铁素体/贝氏体双相钢的变形和断裂特性
Keywords: 金属材料,铁素体/贝氏体双相钢,单轴拉伸,变形行为,断裂特性
Abstract:
？对一种低碳硅锰钢进行tmcp实验,获得了不同铁素体形态的铁素体/贝氏体双相钢(fb钢).研究了fb钢在单轴拉伸下的变形行为及断裂特性,结果表明:在均匀塑性变形阶段,fb钢的瞬时加工硬化指数n*值与真应变ε的关系曲线可分为n*值较高、n*值随ε缓慢下降以及n*值随ε迅速下降三个阶段.与等轴铁素体/贝氏体双相钢相比,准多边形铁素体/贝氏体双相钢的强度和低应变区的n*值均比较高.fb钢拉伸试样颈缩区的孔洞或微裂纹产生在f--b相界面附近和铁素体内,有助于减弱裂纹尖端附近的局部应力集中,改善钢材的抗裂纹扩展性能.
| [1] | (康永林,现代汽车板的质量控制与成形性(北京,冶金工业出版社,1999)p.129)
|
| [2] | 3m.takahashi,developmentofhighstrengthsteelsforautomobiles,nipponsteeltechnicalreport,88,3(2003)
|
| [3] | 4a.barbacki,theroleofbainiteinshapingmechanicalpropertiesofbainite,journalofmaterialsprocessingtechnology,53,57(1995)
|
| [4] | (许云波,于永梅,吴迪,王国栋,低温变形nb微合金钢铁素体相变的数学模型,材料研究学报,20(2),131(2006))
|
| [5] | 1a.kumar,s.b.singh,k.k.ray,influenceofbainite/martensite–contentonthetensilepropertiesoflowcarbondual–phasesteels,materialsscienceengineeringa,474,270(2008)
|
| [6] | 2kangyonglin,qualitycontrollingandformingpropertyofmodernautomobilesteelplates(beijing,thepressofmetallurgicalindustry,1999)p.129
|
| [7] | 5xupingguang,fanghongsheng,baibingzhe,wangzhenjia,yangzhigang,huangjinfeng,newduplexmicrostructureofgrainboundaryallotriomorphicferrite/granularbainite,journalofironandsteelresearchinternational,9(2),33(2002)
|
| [8] | 6xupingguang,baibingzhe,fanghongsheng,wangzhenjia,wangjianping,panyongkun,developmentofgrainboundaryallotriomorphicferrite/granularbainiteduplexsteel,journalofuniversityofscienceandtechnologybeijing,10(2),39(2003)
|
| [9] | 7lilong,dinghua,dulinxiu,songhongmei,zhengfang,microstructuresandmechanicalpropertyoflowcarbonmanganesesteelwithgrainboundaryallotriomorphicferrite/bainitestructure,actametallurgicasinica,42(11),1227(2006)
|
| [10] | (李龙,丁桦,杜林秀,宋红梅,郑芳,仿晶界型铁素体/贝氏体低碳锰钢的组织和力学性能,金属学报,42(11),1227(2006))
|
| [11] | 8lilong,dinghua,wenjinglin,songhongmei,zhangpijun,mechanicalbehaviorsofalowcarbonsteelwithaduplexmicrostructureofbainiteandferrite,chinesejournalofmaterialsresearch,21(5),517(2007)
|
| [12] | (李龙,丁桦,温景林,宋红梅,张丕均,铁素体/贝氏体复相组织低碳钢的力学特性,材料研究学报,21(5),517(2007))
|
| [13] | 9xuyunbo,yuyongmei,wudi,wangguodong,mathematicalmodelofferritetransformationofnbmicroslloyedsteelsthroughlowtemperatureheavydeformation,chinesejournalofmaterialsresearch,20(2),
|
| [14] | 131(2006)
|
| [15] | 10mamingtu,dual–phasesteels–metallurgyofphysicsandmechanics(beijing,thepressofmetallurgicalindustry,1988)p.137
|
| [16] | (马鸣图,双相钢--物理和力学冶金(北京,冶金工业出版社,1988)p.137)
|
| [17] | 11p.c.m.rodrigues,ev.pereloma,d.b.santos,mechanicalprosperitiesofanhslabainiticsteelsubjectedtocontrolledrollingwithacceleratedcooling,materialsscienceengineeringa,283,136(2000)
|
| [18] | 12qianzhiping,deformationandfractureofmaterials(shanghai,thepressoftongjiuniversity,1989)p.270
|
| [19] | (钱志平,材料的变形与断裂(上海,同济大学出版社,1989)p.270)
|
| [20] | 13m.erdogan,theeffectofnewferritecontentonthetensilefracturebehaviorofdualphasesteels,journalofmaterialsscience,37,3623(2002)
|
| [21] | 14k.hasegawa,k.kawamura,t.urabe,y.hosoya,effectsofmicrostructureonstretch–flange–formabilityof980mpagradecold–rolledultrahighstrengthsteelsheets,isijinternational,44(3),603(2004)
|
| [22] | 15m.f.shi,sunzhongming,comparingmouldingpropertiesbetweendual–phasesteelandhslasteel,theworldiron&steel,4,18(2002)
|
| [23] | (m.f.shi,孙忠明,双相钢和低合金高强度钢成形性能的对比,世界钢铁,4,18(2002))
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|