钢渣碳化机理研究
Abstract:
通过测定钢渣碳化反应中的温度变化,分析钢渣碳化产物的矿物相,以及测试碳化前后钢渣的热重及孔结构变化,研究钢渣碳化的放热性能和结构组成变化。结果表明钢渣水化24h累计放热量为30J/g,而钢渣试样碳化1h的累计放热总量达95J/g。碳化后的钢渣试样中有碳酸盐矿物生成,每kg钢渣约可固化储存CO2气体121.8g,并且试样的孔隙率由碳化前的21.76%降至13.34%,抗压强度由碳化前的6.69MPa提高至42.14MPa,且碳化后试样压蒸安定性合格。
| [1] | 唐明述,袁美栖,韩苏芬.钢渣中MgO、FeO、MnO的结晶状态与钢渣的体积安定性[J].硅酸盐学报,1979,7(1):35-46.TANG Mingshu,YUAN Meixi,HAN Fenfang.J Chin Ceram Soc(in Chinese),1979,7(1):35-46. [2]常钧,WANG Sanwu,SHAO Yixin.碳化养护电弧熔炉矿渣制备混凝土的研究[J].硅酸盐学报,2007,35(9):1264-1269.CHANG Jun,WANG Sanwu,SHAO Yixin.J Chin Ceram Soc(in Chinese),2007,35(9):14-19. [3]BERTOS M Fernández,SIMONS S J R,HILLS C D,et al.A review of accelerated carbonation technology in the treatment of cement-based materials and sequestration of CO2[J].J Hazardous Mater,2004,112(1):193-205. [4]WU Haoze,CHANG Jun.Carbonate steelmaking slag to manufacture building materials[J].Adv Mater Res,2009,79(1):1943-1946. [5]吴昊泽,张林菊,叶正茂,等.水分对钢渣碳化的影响[J].济南大学学报:自然科学版,2009,23(3):218-222.WU Haoze,ZHANG Linju,YE Zhengmao.J Univ Jinan:Sci&Tech(in Chinese),2009,23(3):218-222. [6]林传仙.矿物及有关化合物热力学数据手册[M].北京:科学出版社,1985:200-240.LING Chuanxian.Thermodynamic Data of Minerals and Related Com-pounds(in Chinese),Beijing:Science Press,1985. [7]印永嘉.物理化学简明教程[M].北京:高等教育出版社,2002:120-190.YIN Yongjia.Physical and Chemistry Course(in Chinese),Beijing:Higher Education Press,2002:120-190. [8]姚晓,唐明述.油井水泥石CO2腐蚀的热力学条件[J].油田化学,1999,16(1):10-13.YAO Xiao,TANG Mingshu.Oilfield Chem(in Chinese),1999,16(1):10-13. [9]王宗华,张军营,徐俊.CO2矿物碳化隔离的理论研究[J].工程热物理学报,2008,26(6):1063-1068.WANG Zonghua,ZHANG Junying,Xu Jun.J Eng Thermo Phys(in Chinese),2008,26(6):1063-1068. [10]王强,阎培渝.大掺量钢渣复合胶凝材料早期水化性能和浆体结构[J].硅酸盐学报,2008,36(10):1406-1410.WANG Qiang,YAN Peiyu.J Chin Ceram Soc(in Chinese),2008,36(10):1406-1410. [12]侯贵华,李伟峰,郭伟.转炉钢渣的显微形貌及矿物相[J].硅酸盐学报,2008,36(4):436-443.HOU Guihua,LI Weifeng,GUO Wei.J Chin Ceram Soc(in Chinese),2008,36(4):436-443. [11]杨南如.无机非金属材料图谱手册[M].武汉:武汉工业大学出版社,2000:20-150.YANG Nanru.The handbook of Inorganic Metalloid Materials Atlas(in Chinese),Wuhan:Wuhan Industrial University Press,2000:20-150.
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|