钛表面接枝 大分子季铵盐抗菌性的研究
|
Abstract:
摘要 目的:在钛表面接枝大分子季铵盐,以增强钛种植体的表面抗菌效果。方法:采用表面引发原子转移自由基聚合反应(ATRP)引发甲基丙烯酸 N,N-二甲氨基乙酯 (DMAEMA)单体在钛片表面聚合,获得含叔胺基团的高分子聚合物刷,然后与十六烷基溴发生季铵化反应,在钛表面形成通过共价键连接的季铵盐涂层。用用静态接触角仪、傅立叶红外光谱仪(FTIR)、X射线光电子能谱(XPS)对改性的钛表面进行表征;以纯钛为对照组,季铵化后的钛片作实验组,分别在其表面进行变形链球菌(S.m)和大肠杆菌(E. coli )培养,4、 24 h后用荧光显微镜和扫描电镜 检测钛片表面的细菌活性。 结果:静态接触角仪、傅立叶红外光谱仪、X射线光电子能谱仪等结果证明大分子季铵盐被接枝到钛片表面。荧光显微镜显示无论是G+变形链球菌还是G-大肠杆菌,纯钛表面均有大量的活细菌;而实验组上细菌几乎全为死菌。SEM显示实验组钛片表面的细菌比空白组钛表面量明显少些,结果与荧光显微镜结果一致。结论:钛表面成功接枝大分子季铵盐物季铵盐,接枝大分子季铵盐的钛表面对变形链球菌和大肠杆菌具有显著的杀菌作用
| [1] | Meng HW. EY Chien, HH Chien. Dental implant bioactive surface modifications and their effects on osseointegration: a review [J]. BIOMARK RES, 2016, 4(1)∶24 |
| [2] | Gao, G, Yu K, Kindrachuk J, et al. Antibacterial surfaces based on polymer brushes: investigation on the influence of brush properties on antimicrobial peptide immobilization and antimicrobial activity [J]. BIOMACROMOLECULES, 2011, 12(10)∶3715 |
| [3] | Zhao L, Chu P K, Zhang Y, et al. Antibacterial coatings on titanium implants [J]. J BIOMED MATER RES B, 2010, 91B(1)∶470-480 |
| [4] | Maas F M, Da V D W, van Beusichem M L, et al. Bacterial colonization immediately after installation on oral titanium implants [J]. CLIN ORAL IMPLAN RES, 2007, 18(4)∶501-508 |
| [5] | 孟星,赵静辉,周延民,等.牙种植体骨感知现象的研究进展[J].口腔医学研究,2015,31(11)∶1156-1158 |
| [6] | 肖慧娟,杨云东,施斌,等.种植体即刻负重或早期负重与延期负重相比对种植体成功率影响的Meta分析[J].中国循证医学杂志,2008,8(2)∶120-126 |
| [7] | Antonucci JM, Zeiger DN, Tang K, et al. Synthesis and characterization of dimethacrylates containing quaternary ammonium functionalities for dental applications [J]. DENT MATER J, 2012, 28(2)∶219-228 |
| [8] | Windler L, Height M, Nowack B. Comparative evaluation of antimicrobials for textile applications [J]. ENVIRON INT, 2013, 53(2)∶62 |
| [9] | Mai L, Zhang S, Wang C, et al. Synthesis and antibacterial effect against Escherichia coli of TiO2:C composite film deposited on titanium [J]. ACTA SCI NAT U SUN, 2011, 50(6)∶82-87 |
| [10] | Videla, H.A. Prevention and control of biocorrosion [J]. INT BIODETER BIODEG, 2002, 49(4)∶259-270 |
| [11] | Fan X, Lin L, Dalsin JL, et al. Biomimetic anchor for surface-initiated polymerization from metal substrates [J]. J Am Chem Soc, 2005, 127∶15843-15847 |
| [12] | Fürst M M, Salvi G E, Lang N P, et al. Bacterial colonization immediately after installation on oral titanium implants [J]. CLIN ORAL IMPLAN RES, 2014, 18(4)∶501 |
| [13] | 左华江,温婉华,吴丁财,等.季铵盐类抗菌聚合物的研究现状[J].化工进展, 2013,32(10)∶2416-2422 |
| [14] | Chrcanovic BR, Albrektsson T, Wennerberg A, et al. Bisphosphonates and dental implants: A meta-analysis [J]. QUINTESSENCE INT, 2016, 24(5)∶505-516 |
| [15] | 付辉.不同种植系统口腔种植临床病例十年回顾性研究[D].山东大学, 2008 |
| [16] | Boyací E, Pawliszyn J. Micelle assisted thin-film solid phase microextraction: a new approach for determination of quaternary ammonium compounds in environmental samples [J]. ANAL CHEM, 2014, 86(18)∶8916 |
| [17] | 周轩榕,卢滇楠,邵曼君,等.表面接枝季铵盐型高分子材料抗菌过程的特性研究[J].高等学校化学学报,2003,24(6)∶1131-1135 |
| [18] | Guillaume B. Dental implants: A review [J]. MOR BULL De LAS Des ANA, 2016, 100(331)∶189-198 |