤维进行表面改性，通过缝合-模压工艺制备了单向连续竹原纤维/不饱和聚酯树脂（BF/UP）复合材料。研究了不同表面改性方法对BF/UP复合材料静态、动态力学性能、吸水性能等的影响，并用SEM、红外光谱等技术研究了改性处理后纤维的表面及复合材料界面结合情况。结果表明：经过不同表面处理后BF/UP复合材料的性能均有所改善。当采用5wt%碱-3wt%偶联剂联合处理时，BF/UP复合材料综合性能最优，其拉伸强度、弯曲强度、弯曲模量、剪切强度较未处理的分别提高了34.29%、15.95%、11.26%、29.39%；复合材料存储模量（33℃）较未处理的提高了63.80%，损耗因子有所降低；BF/UP复合材料24 h、720 h吸水率较未处理的分别减小了55.35%、27.32%。SEM和红外光谱结果表明，改性处理后竹原纤维表面杂质减少，附着了一层偶联剂膜，BF/UP复合材料中纤维与树脂之间的界面结合更好。 The surface of bamboo fibers was modified by using two sorts of methods including alkali treatment,alkali-silane treatment.Then unidirectional continuous bamboo fibers reinforced unsaturated polyester resin (BF/UP) composite was prepared by means of stitching-compression molding technology.The effects of different surface modification methods on the static and dynamic mechanical properties,water absorption were studied.SEM and FITR were used to describe the surface of treated fibers and the interface bonding condition in the BF/UP composite.The results show that the properties of the BF/UP composite after treating bamboo fiber using different modification methods all are improved.The performances of BF/UP composite are optimal with the treatment of 5wt% alkali-3wt% silane coupling agent.The BF/UP composite has the best comprehensive properties with the treatment of 5wt% alkali-3wt% silane coupling agent,whose tensile strength,flexural strength,flexural modulus and shear strength increase by 34.29%,15.95%,11.26% and 29.39% respectively.Compared with the untreated sample,the storage modulus of the BF/UP composite increases by 63.80%,the loss factor of BF/UP composite decreases,and the 24 h and 720 h water absorption of the BF/UP composite decrease by 55.35% and 27.32%.The results of SEM and FITR show that the impurity decrease and a layer of coupling agent film is attached on the surface of bamboo fiber,and there is a better interface adhesion occurs between the fiber and matrix after surface modification. 天津市科技特派员项目（16JCTPJC44900）；国家自然科学基金资助项目（51303131）
| [1] | 吴如艳, 陈凤舞. 玻璃钢材料发展现状综述[J]. 河南科技, 2013, 2(4):120-127. WU R Y, CHEN F W. Review of the development status of FRP materials[J]. Journal of Henan Science and Technology, 2013, 2(4):120-127(in Chinese). |
| [2] | 张立国, 吕琴. 我国玻璃钢/复合材料行业发展对玻璃纤维的市场需求[J]. 玻璃纤维, 2010(5):51-56. ZHANG L G, LV Q. Demand for glass fibers by growing FRP/composites industry in China[J]. Fiber Glass, 2010(5):51-56(in Chinese). |
| [3] | 王亚亮, 杨敏鸽, 王俊勃, 等. 苎麻纤维增强复合材料的研究现状[J]. 材料导报, 2008, 22(增刊1), 342-345. WANG Y L, YANG M G, WANG J B, et al. Present research status of ramie fiber reinforced composites[J]. Materials Review, 2008, 22(z1):342-345(in Chinese). |
| [4] | 郑霞, 李新功, 吴义强, 等. 竹纤维聚乳酸可生物降解复合材料自然降解性能[J]. 复合材料学报, 2014, 3(12):362-367. ZHENG X, LI X G, WU Y Q, et al. Natural degradation properties of bamboo fibers/polylactic acid biodegradable composites[J]. Acta Materiae Compositae Sinica, 2014, 3(12):362-367(in Chinese). |
| [5] | ZAKIKHANI P, ZAHARI R, SULTAN M T H, et al. Extraction and preparation of bamboo fibre-reinforced composites[J]. Materials & Design, 2014, 63(2):820-828. |
| [6] | TUNG N H, YAMAMOTO H, MATSUOKA T, et al. Effect of surface treatment on interfacial strength between bamboo fiber and PP resin[J]. International Journal Series A Solid Mechanics and Material Engineering, 2004, 47(4):561-565. |
| [7] | KHALIL H P S A, BHAT I U H, JAWAID M, et al. Bamboo fiber reinforced biocomposites:A review[J]. Materials & Design, 2012, 42:353-368. |
| [8] | 吴义强, 卿彦, 李新功, 等. 竹纤维增强可生物降解复合材料研究进展[J]. 高分子通报, 2012(1):71-75. WU Y Q, QING Y, LI X G, et al. Research progress on bamboo fiber reinforced biodegradable composites[J]. Polymer Bulletin, 2012(1):71-75(in Chinese). |
| [9] | 王春红, 刘胜凯. 碱处理对竹纤维及竹纤维增强聚丙烯复合材料性能的影响[J]. 复合材料学报, 2015, 32(3):683-690. WANG C H, LIU S K. Effect of alkali treatment on properties of bamboo fiber and bamboo fiber reinforced polypropylene composites[J]. Acta Materiae Compositae Sinica, 2015, 32(3):683-690(in Chinese). |
| [10] | BLEDZKI A K, GASSAN J. Composites reinforced with cellulose based fibres[J]. Progress In Polymer Science, 1999, 24(2):221-274. |
| [11] | ZHANG K, BRENDLER E, GEISSLER A, et al. Synthesis and spectroscopic analysis of cellulose sulfates with regulable total degrees of substitution and sulfation patterns via 13C NMR and FT Raman spectroscopy[J]. Polymer, 2011, 52(1):26-32. |
| [12] | ZUGENMAIER P. Conformation and packing of various crystalline cellulose fibers[J]. Progress In Polymer Science, 2001, 26(9):1341-1417. |
| [13] | 周楠婷. 苎麻纤维增强聚乳酸复合材料的界面、结构改进及其力学性能研究[D]. 上海:东华大学, 2014. ZHOU N T. Interfacial, structure and mechanical properties of ramie fiber reinforced poly(Lactic Acid) (PLA) composites[D]. Shang Hai:Donghua University, 2014(in Chinese). |
| [14] | SAWPAN M A, PICKERINGA K L, FERNYHOUGH A. Improvement of mechanical performance of industrial hemp fibre reinforced polylactide biocomposites[J]. Composites Part A:Applied Science and Manufacturing, 2011, 42(3):310-319 |
| [15] | America Standard Test Method Committee. ASTM D638-2003 Standard test methods for tensile properties of plastics[S]. United States:America Standard Test Method International, 2003. |
| [16] | American Society of Testing Materials International. ASTM790_03 Standard test methods for flexural properties of unreinforced and reinforced plastics and electrical insulating materials[S]. West Conshohocken:ASTM International, 2003. |
| [17] | 全国纤维增强塑料标准化技术委员会. JC/T773-2010/ISO 14130:1997纤维增强塑料短梁法测定层间剪切强度[S]. 北京:北京建材工业出版社, 2010. Fiber Reinforced Plastic of Standardization Administration of China. JC/T 773-2010/ISO 14130:1997 Fiber-reinforced plastics composites-determination of apparent interlaminar shear strength by short-beam method[S]. Beijing:China Building Materials Press, 2010(in Chinese). |
| [18] | American Society of Testing Materials International. ASTM D570-2005 Standard test method for water absorption of plastics[S]. United States:ASTM International, 2005. |
| [19] | GORIPARTHI B K, SUMAN K N S, RAO N M, et al. Effect of fiber surface treatments on mechanical and abrasive wear performance of polylactide/jute composites[J]. Composites Part A:Applied Science and Manufacturing, 2012, 43(10):1800-1808. |
| [20] | TAO Y, REN J, LI S M, et al. Effect of fiber surface-treatments on the properties of poly (lactic acid)/ramie composites[J]. Composites Part A:Applied Science and Manufacturing, 2010, 41(4):499-505. |
| [21] | 李兰杰, 胡娅婷, 刘得志, 等. 木粉的碱化处理对木塑复合材料性能的影响[J]. 合成树脂及塑料, 2006, 22(6):53-56. LI L J, HU Y T, LIU D Z, et al. Effect of alkaline treatment of wood flour on properties of wood/plastic composite[J]. China Synthetic Resin and Plastics, 2006, 22(6):53-56(in Chinese). |
| [22] | LUNSING E, KARNANI R, KRISHNAN M, et al. Biofiber-reinforced polypropylene composites[J]. Polymer Engineering & Science, 1997, 37(2):476-483 |
| [23] | RAJ R G, KOKTA B V. Composites of silane treated cellulosic fibers and high density polyethylene[J]. Macromolecular Materials and Engineering, 1991, 189(1):169-182. |
| [24] | 高聪, 李敏, 王娟, 等. 化学处理和吸湿水对剑麻纤维及其与树脂界面性能的影响[J]. 复合材料学报, 2013, 30(5):21-28. GAO C, LI M, WANG J, et al. Effect of chemical treatment and water absorption on properties of sisal fiber and its interface with resin[J]. Acta Materiae Compositae Sinica, 2013, 30(5):21-28(in Chinese). |
| [25] | 许民, 陶红梅, 陈磊, 等. 偶联剂含量对植物纤维高密度聚乙烯复合材料力学性能的影响[J]. 东北林业大学学报, 2007, 35(10):33-34. XU M, TAO H M, CHEN L, et al. Effect of coupling agent content on the mechanical properties of plant fiber/HDPE Composites[J]. Journal of Northeast Forestry University, 2007, 35(10):33-34(in Chinese). |