CLAM钢焊接热影响区连续冷却过程相变规律

DOI: 10.3969/j.issn.1001-4381.2013.04.013, PP. 68-73

Keywords: 中国低活化马氏体钢,焊接热模拟,热影响区,连续冷却转变曲线

Full-Text   Cite this paper   Add to My Lib

Abstract:

采用Gleeble1500热模拟机,物理模拟中国低活化马氏体(CLAM)钢焊接热影响区粗晶区(CGHAZ)的冷却过程,结合组织观察、Thermo-calc热力学软件计算和硬度测试等手段分析了冷速ωc对CGHAZ的组织演变及硬度的影响,并绘制了CLAM钢的SH-CCT图。结果表明CLAM钢的CGHAZ中过冷奥氏体仅发生低温板条马氏体(LM)及先共析铁素体(α铁素体)转变。0.25℃/s为CGHAZ过冷奥氏体发生完全LM相变的临界冷速。当ωc>0.25℃/s时,CGHAZ的组织除LM外,还含有少量的δ铁素体,δ铁素体是δ→γ相变阶段转变不充分而残留至室温的组织,在该冷速范围内粗晶区的组织形态变化不明显。当ωc<0.25℃/s时,由于发生γ→α转变,CGHAZ的组织为α铁素体及LM的混合组织,随着冷速的降低,α铁素体含量增加;当ωc=0.04℃/s时,CGHAZ的组织已完全转变为α铁素体和碳化物的混合组织。

References

[1]  HISHINUMA A, KOHYAMA A, KLUEH R L, et al. Current status and future R&D for reduced-activation ferritic/martensitic steels[J]. Journal of Nuclear Materials,1998,258-263(1):193-204.
[2]  拉达衣.焊接效应·温度场、残余应力、变形[M].熊第京,郑朝云,史耀武,等译.北京:机械工业出版社,1997.36-38.
[3]  POITEVIN Y, BOCCACCINI L V, DELL’ORCO G, et al. The test blanket modules project in Europe: from the strategy to the technical plan over next 10 years[J]. Fusion Engineering and Design,2007,82(15-24):2164-2170.
[4]  GASPAROTTO M, ANDREANI R, BOCCACCINI L V, et al. Survey of in-vessel candidate materials for fusion power plants-the european materials R&D programme[J]. Fusion Engineering and Design,2003,66-68(1):129-137.
[5]  WAKAI E, OHTSUKA H, MATSUKAWA S, et al. Mechanical properties of small size specimens of F82H steel[J]. Fusion Engineering and Design,2006,81(8-14):1077-1084.
[6]  TANIGAWA H, HIROSE T, SHIBA K, et al. Technical issues of reduced activation ferritic/martensitic steels for fabrication of ITER test blanket modules[J].Fusion Engineering and Design, 2008,83(10-12):1471-1476.
[7]  李华杰,武会宾,唐荻.中国低活化马氏体钢组织性能及强化机理[J]. 北京科技大学学报,2011,33(2):166-171.LI Hua-jie,WU Hui-bin,TANG Di. Microstructure, properties and strengthening mechanism of China low activation martensitic steel[J]. Journal of University of Science and Technology Beijing,2011,33(2):166-171.
[8]  黄群英,郁金南,万发荣,等.聚变堆低活化马氏体钢的发展[J].核科学与工程,2004,24(1):56-64.HUANG Qun-ying,YU Jin-nan,WAN Fa-rong,et al. The development of low activation martensitic steels for fusion reactor[J]. Chinese Journal of Nuclear Science and Engineering,2004,24(1):56-64.
[9]  HUANG Q, LI C, LI Y, et al. Progress in development of China low activation martensitic steel for fusion application[J].Journal of Nuclear Materials,2007,367-370(1):142-146.
[10]  刘松林,柏云清,陈红丽,等.ITER氚增殖实验包层设计研究进展[J].核科学与工程,2009,29(3):266-273.LIU Song-lin,BAI Yun-qing,CHEN Hong-li,et al. Progress in design and study of ITER test blanket modules[J]. Chinese Journal of Nuclear Science and Engineering,2009,29(3):266-273.
[11]  WU Y, THE FDS TEAM. Design analysis of the China dual-functional lithium lead (DFLL) test blanket module in ITER[J]. Fusion Engineering and Design,2007,82(15-24):1893-1903.
[12]  LUCON E, DECRETON M,VAN W E, et al. Mechanical characterisation of irradiated EUROFER97(0.32dpa, 300℃)[J]. Fusion Engineering and Design,2003,69(1-4):373-377.
[13]  STEVEN J ZINKLE. Advanced materials for fusion technology[J].Fusion Engineering and Design,2005,74(1-4):31-40.
[14]  刘宗昌,任慧平,王海燕.奥氏体形成与珠光体转变[M].北京:冶金工业出版社,2010.104-121.
[15]  刘宗昌,计云萍,任慧平.贝氏体相变理论研究新进展[J].内蒙古科技大学学报,2012,31(1):34-43. LIU Zong-chang,JI Yun-ping,REN Hui-ping. Latest advance in theoretical study on bainite phase transformation[J]. Journal of Inner Mongolia University of Science and Technology,2012,31(1):34-43.
[16]  CABALLERO F G,MILLER M K,BABU S S,et al. Atomicscale observations of bainite transformation in a high carbon high silicon steel[J]. Acta Materialia,2007,55(1):381-390.

Full-Text

Contact Us

service@oalib.com

QQ:3279437679

WhatsApp +8615387084133