深过冷ni-sn合金非规则共晶的形成机制
Abstract:
？采用熔融玻璃净化配合循环过热使ni-32.5%sn(质量分数)共晶合金实现了深过冷快速凝固.当过冷度大于某一临界值时,非规则共晶在凝固组织中出现.随着过冷度的提高,最终得到完全的非规则共晶组织.通过分析ni-sn共晶合金中各相形核、生长、以及枝晶熔断机制随过冷度的变化,解释了非规则共晶的形成机制.在深过冷条件下熔体中初生相率先形核并长入过冷熔体中,形成枝晶骨架,再辉重熔后次生相从残余熔体中析出并包围初生相,形成非规则共晶.
| [1] | 1s.v.raj,i.e.locci,j.d.whittenberger,instructuralintermetallics2001,developmentandevalutionofdirectionally-solidifiednial/(cr,mo)-basedeutecticalloysforairfoilapplications,editedbyk.j.hemker,d.m.dimiduk,h.clemens,r.darolin,h.inui,j.m.larsen,v.k.sikka,m.thomas,j.d.whittenberger(warrendale,pa,tms,2001)p.785
|
| [2] | 4r.darolia.ductilityandfracturetoughnessissuesrelatedtoimplementationofnialforgasturbineapplications,intermetallics,8,1321(2000)
|
| [3] | 5guojiantiug,cuichuanyong,zhoulanzhang,ligu-song,investigationonintermetallicnia1-cr(mo,hf)al-loys,actametal.sin.,38,1157(2002)(郭建亭，崔传勇，周兰章，李谷松，金属间化合物nial-cr(mo,hf)合金的研究，金属学报，38，1157(2002))
|
| [4] | 7r.s.polvani,w.s.tzeng,p.r.strutt,hightemperaturecreepinsemi-coherentnial-ni_2altialloy,metall.trans.,7a,33(1976)
|
| [5] | 10j.d.whittenberger,s.v.raj,i.e.locci,j.a.salem,effectofgrowthrateonelevatedtemperatureplasticflowandroomtemperaturefracturetoughnessofdirectionallyso-lidifiednial-31cr-3mo,intermetallies,7,1159(1999)
|
| [6] | 2j.d.whittenberger,i.e.locci,s.v.raj,j.a.salem,ele-vatedtemperaturestrengthandroom-temperaturetough-hessofdirectionallysolidifiedni-33al-33cr-1mo,metal.mater.trans.,33a,1385(2002)
|
| [7] | 3w.s.walston,r.darolia,instructuralintermetallics2001,propertiesandapplicationofnialeutectical-loys,editedbyk.j.hemker,d.m.dimiduk,h.clemens,r.darolia,h.inui,j.m.larsen,v.k.sikka,m.thomas,j.d.whittenberger(warrendale,pa,tms,2001)p.735
|
| [8] | 6c.y.cui,j.t.guo,y.h.qi,h.q.ye,deformationbehaviorandmicrostructureofdsnial/cr(mo)alloycontaininghf,intermetallics,10,1001(2002)
|
| [9] | 8xiaoxuan,guojianting,yuhalpeng,microstructureandmechanicalpropertiesofacastnial(ti)-cr(mo)eu-tecticalloy,actametal.sin.,42(10),1031(2006)(肖旋，郭建亭，于海朋，nial(ti)-cr(mo)共晶合金的微观组织和力学性能，金属学报，42(10)，1031(2006))
|
| [10] | 9s.v.raj,i.e.locci,microstructuralcharacterizationofadirectionally-solidifiedni-33(at.%)al-31cr-3moeutecticalloyasafunctionofwithdrawalrate,intermetallics,9,217(2001)
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|