不同锌含量Zn/PLGA/HA复合支架对人牙髓干细胞粘附能力影响的体外研究
|
Abstract:
摘要 目的:制备含有不同锌含量的Zn/PLGA/HA复合支架并检测其机械性能;探讨不同锌含量的Zn/PLGA/HA复合支架在体外对人牙髓干细胞粘附能力的影响。方法:通过溶液浇铸/粒子沥滤法制备含锌质量分数0.5%、1%及2%的Zn/PLGA/HA复合支架,每组HA含量均为20%质量分数,对照组为不含锌的20%HA/PLGA支架。使用扫描电镜观察支架的表面形态,电子万能试验机检测支架的拉伸强度。将人牙髓干细胞接种在不同锌含量的Zn/PLGA/HA复合支架上培养,采用DAPI染色细胞计数法检测细胞粘附能力。结果:含锌质量分数1%和2%的Zn/PLGA/HA复合支架组拉伸强度均高于对照组(P<0.05)。扫描电镜观察到各组支架表面孔隙率均较高(87.6%),孔径158～372 μm,并具有良好的孔间连通性。0.5%Zn组支架与对照组相比具有较好的促牙髓干细胞粘附能力(P<0.05)。结论:本实验中,含1%,2% Zn(wt%)的Zn/PLGA/HA支架具有较好的机械性能,含0.5%Zn(wt%)的Zn/PLGA/HA支架在体外对人牙髓干细胞粘附具有更好的促进作用,为含锌支架作为支架材料用于组织工程提供了理论基础
| [1] | Horiuchi S, Hiasa M, Yasue A, et al. Fabrications of zinc-releasing biocement combini-ng zinc calcium phosphate to calcium phosphate cement [J]. Journal of Mechanical Behavior of Biomedical Materials,2014,29,151-160 |
| [2] | Sub H. Tissue restoration,tissue engineering an regenerative medicine [J]. Yonsei Med J,2000,41(6)∶681-684 |
| [3] | Balasubramanian P, Strobel LA, Kneser U, et al. Zinc-containing bioactive glasses for bone regeneration, dental and orthopedic applications [J]. Biomedical Glasses,2015, 1∶51-69 |
| [4] | Ghorbani FM, Kaffashi B, Shokrollahi P, et al. PCL/chitosan/Zn-doped nHA electrospun nano-composite scaffold promotes adipose derived stem cells adhesion and proliferation [J]. Carbohydr Polym, 2015;15,118∶133-142 |
| [5] | 王冉旭,潘爽,牛玉梅,等.人牙髓干细胞在不同HA含量的PLGA/HA复合支架材料上的粘附研究[J].口腔医学研究,2015,31(12)∶1171-1173 |
| [6] | Kim BS,Mooney DJ. Development of biocompatible synthetic extracellular matries for tissue engineering [J]. Trends Biotechnol,1998,16(5)∶224-230 |
| [7] | Ito A, Ojima K, Naito H, et al. Preparation,solubility,and cytocompatibility of zinc-releasing calcium phosphate ceramics [J]. J Biomed Mater Res, 2000,50(2)∶178-183 |
| [8] | Aina V, Perardi A, Bergandi L, et al. Cytotoxicity of zinc-containing bioactive glasses in contact with human osteoblasts [J]. Chemico-Biological Interactions,2007,167(3)∶207-218 |
| [9] | Schroeder JE, Mosheiff R. Tissue engineering approaches for bone repair:concepts and evidence [J]. Injury,2011,42(6)∶609-613 |
| [10] | 孙皎.口腔生物材料学[M].北京:人民卫生出版社,2016 |