聚氨酯改性不饱和聚酯/色浆复合体系的固化特性
DOI: 10.3724/SP.J.1105.2013.13075
Keywords: 聚氨酯改性不饱和聚酯树脂 ,色浆 ,固化特性 ,黏附力
Abstract:
系统研究了聚氨酯改性不饱和聚酯/色浆复合体系的黏度与固化特性,发现随着色浆含量的增加,复合体系的黏度呈递增趋势,但明显低于理论加和值;而复合体系的凝胶时间、表观起始固化温度与表观峰值固化温度随着色浆含量的增加而增加,但表观终止固化温度与固化热焓却降低;随着升温速率的增大,复合体系的特征固化温度均向高温方向移动,但固化热焓基本不变.将升温速率外推至零,可计算出体系的起始固化温度、峰值固化温度以及终止固化温度,从而确定体系的固化工艺.同时基于不同升温速率下的表观峰值固化温度,通过Kissinger方程可计算得到聚氨酯改性不饱和聚酯/色浆复合体系的固化反应表观活化能以及固化反应动力学指前因子.在最佳固化工艺条件下,聚氨酯改性不饱和聚酯树脂/色浆复合涂层的黏附力均在一级以上.
References
[1] 2 Kanerva M,Saarela O.Int J Adhes Adhes,2013,43:60~69 [2] 13 Xie X L,Tjong S C,Li R K Y.J Appl Polym Sci,2000,77:1975~1988 [3] 1 Akil H M, Omar M F,Mazuki A A M,Safiee S,Ishak Z A M,Abu Bakar A.Mater Des,2011,32(8-9):4107~4121 [4] 3 Urena-Benavides E E,Kayatin Matthew J,Davis V A.Macromolecules,2013,46(4):1642~1650 [5] 4 Liu Jingcheng(刘敬成),Jia Xiuli(贾秀丽),Zhang Shengwen(张胜文),Liu Ren(刘仁),Jiang Jinqiang(江金强),Liu Xiaoya(刘晓亚).Polymer Materials Science and Engineering(高分子材料科学与工程),2011,27(8):87~90 [6] 5 Yu Zaiqian(于在乾),Feng Wenping(冯文平),Zhang Long(张龙).Polymer Materials Science and Engineering(高分子材料科学与工程),2012,28(11):158~165 [7] 6 Xu Meixuan(许美萱),Xiao Jingsong(肖景松),Guan Yunlin(管云林).Acta Polymerica Sinica(高分子学报),1995,(4):453~458 [8] 7 Li W,Lee L J.Polymer,2000,41(2):697~710 [9] 8 Singh B,Gupta M,Randhawa A,Tyagi S,Sharma S.J Appl Polym Sci,2011,122(2):1206~1218 [10] 9 Duan H J,Zhang L M,Wang J,Yang X L,Wang X.Journal of Wuhan Unversity of Technology-Materials Science Edtion(武汉理工大学学报),2009,24(4):627~630 [11] 10 Lin Y,Jin J,Song M,Shaw S J,Stone C A.Polymer,2011,52(8):1716~1724 [12] 11 Martin J L.Polym Eng Sci,2007,47:62~70 [13] 12 Wang J,Fang X,Wu M Q,He X Y,Liu W B,Shen X D.Eur Polym J,2011,47(11):2158~2168 [14] 14 Polios I S,Lee C,Gido S P,Schmidtrohr K,Winter H H,Soliman M.Macromolecules,1997,30(15):4470~4480 [15] 15 Zhou Y,Yang X Y,Jia D M.Polym Int,2007,56:267~271 [16] 16 Puci? I,Ranogajec F.Radiat Phys Chem,2003,67:415~419 [17] 17 Delahaye N,Marais S,Saiter M,Metayer M J.Appl Polym Sci,1998,67:695~703 [18] 18 Simitzis J,Zoumpoulakis L,Soulis S.Polym Int,2002,51:308~318 [19] 19 Li L,Cao X,Lee L J.Polymer,2004,45:6601~661220 Min K E,Hwang Y G,Choi G Y,Kim H G,Kim W S,Lee D H,Park L S,Seo K H,Kang I K,Jun I R,Lim J C,Song H C.J Appl Polym Sci,2002,84:735~740
Full-Text
Contact Us
service@oalib.com
QQ:3279437679
WhatsApp +8615387084133