新型磁性离子交换吸附TiO2@Fe3O4/聚吡咯树脂复合材料制备及其吸附性能
|
Abstract:
首先采用溶胶-凝胶法制备TiO2@Fe3O4核壳结构的磁性纳米粒子，然后与聚吡咯（PPy）采用原位聚合法制备TiO2@Fe3O4/PPy磁性离子交换吸附剂。通过TEM、SEM对样品的形貌及粒径进行表征，用XRD表征分析物相，FTIR表征样品的表面性质，用VSM测定磁性能，由紫外-可见分光光度计测定吸光度，并对孔雀石绿溶液进行吸附性能测试。结果表明，PPy与TiO2@Fe3O4纳米粒子复合后形貌未变，团聚现象明显改善，磁强度为5.384 emu·g-1，具有超顺磁性。在pH=7，温度为298 K条件下，用0.05g TiO2@Fe3O4/PPy吸附剂对25 mL 20 mg·L-1孔雀石绿溶液（MG）进行吸附，饱和吸附容量为312.50 mg·g-1，且30 min内去除率可达到99.1%。与活性炭相比较，TiO2@Fe3O4/PPy磁性离子交换吸附树脂可以进行大面积动态交换与吸附，吸附性能优于活性炭。 TiO2@Fe3O4 magnetic nanoparticles with core-shell structure was prepared by sol-gel method,and then TiO2@Fe3O4/polypyrrole (PPy) magnetic ion exchange adsorption resin was prepared with PPy by chemical oxidation.The morphology and particle size of the samples were observed by TEM and SEM.The phase analysis was represented by XRD.The surface properties of the samples were represented by FTIR.VSM was used to determine the magnetic property.The absorbance could be represented by UV,and malachite green solution was used for the adsorption test.The results show that TiO2@Fe3O4/PPy composite nanoparticles which are superparamagnetic unchanged,agglomeration is obviously improved, the magnetic intensity is about 5.384 emu·g-1. When 0.05 g TiO2@Fe3O4/PPy adsorbent is used to adsort 25 mL 20 mg·L-1 malachite green solution (MG) at 298 K in the solution with pH=7,the saturated adsorption capacity of TiO2@Fe3O4/PPy adsorbent can reach up to 312.50 mg·g-1, and the removal rate of which can reach up to 99.1% within 30 min.Compared with the activated carbon,TiO2@Fe3O4/PPy magnetic ion exchange adsorption resin can undertake large area dynamic exchange and adsorption,which illustrates that its adsorption propertities are better than that of the activated carbon. 西北旱区生态水利工程国家重点实验室培育基地资助项目（2013ZZKT-9）
| [1] | 闻振涛. 有机废水处理中常用吸附剂的应用研究进展[J]. 科技信息, 2011(14):90. WEN Z T. The study of the application of common adsorbent in organic wastewater treatment[J]. Science and Technology Information, 2011(14):90(in Chinese). |
| [2] | 杨国华, 黄统琳, 姚忠亮, 等. 吸附剂的应用研究现状和进展[J]. 化学工程与装备, 2009(6):84-88. YANG G H, HUANG T L, YAO Z L, et al. Current application research on the adsorbents and their development tendency[J]. Chemical Engineering and Equipment, 2009(6):84-88(in Chinese). |
| [3] | 张婷, 俞树荣, 冯辉霞, 等. 新型复合吸附剂的制备及性能研究[J]. 中国非金属矿工业导刊, 2007(1):32-34. ZHANG T, YU S R, FENG H X, et al. Preparation and properties of new compound adsorbent[J]. China Non-Metallic Mining Industry Herald, 2007(1):32-34(in Chinese). |
| [4] | CHEN W, DUAN L, ZHU D Q. Adsorption of polar and nonpolar organic chemicals to carbon nanotubes[J]. Environmental Science & Technology, 2007, 41(24):8295-8300. |
| [5] | HYUNG H, FORTNER J D, HUGHES J B, et al. Natural organic matter stabilizes carbon nanotubes in the aqueous phase[J]. Environmental Science & Technology, 2007, 41(1):179-184. |
| [6] | ZHAO Y, CHEN H L, LI J, et al. Hierarchical MWCNTs/Fe3O4/PANI magnetic composite as adsorbent for methyl orange removal[J]. Colloid Interface Science, 2015, 450:189-195. |
| [7] | 陈婵维, 付忠田, 于洪蕾, 姜彬慧. 染料废水处理技术进展[J]. 环境保护与循环经济, 2010, 30(4):37-40. CHEN J W, FU Z T, YU H L, et al. The development of the dye wastewater treatment technology[J]. Environmental Protection and Circular Economy, 2010, 30(4):37-40(in Chinese). |
| [8] | 张小璇, 叶李艺, 沙勇, 邸婧. 活性炭吸附法处理染料废水[J]. 厦门大学学报, 2005, 44(4):542-545. ZHANG X X, YE L Y, SHA Y, DI Q. Treatment of dyeing wastewater with activated carbon[J]. Journal of Xiamen University, 2005, 44(4):542-545(in Chinese). |
| [9] | 周利民, 王一平, 黄群武, 等. 改性磁性壳聚糖微球对Cu2+、Cd2+和Ni2+的吸附性能[J]. 物理化学学报, 2007, 23(12):1979-1984. ZHOU L M, WANG Y P, HUANG Q W, et al. Adsorption properties of Cu2+, Cd2+ and Ni2+ by modified magnetic chitosan microspheres[J]. Acta Physico-chimica Sinica, 2007, 23(12):1979-1984(in Chinese). |
| [10] | YANG H, JIANG W, LU Y. Fabrication and characteristic of conductive and ferro magnetic hollow composite microcapsules[J]. Materials Letters, 2007, 6l(13):2789-2793. |
| [11] | 马宏飞, 刘荣强, 李薇, 葛琳琳. 茶叶渣对孔雀石绿吸附性能研究[J]. 应用化工, 2015, 44(6):1090-1094. MA H F, LIU R Q, LI W, GE L L. Study on the adsorption behavior of malachite green on tea waste[J]. Applied Chemical Industry, 2015, 44(6):1090-1094(in Chinese). |
| [12] | 朱灵峰, 吴洁琰, 郝丹迪, 等. 柚子皮对孔雀石绿的吸附性能[J]. 江苏农业科学, 2015, 43(4):366-368. ZHU L F, WU J Y, HAO D D, et al. Adsorption properties of malachite green onto pomelo peel[J]. Jiangsu Agricultural Sciences, 2015, 43(4):366-368(in Chinese). |
| [13] | 谭艳芝, 王秀芳, 钟国英. 新型竹活性炭对水体违禁药物孔雀石绿吸附性能的影响[J]. 中南大学学报, 2010, 41(4):1287-1291. TAN Y Z, WANG X F, ZHONG G Y. Effect of novel bamboo-based activated carbons on adsorption properties of prohibited drug malachite green in aquatic system[J]. Journal of Central South University, 2010, 41(4):1287-1291(in Chinese). |
| [14] | 刘晴. 氨基修饰纳米SiO2吸附4种染料的性能研究[D]. 开封:河南大学, 2010. LIU Q. Adsorption of four dyes by nanosilica modified with γ-amino propyl trieth oxysilane[D]. Kaifeng:Henan University, 2010(in Chinese). |
| [15] | YANG K, ZHU L Z, XING B S. Adsorption of polycyclic aromatic hydrocarbons by carbon nano materials[J]. Environmental Science & Technology, 2006, 40(6):1855-1861. |
| [16] | 黄金阳, 刘明华, 黄统琳, 等. 一种新型纤维素螯合吸附剂的制备[J]. 中国造纸学报, 2008, 23(4):44-47. HUANG J Y, LIU M H, HUANG T L, et al. The preparation of a new cellulose chelating adsorbent[J]. Transactions of China Pulp and Paper, 2008, 23(4):44-47(in Chinese). |
| [17] | 林生岭, 曹旭, 陈传祥, 等. 镧掺杂钙锰氧体/聚吡咯复合物的制备、表征及其电化学性能[J]. 复合材料学报, 2010, 27(3):56-60. LIN S L, CAO X, CHEN C X, et al. Preparation and characterization of La-doped Ca manganese oxide/polyrrole composites and its electrochemical properties[J]. Acta Materiae Compositae Sinica, 2010, 27(3):56-60(in Chinese). |
| [18] | CHENG Q L, PAVLINEK V, LI C Z, et al. Synthesis and structural properties of polypyrrole/nano-Y2O3 conducting composite[J]. Applied Surface Science, 2006, 253(4):1736-1740. |
| [19] | 张清爽, 李巧玲, 陈海利, 等. 静止原位复合法制备聚吡咯-TiO2纸及其催化性能[J]. 化学学报, 2011, 69(17):2009-2014. ZHANG Q S, LI Q L, CHEN H L, et al. Preparation and photocatalytic properties of PPy/TiO2 paper via unstirred in-situ polymerization[J]. Acta Chimica Sinica, 201l, 69(17):2009-2014(in Chinese). |