csp变形过程中碳化铌析出的动力学模型
Abstract:
?本文在经典形核和长大理论模型的基础上,建立了适用于薄板坯连铸连轧(csp)变形过程中nbc析出的动力学模型.该模型考虑了不同扩散速率原子的质量守恒、软撞击及毛细管效应,并假设碳化物主要在位错上析出,位错密度按照atsuhiko模型计算.计算结果表明,在不发生软化行为的情况下,按照某实际csp生产线生产工艺六道次变形后,fe-0.046nb-0.053c%(质量分数)钢的平均位错密度为3×1013m-2,开轧2s后nbc开始析出.随着轧制过程的进行,nbc的最大半径逐渐增大,六道次轧制后最大半径为57nm.随着轧制过程的进行、变形量的增大以及温度的降低,nbc的平均半径逐渐增大.轧制完成的瞬时钢中析出的nbc粒子的平均半径为27nm,体积分数为0.0011%,后者远低于对应的平衡体积分数0.0496%.
References
[1] | 1yinruiyu.progressandprospectofthinslabcastingandrollingprocessinchina.ironandsteel,41(7),1(2006)(殷瑞钰,中国薄板坯连铸连轧的进展与展望,钢铁,41(7),1(2006))
|
[2] | 2sunjueding,dingshixue,technologicalcharacteristicsofthinslabcontinuouscasting-rollingprocessinchina,researchoniron&steel.,144(3),58(2005)(孙决定,丁世学,我国薄板坯连铸连轧生产技术特点,钢铁研究,144(3),58(2005))
|
[3] | 14a.yoshie,t.fujita,m.fujioka,k.okamoto,h.morikawa,formulationofthedecreaseindislocationdensityofde-formedausteniteduetostaticrecoveryandrecrystalliza-tion,isijint.,36(4),474(1996)
|
[4] | 15b.dutta,e.valdes,c.m.sellars,mechanismandkineticsofstraininducedprecipitationofnb(c,n)inaustenite,actametall.mater.,40(4),653(1992)
|
[5] | 16b.dutta,e.j.palmiere,c.m.sellars,modelingthekineticsofstraininducedprecipitationinnbmicroalloyedsteels,actamater.,49,785(2001)
|
[6] | 3w.j,liu,anewtheoryandkineticmodelingofstrain-inducedprecipitationofnb(cn)inmicroalloyedausten-ite,metall.mater.trans.,26a,1641(1995)
|
[7] | 4b.dutta,c.m.sellars,effectofcompositionandprocessvariableonnb(c,n)precipitationinniobiummicroal-loyedaustenite.mater.sci.techno.,3,197(1987)
|
[8] | 5d.q.bai,s.yue,w.p.sun,j.j.jonas,effectofdeforma-tionparametersontheno-recrystallizationtemperatureinnb-bearingsteel,metall.trans.,24,2151(1993)
|
[9] | 6s.okaguchi,t.hashimoto,computermodelforpredictionofcarbonitrideprecipitationduringhotworkinginnb-tibearinghslasteels,isijint.,32(3),283(1992)
|
[10] | 7n.fujita,h.k.d.h.bhadeshia,modellingprecipitationofniobiumcarbideinaustenite:multicomponentdiffusion,capillarityandcoarsening,mater.sci.techno.,17(4),403(2001)
|
[11] | 8n.fujita,h.k.d.h.bhadeshia,precipitationofmolybde-numcarbideinsteel:multicomponentdiffusionandmulti-ocomponentcapillaryeffects,mater.sci.techno.,15(6),627(1999)
|
[12] | 9j.w.christian,theoryoftransformationsinmetalsandalloys,part13rdedition,oxford,pergamonpress,2002
|
[13] | 10n.fujita,h.k.d.h.bhadeshia,m.kikuchi,precipitationsequenceinniobium-alloyedferriticstainlesssteel,mod-ellingsimul.mater.sci.eng.,12(4),273(2004)
|
[14] | 11s.h.park,s.yue,j.j.jonas,continuous-cooling-precipitationkineticofnb(c,n)inhigh-strengthlow-ailoysteels,metall.trans.,23(a),1641(1992)
|
[15] | 12h.s.zurob,y.brechet,g.purdy,amodelforthecompe-titionofprecipitationandrecrystailizationindeformedausetnite,actamater.,49,4183(2001)
|
[16] | 13a.yoshie,t.fujita,m.fujioka,k.okamoto,h.morikawa,formulationofflowstressofnbaddedsteelsbyconsid-eringwork-hardeninganddynamicrecovery,isijint.,36(4),467(1996)
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|