马氏体冷轧-回火制备超细晶钢及其热稳定性
Keywords: 金属材料,超细晶,冷轧马氏体,回火,微合金钢
Abstract:
？在低碳钢和低碳加铌、钒、钛微合金钢中,通过马氏体冷轧--回火的方法获得了尺寸为数百纳米的超细晶粒铁素体组织,研究了超细晶粒组的形成机制和热稳定性.通过马氏体相变在这些钢中引入了大量高密度位错,马氏体冷轧后位错进一步增殖,形成大量位错胞状结构;在500-600℃进行的60min回火将上述胞状结构转变成具有清晰大角晶界的超细晶粒.在回火过程中形成的微合金元素碳化物对位错运动和晶界移动具有有效的“钉扎”作用,有助于获得超细晶组织并明显提高其热稳定性.
| [1] | 3v.v.stolyarov,y.t.zhu,t.c.lowe,r.k.islamgalievandr.z.valiev,twostepspdprocessingofultrafine-grainedtitanium,nanostructuredmaterials,11,947(1999)
|
| [2] | 6n.tsuji,y.saito,h.utsunomiya,s.tanigawa,ultra-finegrainedbulksteelproducedbyaccumulativeroll-bonding(arb)process,scriptamaterialia,40,795(1999)
|
| [3] | 7n.tsuji,r.ueji,y.minamino,y.saito,anewandsimpleprocesstoobtainnano-structuredbulklow-carbonsteelwithsuperiormechanicalproperty,scriptamaterialia,46,305(2002)
|
| [4] | 10x.zhao,t.f.jing,y.w.gao,j.f.zhou,w.wang,anneal-ingbehaviorofnano-layeredsteelproducedbyheavycold-rollingoflathmartensite,materialsscienceanden-gineeringa,397,117-121(2005)
|
| [5] | 11s.morito,h.tanaka,r.konishi,t.furuhara,t.maki,themorphologyandcrystallographyoflathmartensiteinfe-calloys,actamaterialia,51,1790(2003)
|
| [6] | 12hiromotokitahara,rintaroueji,nobuhirotsuji,yori-toshiminamino,crystallographicfeaturesoflathmarten-siteinlow-carbonsteel,actamaterialia,54,1282-1283(2006)
|
| [7] | 13d.kuhlmann-wilsdorf,nielshansen,geometricallynec-essary,incidentalandsubgrainboundaries,scriptamet-allurgica&materialia,25,1557-1559(1991)
|
| [8] | 14n.tsuji,r.ueji,y.saito,y.koizumi,y.minamino,anovelprocesstoobtainnanostructuredlow-carbonbulksteelwithhighstrength,in:proc.ofthe21strisφint.symponmaterialsscience,editedbya.r.dinesenm.eldrup(risφnationallaboratory,roskilde,2001)p.607-616
|
| [9] | 15rolfsandstrom,onrecoveryofdislocationsinsubgrainsandsubgraincoalescene,actametallurgica,25,897-904(1997)
|
| [10] | 16j.w.christian,thetheoryoftransformationsinmetalsandalloys,thirdedition(netherlands,pergamon,2002)p.836
|
| [11] | 18r.k.davies,v.randle,g.j.marshall,continuousrecrystallization-relatedphenomenainacommercialal-fe-sialloy,actamater.,46,6021(1998)
|
| [12] | 19t.maki,dynamicrecrystallizationandgrainrefinementofvvarioussteels,in:the3rdinternationalconferenceonadvancedstructuralsteels(gyeongju,2006)p.73
|
| [13] | 20c.zener,quotedbyc.s.smith,grains,phasesandinter-faces:aninterpretationofmicrostructure,trans-aime,175,15(1948)d
|
| [14] | 1yuntiantheodorezhu,terryc.lowe,observationsandissuesonmechanismsofgrainrefinementduringecapprocess,materialsscienceandengineeringa,291,46(2000)
|
| [15] | 2zenjihorita,takayoshifujinami,terenceg.langdon,thepotentialforscalingecap-effectofsamplesizeongrainrefinementandmechanicalproperties,materialssci-enceandengineeringa,318,34(2001)
|
| [16] | 4donghyukshin,kyung-taepark,ultrafinegrainedsteelsprocessedbyequalchannelangularpressing,ma-terialsscienceandengineeringa,410-411,299(2005)
|
| [17] | 5y.saito,n.tsuji,h.utsunomiya,t.sakai,r.g.hong,ultra-finegrainedbulkaluminumproducedbyaccumula-tiveroll-bonding(arb)process,scriptamaterialia,39,1221(1998)
|
| [18] | 8r.ueji,n.tsuji,y.minamino,y.koizumi,ultragrainre-finementofplainlowcarbonsteelbycold-rollingandan-nealingofmartensite,actamater.,50,4177(2002)
|
| [19] | 9rintaroueji,nobuhirotsuji,yoritoshiminamino,yuichirokoizumi,effectofrollingreductiononultrafinegrainedstructureandmechanicalpropertiesoflow-carbonsteelthermomechanicallyprocessedfrommartensitestart-ingstructure,scienceandtechnologyofadvancedmate-rials,5,153(2004)
|
| [20] | 17a.belyakov,t.sakai,h.miura,r.kaibyshev,k.tsuzaki,continuousrecrystallizationinausteniticstainlesssteelaf-terlargestraindeformation,actamater.,50,1547(2002)
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|