新型生物降解交联剂的制备和交联壳聚糖的性能
Abstract:
？制备异氰酸酯基封端的一系列生物降解型交联剂,研究了反应条件对产物的影响.进一步使用此生物降解交联剂制备了交联壳聚糖多孔材料,研究了所得材料的性能.结果表明,当反应温度为70℃,反应时间为3h,投料比为2.2:1时,交联剂中nco的质量分数为4.64%,浓度为50%的thf溶液粘度为500mpa·s,其性能适宜交联壳聚糖.随着-nco/-nh2摩尔比的增加,交联壳聚糖多孔材料表面形貌呈现出从开孔结构逐渐过渡为闭孔结构的状态,保水率基本为未交联材料的3倍,其最大拉伸强度和弹性模量均有较大提高,最大为0.17gpa和1.4gpa.新型交联剂由于具有可降解的peg-b-pla链段,不仅保证了交联壳聚糖的降解性能,改善其亲水性,也提高了材料的力学性能
| [1] | 1j.ahubbell,r.langer,specialreport:tissueengineer-ing,c&en,march13,42(1995)
|
| [2] | 2n.a.peppas,r.langer,newchallengesinbiomaterials,science,263(5154),1715(1994)
|
| [3] | 3f.w.cooke,j.e.lemons,b.d.ratner,propertiesofma-terialsinbiomaterialsscience:anintroductiontoma-terialsinmedicine(academicpress,newyork,1996)
|
| [4] | 4o.a.monteiro,c.airoldi,somestudiesofcrosslink-ingchitosan-glutaraldehydeinteractioninahomoge-neoussystem,internationaljournalofbiologicalmacro-molecules,26(2～3),119(1999)
|
| [5] | 5c.g.liu,g.kashappa,h.desai,preparationandcharac-terizationofnanoparticlescontainingtrypsinbasedonhy-drophobicallymodifiedchitosan,j.agric.foodchem.,53(5),1728(2005)
|
| [6] | 6k.c.gupta,f.h.jabrail,glutaraldehydeandglyoxalcross-linkedchitosanmicrospheresforcontrolleddeliv-eryofcentchroman,carbohydrateresearch,341(6),744(2006)
|
| [7] | 7r.p.vijag,m.a.mansoor,preparationandcharacteriza-tionoffreeze-driedchitosan-poly(ethyleneoxide)hy-drogelsforsite-specificantibioticdeliveryinthestomach,pharm.res.,13,588(1996)
|
| [8] | 8z.k.yang,y.yang,studiesonthesynthesisandproper-tiesofhydroxylazacrownether-graftedchitosanj.appl.polym.sci.,82,1838(2001)
|
| [9] | 9h.s.bae,s.m.hudson,thecooperativebindingbehaviorofsodiumdodecylsulfatetocrosslinkedchitosanfilms,j.polym.sci.a:polym.chem.,35,3755(1997)
|
| [10] | 10r.w.eric,r.p.ronald,chitosancross-linkingwithawa-tersoluble,blockeddiisocyanate.2.solvatssandhydrogel-lls,biomacromolecules,4,1357(2003)
|
| [11] | 12d.w.jenkins,s.m.hudson,reviewofvinylgraftcopolymerizationfeaturingrecentadvancestowardcon-trolledradical-basedreactionsandillustratedwithchitin/chitosantrunkpolymers,chem.rev.,101(11),3245(2001)
|
| [12] | 13h.sashiwa,n.kawasaki,s.aiba,chemicalmodificationofchitosan.part15:synthesisofnovelchitosanderiva-tivesbysubstitutionofhydrophilicamineusingn-carboxyethylchitosanethylesterasanintermediate,car-bohydrateres.,338(6),557(2003)
|
| [13] | 14m.alexandra,v.christophe,d.alaln,rheometricstudyofthegelationofchitosaninaqueoussolutionwithoutcross-linkingagent,biomacromolecules,6(2),653(2005)
|
| [14] | 19jiangxin,chenlianxi,hejianhua,studyonsyn-thesisandpurificationoflactide,j.wuhanuniversityoftechnology,24(4),42(2002)(江昕,陈连喜,贺建华等,丙交酯的合成与纯化研究,武汉理工大学学报,24(4),42(2002))
|
| [15] | 20d.k.han,j.a.hubbell,synthesisofpolymernetworkscaf-foldsfrom1-lactideandpoly(ethyleneglycol)andtheirin-teractionwithcells,macromolecules,30(20),6077(1997)
|
| [16] | 21r.l.dunn,j.p.english,d.f.vanderbilt,biodegradebletissueadhesives,polym.prepr.,30(1),501(1989)
|
| [17] | 22d.j.gravet,k.d.janda,organicsynthesisonsolublepoly-mersupports:liquid-phasemethodologies,chem.rev.,97(2),489(1997)
|
| [18] | 23r.w.eric,l.s.caroline,b.q.syed,chitosancross-linkingwithawatersoluble,blockeddiisocyanate.2.solidstate,biomacromolecules,3,1370(2002)
|
| [19] | 11b.d.ratner,a.s.hoffman,f.j.shoen,j.e.lemons(eds.),biomaterialsscience:anintroducitontomaterialsinmedicine(academicpress,sandiego,1996)
|
| [20] | 15a.t.metters,k.s.anseth,c.n.bowman,fundamentalstudiesofanovel,biodegradablepeg-b-plahydrogel,polymer,41(11),3993(2000)
|
| [21] | 16a.t.metters,c.n.bowman,k.s.anseth,materials,inter-faces,andelectrochemicalphenomenon:verificationofscalinglawsfordegradingpla-b-peg-b-plahydro-gels,journalofaiche,47(6),1432(2001)
|
| [22] | 17a.s.sawhney,p.p.chandrashekhar,j.a.hubbell,bioerodiblehydrogelsbasedonphotopolymerizedpoly(ethyleneglycol)-co-poly(a-hydroxyacid)diacry-latemacromers,macromolecules,26(4),581(1993)
|
| [23] | 18j.l.west,j.a.hubbell,photopolymerizedhydrogelma-terialsfordrugdeliveryapplications.reactivepolym.,25(2～3),139(1995)
|
| [24] | 24weihongliang,yuhuaiqing,qianlijun,one-potsyn-thesisofmacromerofpla-peg-platerminatedwithmethacryloylmoiety,journaloffunctionalpolymers,18(1),72(2005)(魏宏亮,于怀清,钱立军,一锅法合成甲基丙烯酰基封端的pla-peg-pla大分子单体,功能高分子学报,18(1),72(2005))
|
| [25] | 25j.blanchette,n.kavimandan,n.a.peppas,principlesoftransmucosaldeliveryoftherapeuticagents,biomedicine&pharmacotherapy,58,142(2004)
|
| [26] | 26a.ozkan,m.yekeler,anewmicrocolumnflotationcellfordeterminingthewettabilityandfloatabilityofmin-erals,journalofcolloidandinterfacescience,261(2),476(2003)
|
| [27] | 27j.kohn,r.langer,bioresortableandbioerodiblemateri-als(academicpress,sandiego,1996)
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|