酸蚀及粘结剂对聚醚醚酮粘结强度的影响
|
Abstract:
摘要 目的:研究经过不同表面处理后的聚醚醚酮与饰面树脂间粘结强度的变化。实验方法:将聚醚醚酮样品随机分为4组进行表面处理:98%浓硫酸酸蚀组,粘结剂处理组,98%浓硫酸酸蚀+粘结剂处理组和未处理对照组。各处理组再随机分为2个亚组粘结饰面树脂:GC Gradia组,Ceramage组。每个亚组随机选出一半样品用37 ℃蒸馏水浸泡24 h,其余样品冷热循环10000次后,测量样品的剪切粘结强度,SPSS软件统计分析数据;体视显微镜检查样品断裂界面,统计粘结失败类型。结果:各表面处理实验组与空白对照组之间均存在统计学差异,经硫酸酸蚀处理的聚醚醚酮与Ceramage硬质树脂的粘结强度最高(19.38±5.34) MPa,且与其他实验组有统计学差异(P＜0.05)。在冷热循环后,除粘结Gradia Direct树脂的浓硫酸+粘结剂处理组外,其余实验组的粘结强度明显降低(P＜0.05)。结论:浓硫酸酸蚀与自酸蚀粘结剂均能提高聚醚醚酮与饰面树脂的粘结强度,Gradia Direct饰面树脂与经浓硫酸+粘结剂处理的聚醚醚酮表面可形成稳定的粘结作用
| [1] | Daneshkazemi A, Davari A, Akbari M J, et al. Effects of Thermal and Mechanical Load Cycling on the Dentin Microtensile Bond Strength of Single Bond-2 [J]. J Int Oral Health,2015,7(8)∶9-13 |
| [2] | Stawarczyk B, Beuer F, Wimmer T, et al. Polyetheretherketone-a suitable material for fixed dental prostheses [J]. J Biomed Mater Res B Appl Biomater,2013,101(7)∶1209-1216 |
| [3] | Sproesser O, Schmidlin PR, Uhrenbacher J, et al. Effect of sulfuric acid etching of polyetheretherketone on the shear bond strength to resin cements [J]. J Adhes Dent,2014,16(5)∶465-472 |
| [4] | Schmidlin PR, Stawarczyk B, Wieland M, et al. Effect of different surface pre-treatments and luting materials on shear bond strength to PEEK [J]. Dent Mater,2010,26(6)∶553-559 |
| [5] | Hallmann L, Mehl A, Sereno N, et al. The improvement of adhesive properties of PEEK through different pre-treatments [J]. Appl. Surf. Sci,2012,258(18)∶7213-7218 |
| [6] | Stawarczyk B, Bahr N, Beuer F, et al. Influence of plasma pretreatment on shear bond strength of self-adhesive resin cements to polyetheretherketone [J]. Clin Oral Investig,2014,18(1)∶163-170 |
| [7] | Kern M, Lehmann F. Influence of surface conditioning on bonding to polyetheretherketon (PEEK) [J]. Dent Mater,2012,28(12)∶1280-1283 |
| [8] | Stawarczyk B, Jordan P, Schmidlin P R, et al. PEEK surface treatment effects on tensile bond strength to veneering resins [J]. J Prosthet Dent,2014,112(5)∶1278-1288 |
| [9] | Ikemura K, Tanaka H, Fujii T, et al. Design of a new, multi-purpose, light-curing adhesive comprising a silane coupling agent, acidic adhesive monomers and dithiooctanoate monomers for bonding to varied metal and dental ceramic materials [J]. Dent Mater J,2011,30(4)∶493-500 |
| [10] | Ikemura K, Jogetsu Y, Shinno K, et al. Effects of a newly designed HEMA-free, multi-purpose, single-bottle, self-etching adhesive on bonding to dental hard tissues, zirconia-based ceramics, and gold alloy [J]. Dent Mater J,2011,30(5)∶616-625 |
| [11] | Hahnel S, Henrich A, Burgers R, et al. Investigation of mechanical properties of modern dental composites after artificial aging for one year [J]. Oper Dent,2010,35(4)∶412-419 |
| [12] | Uhrenbacher J, Schmidlin PR, Keul C, et al. The effect of surface modification on the retention strength of polyetheretherketone crowns adhesively bonded to dentin abutments [J]. J Prosthet Dent,2014,112(6)∶1489-1497 |
| [13] | Williams DF, Mcnamara A, Turner RM. Potential of polyetheretherketone (PEEK) and carbon-fibre-reinforced PEEK in medical applications [J]. J Mater Sci Lett,1987,6(2)∶188-190 |
| [14] | Skinner HB. Composite technology for total hip arthroplasty [J]. Clin Orthop Relat Res,1988(235)∶224-236 |
| [15] | Keul C, Liebermann A, Schmidlin PR, et al. Influence of PEEK surface modification on surface properties and bond strength to veneering resin composites [J]. J Adhes Dent,2014,16(4)∶383-392 |
| [16] | De Munck J, Van Landuyt K, Peumans M, et al. A critical review of the durability of adhesion to tooth tissue: methods and results [J]. J Dent Res,2005,84(2)∶118-132 |
| [17] | 孙皎. 《口腔生物材料学》[M].北京:人民卫生出版社,2011∶165 |
| [18] | Cengiz S, Yuzbasioglu E, Cengiz M I, et al. Color Stability and Surface Roughness of a Laboratory-Processed Composite Resin as a Function of Mouthrinse [J]. J Esthet Restor Dent,2015,27(5)∶314-321 |