电泳沉积制备氧化钇稳定的二氧化锆薄膜
Keywords: 无机非金属材料,电泳沉积,薄膜,钇稳定的二氧化锆
Abstract:
？采用恒压电泳沉积方法在ni-ysz(氧化钇稳定的氧化锆)阳极基体上制备ysz电解质膜,研究了悬浮体系ysz含量、外加电压、沉积时间对电泳过程及ysz膜层质量的影响.结果表明,ysz含量为20g/l,沉积电压为10v,沉积时间\linebreak5min时,恒压电泳一次即可得到均匀致密的ysz膜.膜层与基体结合紧密,厚度约为10？μm.
| [1] | 11i.zhitomirsky,a.petric,electrophoreticdepositionofceramicmaterialsforfuelcellapplications,j.eur.ceram.soc.,20,2055(2000)
|
| [2] | 13zhangheng,dongxinfa,linweiming,theapplicationofelectrophoreticdepositiontechniqueforpreparingsofcelectrolytefilms,chinesejournalofpowersources,29(12),837(2005)
|
| [3] | (张恒,董新法,林维明,电泳沉积在制备sofc电解质膜中的应用,电源技术,29(12),837(2005))
|
| [4] | 14lulizhu,huhusheng,xiehuiqin,lilingchuan,mechanismandkineticsofelectrophoreticdeposition(epd)ofyttria-stabilizedzirconia(ysz)film,engineeringchemistry&metallurgy,19(2),97(1998)
|
| [5] | (卢立柱,胡湖生,谢慧琴,李陵川,电泳沉积法制备固体电解质薄膜的沉积速率和沉积机理,化工冶金,19(2),97(1998))
|
| [6] | 18y.h.lee,c.w.kuo,c.j.shih,i.m.hung,k.z.fung,s.b.wen,m.c.wang,characterizationontheelectrophoreticdepositionofthe8mol%yttria-stabilizedzirconiananocrystallitespreparedbyasol-gelprocess,materialsscienceandengineeringa,445-446,347(2007)
|
| [7] | 1hanminfang,pengsuping,solidoxidefuelcellcomponentsandmanufactureprocesses(beijing,chinesesciencepress,2004)p.19
|
| [8] | (韩敏芳,彭苏萍,固体氧化物燃料电池材料及制备(北京,科学出版社,2004)p.19))
|
| [9] | 2b.uday,electrochemicalvapordepositionofsolidoxidefilms,solidstateionics,52,227(2002)
|
| [10] | 3j.will,a.mitterdorfer,c.kleinlogel,d.perednis,l.j.gauckler,fabricationofthinelectrolytesforsecondgenerationsolidoxidefuelcells,solidstateionics,131(1-2),79(2000)
|
| [11] | 4changjiuli,chengxinli,influenceofyszelectrolytethicknessonthecharacteristicsofplasma-sprayedcermetsupportedtubularsofc,solidstateionics,177,2065(2006)
|
| [12] | 5changrongxia,huaqiangcao,hongwang,pinghuayang,guangyaomenganddingkunpeng,sol-gelsynthesisofyttriastabilizedzirconiamembranesthroughcontrolledhydrolysisofzirconiumalkoxide,journalofmembranescience,162(1-2),181(1999)
|
| [13] | 6yaohuizhang,xiqianghuang,zhelu,xiaodongge,jiahuaxu,xianshuangxin,xueqingsha,wenhuisu,effectofstartingpowderonscreen-printingyszfilmusedaselectrolyteinsofcs,solidstateionics,177,281(2006)
|
| [14] | 7lijigang,sunkening,kongjiangrong,fabricationofni-ysz/yszcompoundsubstratemembranesusingtapecastingmethodandperformancemeasurements,chemicalindustryandengineeringprogress,27(1),135(2008)
|
| [15] | (李吉刚,孙克宁,孔江榕,流延法制备ni-ysz/ysz复合基膜及性能测试,化工进展,27(1),135(2008))
|
| [16] | 8h.negishi,n.sakai,k.yamaji,applicationofelectrophoreticdepositiontechniquetosolidoxidefuelcells,j.electrochem.soc.,147,1682(2000)
|
| [17] | 9j.will,m.hrushka,l.gubler,electrophoreticdepositionofzirconiaandporousanodicsubstrates,j.am.ceram.soc.,84,328(2001)
|
| [18] | 10t.ishishara,k.sato,y.takita,electrophoreticdepositionofy2o3stabilizedzro2electrolytefilmsinsolidoxidefuelcells,j.am.ceram.soc.,79,913(1996)
|
| [19] | 12h.negishi,k.yamaji,electrophoreticdepositionofyszpowdersforsofc,journalofmaterialsscience,39,833(2004)
|
| [20] | 15lulizhu,dianhongwei,xiehuiqin,fabricationofyttria-stabilizedzirconia(ysz)filmbycombinedoperationofelectrophoreticdepositionandelectrochemicaldeposition,chinesejournalofmaterialsresearch,15(5),525(2001)
|
| [21] | (卢立柱,赁泓威,谢慧琴,用电泳沉积-电沉积联合法制备二氧化锆(ysz)薄膜,材料研究学报,15(5),525(2001))
|
| [22] | 16i.zhitomirsky,l.galor,electrophoreticdepositionofhydroxyapatite,journalofmaterialscience:materialinmedicine,8(4),213(1997)
|
| [23] | 17i.zhitomirsky,a.petric,electrophoreticdepositionofelectrolytematerialsforsolidoxidefuelcells,journalofmaterialscience,39,825(2004)
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|