铝合金硬阳极化膜的耐磨试验
Keywords: 硬阳极化膜 ,耐磨试验
Abstract:
评述了关于铝合金硬阳极化膜耐磨试验的三种试验方法,即轮式磨损试验法,喷磨试验法和Taber耐磨试验法,着重评述了Taber试验法的各种影响因素。
References
[1] 1 S.Wernicketal.The Surface Treatment and Finishing of Aluminu mandits Alloys.Fif thedition.ASM International Metals Park Chil U.S.A,1987 [2] 2 ISO8251:1987,Anodized Aluminum and Aluminum Alloys-Measurement of Wear Resistance and Wear Indixof Anodic Oxide Coatings with Abresive Wheel Wear Test Apparatus [3] 3 ISO8252:1987,Andized Aluminum and Aluminum Alloys-Measurement of Mean Specific Abrasion Resistance of Anodic Oxidation Coatings with an Abrasive Jet Test Apparatus [4] 4 GB/T.12967.2-91,铝及铝合金阳极化-用轮式损试验仪测定阳极氧化膜的耐磨性和磨损系数 [5] 5 G B/T,12967.1-91,铝及铝合金阳极化-用喷磨试验仪测定阳极氧化膜的平均耐磨性 [6] 6 R.T.Hitchcook.Trns Inst Metal Finish,1991,69(3):100 [7] 11 朱祖芳.铝阳极氧化膜(建筑装饰用)性能及检测方法.国家有色金属材料质量检测中心,铝阳极氧化技术标准资料之一:“铝阳极氧化性能检测”,1994 [8] 12 FEDTEST,STDNO.141C Method 192.1,Abrasion Resis tance(Taber Abraser).1986 [9] 13 A STMD4060-95,Standard Test Method for Abrasion Resistance of Organic Coatings by the Taber Abraser [10] 14 ISO10074-1994,Specification for Hard Anodic Oxidation Coatingson Aluminium and Its Alloys,AnnexB(Normative),Taber Abrasion Test Method [11] 15 R.W.Thomas.Turns IFM,1981,59:97 [12] 16 G.C.Tuand L.Y.Huang.Trans.IMF,1987,65:60 [13] 17 M.Lerner.Plating and Surface finishing,1979,656(12):401 [14] 18 Douglas Process Standard DPS 11.04.M,1990,Hard Anodizing Aluminum [15] 19 Boeing Process Specification BAC5821C,1981,Hard Anodizing [16] 20 D.J.George and J.H.Powers.Plating,1969,56(11):1240 [17] 21 M IL-A-8625F,1993,Anodic Coatings,for Aluminum and Aluminum Alloy [18] 7 C.A.Wittand G.Giken.Aluminium,1971,47(12):748 [19] 8 T.N adayama and K.H agasaka.Proc.of 10th World Congresson Metal Finishing(S.Harugara Ed.),1980,Kakgo,Japan [20] 9 张凤林.轻合金加工技术,1989(6):40 [21] 10 何克明,续玉琛.电镀与精饰,1988,10(1):43
Full-Text
Contact Us
service@oalib.com
QQ:3279437679
WhatsApp +8615387084133