DOPO-PHBA反应型阻燃剂的合成及其与TGIC复配体系对环氧树脂性能的影响
|
Abstract:
以9，10-二氢-9-氧杂-10-磷杂菲-10-氧化物（DOPO）和对羟基苯甲醛（PHBA）为主要原料，合成了一种新型的反应型阻燃剂DOPO-PHBA，利用FTIR和核磁共振谱（1H-NMR、31P-NMR）对其分子结构和组成进行了分析表征。将DOPO-PHBA与异氰尿酸三缩水甘油酯（TGIC）复配用于制备DOPO-PHBA-TGIC/环氧树脂（EP）复合材料，通过极限氧指数（LOI）、动态热机械测试（DMA）和TGA分别对DOPO-PHBA-TGIC/EP复合材料的阻燃性能和热性能进行了研究。结果表明：成功制备了DOPO-PHBA，且DOPO-PHBA-TGIC复配型阻燃剂能显著改善EP的阻燃性能，当体系磷元素的质量分数为0.6wt%时，氧指数（LOI）由24%提高至32.5%；此外不同磷含量的DOPO-PHBA-TGIC/EP复合材料的玻璃化转变温度（Tg）均保持在200℃以上并且在800℃时的残炭量不断提高，其初始分解温度和最大热失重速率均有所下降；燃烧后残炭的红外分析表明，该体系满足凝聚相阻燃机制，且DOPO-PHBA-TGIC的加入不会削弱EP的力学性能。 A novel reactive flame retardant (DOPO-PHBA) was synthesized by the reaction between 9,10-dihydro-9-oxa-10-phosphine-10-oxide (DOPO) and p-hydroxybenzaldehyde (PHBA).Its structure and composition were characterized by FTIR and nuclear magnetic resonance spectroscopy 1H-NMR and 31P-NMR. DOPO-PHBA was compounded with triglycidyl isocyanurate (TGIC) to prepare DOPO-PHBA-TGIC/epoxy resin(EP) composites. The flame retardancy and thermal properties of DOPO-PHBA-TGIC/EP composites were respectively investigated by limiting oxygen index (LOI), dynamic mechanical analysis (DMA) and thermogravimetric analysis. Results indicate that DOPO-PHBA is successfully synthesized. The addition of DOPO-PHBA-TGIC can significantly enhance the flame retardancy of EP resin, while the mass fraction of phosphorus is 0.6wt%, LOI value increases from 24% to 32.5%. Additionally, the glass transition temperature (Tg) of DOPO-PHBA-TGIC/EP composites with different phosphorus mass fractions are maintained at 200℃ or higher, and the residues at 800℃ under nitrogen atmosphere are increased. But the initial degradation temperatures and maximum decomposition rates of DOPO-PHBA-TGIC/EP composites are decreased. FTIR analysis of char residues reveal that this flame retardant system satisfies condensed phase flame retardant mechanism, and the incorporation of DOPO-PHBA-TGIC does not impair the physical property of EP resin. 国家自然科学基金（51373129）
| [1] | 史婷, 郑亚萍, 李沛沛. 不同沉积物无溶剂纳米石墨烯流体/环氧树脂阻燃性能对比[J]. 复合材料学报, 2017, 34(1):31-39. SHI T, ZHENG Y P, LI P P. Flame resistance of epoxy matrix filled with different solvent-free grapheme nanofluids[J]. Acta Materiae Compositae Sinica, 2017, 34(1):31-39(in Chinese). |
| [2] | 卢林刚, 陈英辉, 赵瑾, 等. DOPOMPC-APP-MWCNTs协同阻燃环氧树脂的制备[J]. 复合材料学报, 2015, 32(1):101-107. LU L G, CHEN Y H, ZHAO J, et al. Preparation of DOPOMPC-APP-MWCNTs intumescent flame-retardant epoxy resin[J]. Acta Materiae Compositae Sinica, 2015, 32(1):101-107(in Chinese). |
| [3] | 刘学清, 刘继廷, 蔡少君, 等. 甲基乙基次磷酸铝/环氧树脂阻燃复合材料性能[J]. 复合材料学报, 2012, 29(4):83-87. LIU X Q, LIU J T, CAI S J, et al. Properties of aluminum methylethyl phosphinate/epoxy resin flame retardant cpmposites[J]. Acta Materiae Compositae Sinica, 2012, 29(4):83-87(in Chinese). |
| [4] | BISWAS B, KANDOLA B K. The effect of chemically reactive type flame retardant additives on flammability of PES toughened epoxy resin and carbon fiber-reinforced composites[J]. Polymers for Advanced Technologies, 2011, 22(7):1192-1204. |
| [5] | 宋健, 周文君, 陈友财, 等. 聚硼硅氧烷与有机磷酸酯阻燃剂复配协同阻燃聚碳酸酯[J]. 复合材料学报, 2012, 29(3):65-71. SONG J, ZHOU W J, CHEN Y C, et al. Synergistic effect between polyborosiloxane and organophosphate flame retardants on polycarbonate[J]. Acta Materiae Compositae Sinica, 2012, 29(3):65-71(in Chinese). |
| [6] | WU C S, YING L L, CHIU Y S. Epoxy resins possessing flame retardant elements from silicon incorporated epoxy compounds cured with phosphorus or nitrogen containing curing agents[J]. Polymer, 2002, 43(15):4277-4284. |
| [7] | XIN W, LEI S, XING W, et al. A effective flame retardant for epoxy resins based on poly(DOPO substituted dihydroxyl phenyl pentaerythritol diphosphonate)[J]. Materials Chemistry & Physics, 2011, 125(3):536-541. |
| [8] | WANG X, ZHANG Q. Synthesis, characterization, and cure properties of phosphorus-containing epoxy resins for flame retardance[J]. European Polymer Journal, 2004, 40(2):385-395. |
| [9] | RWEI S P, CHENG C Y, LIOU G S, et al. Curing and pyrolysis of cresol novolac epoxy resins containing BABODOPN[J]. Polymer Engineering & Science, 2005, 45(4):478-486. |
| [10] | ZHANG H, XU M, LI B. Synthesis of a novel phosphorus-containing curing agent and its effects on the flame retardancy, thermal degradation and moisture resistance of epoxy resins[J]. Polymers for Advanced Technologies, 2015, 27(7):860-871. |
| [11] | CHEN X, GU A, LIANG G, et al. Novel low phosphorus-content bismaleimide resin system with outstanding flame retardancy and low dielectric loss[J]. Polymer Degradation & Stability, 2012, 97(5):698-706. |
| [12] | WANG L, JIANG J, JIANG P, et al. Synthesis, characteristic of a novel flame retardant containing phosphorus, silicon and its application in ethylene vinyl-acetate copolymer (EVM) rubber[J]. Journal of Polymer Research, 2010, 17(6):891-902. |
| [13] | LIN C H, HWANG T Y, TASO Y R, et al. Phosphorus-containing epoxy curing agents via imine linkage[J]. Macromolecular Chemistry & Physics, 2007, 208(24):2628-2641. |
| [14] | SUN D, YAO Y. Synthesis of three novel phosphorus-containing flame retardants and their application in epoxy resins[J]. Polymer Degradation & Stability, 2011, 96(10):1720-1724. |
| [15] | ZHANG X H, LIU F, CHEN S, et al. Novel flame retardant thermosets from nitrogen-containing and phosphorus-containing epoxy resins cured with dicyandiamide[J]. Journal of Applied Polymer Science, 2007, 106(4):2391-2397. |
| [16] | XU W H, WIRASAPUTRA A, LIU S, et al. Highly effective flame retarded epoxy resin cured by DOPO-based co-curing agent[J]. Polymer Degradation & Stability, 2015, 122:44-51. |
| [17] | TIAN X, WANG Z, YU Q, et al. Synthesis and property of flame retardant epoxy resins modified with 2-(diphenylphosphinyl)-1, 4-benzenediol[J]. Chemical Research in Chinese Universities, 2014, 30(5):868-873. |
| [18] | 全国纤维增强塑料标准化技术委员会. 纤维增强塑料燃烧性能试验方法-氧指数法:GB/T 8924-2005[S]. 北京:中国标准出版社, 2005. China National Technology Committee of Standardization for Fiber Reinforced Plastic Products. Test method for flammability characteristic of fiber reinforced plastics-Oxygen index method:GB/T 8924-2005[S]. Beijing:China Standards Press, 2005(in Chinese) |
| [19] | 全国纤维增强塑料标准化技术委员会. 树脂浇铸体弯曲性能试验方法:GB/T 2570-1995[S]. 北京:中国标准出版社, 1995. China National Technology Committee of Standardization for Fiber Reinforced Plastic Products. Test method for flexural properties of resin casting body:GB/T 2570-1995[S]. Beijing:China Standards Press, 1995(in Chinese). |
| [20] | ENESCU D, FRACHE A, LAVASELLI M, et al. Novel phosphorous-nitrogen intumescent flame retardant system:Its effects on flame retardancy and thermal properties of polypropylene[J]. Polymer Degradation & Stability, 2013, 98(1):297-305. |
| [21] | 宋艳, 许亮, 李锦春, 等. 新型磷氮型阻燃剂的制备及其阻燃性聚氨酯泡沫塑料[J]. 复合材料学报, 2016, 33(11):2461-2467. SONG Y, XU L, LI J C, et al. Synthesis of novel flame retardant containing phosphorus and Nitrogen and its application in retardant polyurethane foam plastic[J]. Acta Materiae Compositae Sinica, 2016, 33(11):2461-2467(in Chinese). |