Obtaining of SiAlON Composite via Metal-Thermal and Nitrogen Processes in the SiC-Si-Al-Geopolymer System

DOI: 10.4236/jectc.2017.74009, PP. 103-122

Keywords: Alum-Thermal Process, Nitrogen Medium, SiAlON, SiC, Composite

Full-Text   Cite this paper   Add to My Lib

Abstract:

Goal: obtaining of composite in the SiC-SiAlON system with the metal thermal method in the nitrogen medium. Method: SiALON-s are solid metal oxide solutions in nitrides. Area of their presence is considered in four-component system-Si3N4-ALN-AL2O3-SiO2. In the present paper SiALON-containing composite was obtained through alum-thermal process in the nitrogen medium on the base of Geopolymer (kaolin and pologycley-Ukraine), SiC, aluminum nano-powder and Si powder with small additives of perlite (Aragatz, Armenia) by the reactive baking method. The advantage of this method is that compounds, which are newly formed thanks to interaction going on at thermal treatment: Si3N4, Si, AlN are active, which contributes to SiALON formation at relatively low temperature, at 1250°C - 1300°C. Results-β-SiAlON was formed at the sintering of SiC-aluminium and silicium powder, geopolymer at 1450°C. Porosity of carbide SiAlON composite obtained by reactive sintering, according to water absorption, equals to 13% - 15%. The samples were fragmented in a jaw-crusher and were powdered in attrition mill till micro-powder dispersion was obtained. Then samples were hot-pressed at 1620°C under 30 MPa pressure. Hold-time at the final temperature was 8 min. Sample water absorption, according to porosity, was less than 0.4%. Further studies were continued on these samples. Conclusion: the paper offers processes of formation of SiC-SiAlON composites and their physical and technical properties. Phase composition of the composites was studied by X-ray diffraction method, while the structure was studied by the use of optic and electron microscope. Electric properties showed that the specimen A obtained by hot-compression is characterized by 2 signs lower resistance than the porous material B, which was used to receive this specimen. Probably this should be connected with transition of the reactively baked structure of the hot-compressed material into compact structure. Obtained materials are used in protecting jackets of thermo couples used for melted metal temperature measuring (18 - 20 measuring) and for constructions used for placing objects in factory furnaces.

References

[1]  Shvedkov, E.L., Kovensky, I.I., Denisova, E.T. and Zyrin, A.V. (1991) Dictionary Reference Book for New Ceramics. Naukova Dumka, Kiev, 182.
[2]  Ekstrom, T., Kall, P.O., Nygren, M. and Olsson, P.O. (1989) Dense Single-Phase Beta-Sialon Ceramics by Glass-Encapsulated Hot Isostatic Pressing. Journal of Materials Science, 24, 1853-1862.
[3]  Rosenflanz, A. and Chen, I.W. (1999) Phase Relationships and Stability of α’-SiALON. Journal of the American Ceramic Society, 82, 25-28.
[4]  Strelov, K.K. (1996) Theoretical Bases in Technology of Refractory Materials: Handbook for High Institutions. 2nd Edition, 608.
[5]  Chukhalina, L.N. (2012) Method to Obtain SiAlON Powder.
http://bd.patent.su/2378000-2378999/pat/servl/servlet7175.html
[6]  Zheng, G., Zhao, J., Gao, Z. and Cao, Q. (2012) Cutting Performance and Wear Mechanisms at Sialon-Si3N4 Graded Nano-Composite Ceramic Cutting Tools. The International Journal of Advanced Manufacturing Technology, 58, 19-28.
[7]  Tressler, R.E. (1994) Theory and Experiment in Corrosion of Advanced Ceramics. In: Nickel, K.G., Ed., Corrosion of Advanced Ceramics, NATO ASI Series E: Applied Sciences, 3-22.
[8]  Piekarczyk, J., Lis, J. and Bialoskorski, J. (1990) Elastic Properties, Hardness and Indentation Fracture Toughness of Beta-Sialons. Key Engineering Materials, 89-91, 542-546.
[9]  Trigg, M.B. and Jack, K.H. (1988) SiAlON Ceramics. Journal of Materials Science, 23, 481-487.
[10]  Jiang, X., Baek, Y.K., Lee, S.M. and Kang, S.J.L. (1998) Formation of an α-SiAlON Layer on β-SiAlON and Its Effect on Mechanical Properties. Journal of the American Ceramic Society, 81, 1907-1912.
[11]  Zhen-Kun, H. (1994) Formation of N-Phase and Phase Relations in MgO-Si2N2O-Al2O3 System. Journal of the American Ceramic Society, 77, 3251.
[12]  Lavrienko, V.A., et al. (2005) High Temperature Oxidation of β-SiAlON Powders in Air Flush. Refractories and Technical Ceramics, No. 2, 8-11.
[13]  Phelps, F.E. (1990) Process for Producing Silicon Aluminum Oxynitride by Carbothermic Reaction. USA Patent No. 4977113.
[14]  Gauckler, L.J., Beshovic, S. and Petrow, G. (1977) Nitrogen Ceramics. In: Riley, F.L., Ed., Proceedings of the NATO Advanced Study Institute on Nitrogen Ceramics, Canterbury, 16-27 August, 1976, 405-414.
[15]  Yeh, C.L. and Sheng, K.C. (2011) Effect of α-Si3N4 and AlN Additional on Formation of α-SiAlON by Combustion Synthesis. Ibid, 509, 529-534.
[16]  Cutler, I.B. (1974) Process for Producing a Solid Solution of Aluminum Oxide in Silicon Nitride. Patente US3960581, 16.
[17]  Cho, Y.W. and Carles, J.A. (1991) Synthesis of Nitrogen Ceramic Powders by Carbothermal Reduction and Nitridation. Part 2 Silicon Aluminium Oxynitride (Sialon). Journal of Materials Science, 7, 399.
[18]  Gavrish, А.М., Puchkov, A.B., Boyarina, et al. (1988) β-SiAlOn Formation in the Si3N4-Al2O3-AlN System. Refractories, No. 8, 28-29.
[19]  Guzman, I.Y., Tumakova, E.I. and Fedotov, A.V. (1970) Correlative Study of Some Properties of Materials Based on Composites SiC+Si3N4 SiC-Si2N2, М. Refractories, No. 3, 44-48.
[20]  Ogbuji, L.U.J.T. (1992) Role of Si2N2O in the Passive-Oxidation of Chemically-Vapor-Deposited Si3N4. Journal of the American Ceramic Society, 75, 2995-3000.
[21]  Washburn, M.E. and Love, R.W. (1962) A Silicon Carbide Refractory with a Complex Nitride Bond Containing Silicon Oxynitride. American Ceramic Society Bulletin, 41, 447-449.
[22]  Кovziridze, Z.D. (1993) Development of Scientific Bases and Technology of Obtaining Celsian and Alumosilicate Ceramic by the Use of Barite and Perlite. Thesis for Scientific Degree of a Doctor of Technical Sciences, Tbilisi, 41-50.
[23]  Kovziridze, Z, Nizharadze, N., Tabatadze, D., Cheishvili, T., Mestvirishvili, Z., Nikoleishvili, E., Mshvildadze, M. and Darakhvelidze, N. (2014) Obtaining of Nanocomposites in SiC-SiAlON and Al2O3-SiAlON System by Alumothermal Processes. Journal of Electronics Cooling and Thermal Control, 4, 2-13.
[24]  Eftekhari Yekta, B. and Hamnabard, Z. (2013) Investigation of the Mechanical Properties and Machinability of Fluorphlogopite-Gehlenite Glass-Ceramics. Journal of Ceramic Science and Technology, 4, 193-196.
http://www.ceramic-science.com
[25]  Anstis, G.R., Chantikul, P., Lawn, B.R. and Marshall, D.B. (1981) A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness, Direct Crack Measurements. Journal of the American Ceramic Society, 64, 533.
[26]  Kovziridze, Z., Nizharadze, N., Tabatadze, G., Cheishvili, T., Mshvildadze, M., Mestvirishvili, Z. and Darakhvelidze, N. (2017) Ceramic and Advanced Technologies. Journal of Georgian Ceramists Association, 19, 3-9.
http://www.ceramics@gtu.ge
[27]  National Center of Intellectual Property of Georgia “Georgian Patent”, Certificate of Deposition 7136 (2017) Formula of Mechanical Modulus of Ceramic Materials and Composites.
[28]  Grifith, A.A. (1920) The Phenomena of Rupture and Flow in Solids, Philosophical Transactions of the Royal Society of London. Series A, Containing Papers of a Mathematical or Physical Character, 221, 163-198.
[29]  Kovziridze, Z., Nijaradze, N., Tabatadze, G., Cheishvili, T., Darakhvelidze, N., Mestvirishvili, Z., Mshvildadze, M. and Nikoleishvili, E. (2014) Obtaining of SiAlONs by Nitro-Alum-Thermal Processes. Journal of Association of Georgian Ceramists “Ceramics”, 2, 23-31.

Full-Text

Contact Us

service@oalib.com

QQ:3279437679

WhatsApp +8615387084133