热处理对大截面7a04铝合金棒材力学性能的影响
Abstract:
？研究了热处理对7a04铝合金力学性能的影响.结果表明,直径60mm的7a04铝合金棒材在200℃电流直接加热回归后再时效,从心部到表层的拉伸强度为620--640mpa,延伸率均匀一致;在3%nacl+0.5\%h$_{2}$o$_{2}$水溶液介质中和375mpa应力下的应力腐蚀断裂时间大于30d,而辐射式加热回归的为575mpa,延伸率从心部至表层表现极不均匀,应力腐蚀断裂时间只有19d.电流直接加热实现了直径60mm7a04铝合金大截面棒材的快速均匀回归,再时效获得了最弥散的晶内析出粒子和尺寸及间距较大的晶界析出相,使合金在保持t6状态拉伸强度的同时,具有优良的抗应力腐蚀性能.
| [1] | 9k.rajan,w.wallace,j.c.beddoes,microstructuralstudyofahighstrength-stress-corrosionresistant7075alu-minumalloy,j.mat.sci.,17,2817(1982)
|
| [2] | 10wuyilei,liyongwei,qiangjun,lichunyu,develop-mentandapplicationofsuper-highstrengthaluminumal-loy,journalofaeronauticalmaterials,2(1),49(1994)(吴一雷，李永伟，强俊，李春玉，超高强度铝合金的发展和应用．航空材料学报，2(1)，49(1994))
|
| [3] | 12s.h.paul,soluteeffectsonelectromigration,phys.rev.b,8,4534(1973)
|
| [4] | 13r.landauer,j.w.f.woo,drivingforceinelectromigra-tion,phys.rev.b,10,1266(1974)
|
| [5] | 14liuzhiyi,xuxiaochang,cuijianzhong,effectofelec-triccurrentoulseongraingrowthinsuperplasticdefor-mationof2091al-lialloy.transactionsofnonferrousmetalssocietyofchina,13(4),743(2003)
|
| [6] | 15liuzhiyi,liubing,dengxiaotie,leiyi,cuijianzhong,baiguangrtm,effectofcurrentpulseonmechanismofsuperplasticdeformationof2091al-lial-loy,acta.metall.sinica,36(9),944(2000)(刘志义，刘冰，邓小铁，雷毅，崔建忠，白光润，脉冲电流对2091al-li合金超塑变形机理的影响，金属学报，36(9)，944(2000))
|
| [7] | 16liuzhiyi,dengxiaotie,wangyinzhen,effectsofelectriccurrentpulseonthedynamicsofdynamicrecrys-tallizationin2091al-lialloy,chinesejournalofmateri-alsresearch,15(3),358(2001)(刘志义，邓小铁，王引真，脉冲电流对2091铝锂合金动态再结晶动力学的影响，材料研究学报，15(3)，358(2001)
|
| [8] | 17j.r.rickens,l.christodoulou,thestress-corrosioncrack-ingbehaviorofhighstrengthaluminumpowdermetallurgealloys,metall.trans.,18a(1),135(1987)
|
| [9] | 1b.cina,u.s.patent3856584,december24,1974
|
| [10] | 2w.wallace,j.c.beddoes,m.c.demalherbe,anewap-proachtotheproblemofstresscorrosioncrackingin7075-t6aluminum.canadianaeronauticsandspacejournal,27,222(1981)
|
| [11] | 3m.u.islam,w.wallace,retrogressionandreagingre-sponseof7475aluminiumalloy.metalstechnology,10(10),386(1983)
|
| [12] | 4c.d.nguyen,k.rajan,w.wallace,atemstudyofmi-crostructuralchangesduringretrogressionandreagingin7075aluminumalloy.metallurgicaltransactionsa(phys-icalmetallurgyandmaterialsscience),14(9),1843(1983)
|
| [13] | 5n.danh,k.rajan,w.wallace,discussionofeffectofret-rogressionandreagingtreatmentsonthemicrostructureofal-7075-t651.metallurgicaltransactionsa(physicalmetallurgyandmaterialsscience),16(11),2068(1985)
|
| [14] | 6m.u.islam,w.wallace,stresscorrosioncrackgrowthbe-haviourof7475t6retrogressedandreagedaluminumal-loy.metalstechnology,11(8),320(1984)
|
| [15] | 7r.t.holt,v.r.parameswaran,w.wallace,rratreat-mentof7075-t6aluminumcomponents,canadianaero-nauticsandspacejournal,42(2),83(1996)
|
| [16] | 8j.c.lin,h.l.liao,w.d.jehng,c.h.chang,s.l.lee,ef-fectofheattreatmentsonthetensilestrengthandscc-resistanceofaa7050inanalkalinesalinesolution,corro-sionscience,48,3139(2006)
|
| [17] | 11d.a.luckasak,r.m.hart,aluminumalloydevelopmenteffortsforcompressiondominatedstructureofaircraft.lightmetalage,10,11(1991)
|
| [18] | 18a.thakur,r.raman,s.n.malhotra,hydrogenembrittle-mentstudiesofagedandretrogressed-reagedal-zn-mgalloys,materialschemistryandphysics,101,441(2007)
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|