氧化锌多孔微米花的制备及其气敏性能研究
DOI: 10.6023/A13121212, PP. 433-439
Keywords: 氧化锌,多孔材料,气敏性能,共沉淀法,纳米材料
Abstract:
具有大比表面积和丰富表面缺陷的三维多孔纳米材料在气体传感中极具潜力.通过液相共沉淀法制备了三维微米花状锌基前驱物，于400℃热处理即转化为ZnO多孔微米花，它继承了锌基前驱物的外观形貌，但片状“花瓣”的表面形成大量无序孔洞，使得ZnO多孔微米花具有大比表面积（31.3m2·g-1）和丰富的表面缺陷.鉴于ZnO多孔微米花的独特微观形貌结构，用其构建的气体传感器对乙醇气体表现出最佳工作温度低、灵敏度高、响应（恢复）快速等优点，与文献报道的ZnO基乙醇气体传感器相比处于领先水平.结合其制备过程简单、成本低等优点，ZnO多孔微米花在气体传感领域有潜在的应用价值.
| [1] | Son, J. Y.; Lim, S. J.; Cho, J. H.; Seong, W. K.; Kim, H. Appl. Phys. Lett. 2008, 93, 053109.
|
| [2] | Gui, Z.; Liu, J.; Wang, Z. Z.; Song, L.; Hu, Y.; Fan, W. C.; Chen, D. Y. J. Phys. Chem. B 2005, 109, 1113.
|
| [3] | Xiong, J. F.; Shen, H.; Mao, J. X.; Qin, X. T.; Xiao, P.; Wang, X. Z.; Wu, Q.; Hu, Z. J. Mater. Chem. 2012, 22, 11927.
|
| [4] | Huang, M. H.; Mao, S.; Feick, H.; Yan, H. Q.; Wu, Y. Y.; Kind, H.; Weber, E.; Russo, R.; Yang, P. D. Science 2001, 292, 1897.
|
| [5] | Wang, Z. L.; Song, J. H. Science 2006, 312, 242.
|
| [6] | Wang, Z. L. Adv. Mater. 2012, 24, 4632.
|
| [7] | Law, M.; Greene, L. E.; Johnson, J. C.; Saykally, R. J.; Yang, P. D. Nat. Mater. 2005, 4, 455.
|
| [8] | Gao, T.; Wang, T. H. Appl. Phys. A 2005, 80, 1451.
|
| [9] | Feng, X. J.; Feng, L.; Jin, M. H.; Zhai, J.; Jiang, L.; Zhu, D. B. J. Am. Chem. Soc. 2004, 126, 62.
|
| [10] | Vayssieres, L. Adv. Mater. 2003, 15, 464.
|
| [11] | Arnold, M. S.; Avouris, P.; Pan, Z. W.; Wang, Z. L. J. Phys. Chem. B 2003, 107, 659.
|
| [12] | Kuo, C. L.; Kuo, T. J.; Huang, M. H. J. Phys. Chem. B 2005, 109, 20115.
|
| [13] | Li, J.; Fan, H.; Jia, X. J. Phys. Chem. C 2010, 114, 14684.
|
| [14] | Greene, L. E.; Law, M.; Goldberger, J.; Kim, F.; Johnson, J. C.; Zhang, Y. F.; Saykally, R. J.; Yang, P. D. Angew. Chem., Int. Ed. 2003, 42, 3031.
|
| [15] | Pan, Z. W.; Dai, Z. R.; Wang, Z. L. Science 2001, 291, 1947.
|
| [16] | Zheng, J. H.; Zhang, X. K.; Lu, H. F. Acta Chim. Sinica 2011, 69, 2434. (郑建华, 张晓凯, 卢慧粉, 化学学报, 2011, 69, 2434.)
|
| [17] | Bai, H. Y.; Bao, J. C.; Dai, Z. H.; Liu, K. Acta Chim. Sinica 2008, 66, 1786. (白红艳, 包建春, 戴志晖, 刘可, 化学学报, 2008, 66, 1786.)
|
| [18] | Zhang, N.; Yu, K.; Li, Q.; Zhu, Z. Q.; Wan, Q. J. Appl. Phys. 2008, 103, 104305.
|
| [19] | Law J. B. K.; Thong, J. T. L. Nanotechnology 2008, 19, 205502.
|
| [20] | Jing, Z. H.; Zhan, J. H. Adv. Mater. 2008, 20, 4547.
|
| [21] | Zuruzi, A. S.; MacDonald, N. C.; Moskovits, M.; Kolmakov, A. Angew. Chem., Int. Ed. 2007, 46, 4298.
|
| [22] | Chen, M.; Wang, Z.; Han, D.; Gu, F.; Guo, G. J. Phys. Chem. C 2011, 115, 12763.
|
| [23] | Zhang, H.; Wu, J. B.; Zhai, C. X.; Du, N.; Ma, X. Y.; Yang, D. R. Nanotechnology 2007, 18, 455604.
|
| [24] | Lee, J. H. Sens. Actuators, B 2009, 140, 319.
|
| [25] | Fu, M.; Zhou, J.; Xiao, Q. F.; Li, B.; Zong, R. L.; Chen, W.; Zhang, J. Adv. Mater. 2006, 18, 1001.
|
| [26] | Ding, G. Q.; Shen, W. Z.; Zheng, M. J.; Fan, D. H. Appl. Phys. Lett. 2006, 88, 103106.
|
| [27] | Zhang, W. X.; Yanagisawa, K. Chem. Mater. 2007, 19, 2329.
|
| [28] | Song, R. Q.; Xu, A. W.; Deng, B.; Chen, G. Y. Adv. Funct. Mater. 2007, 17, 296.
|
| [29] | Korotcenkov, G.; Han, S. D.; Cho, B. K.; Brinzari, V. Critical Rev. Solid State Mater. Sci. 2009, 34, 1.
|
| [30] | Waitz, T.; Becker, B.; Wagner, T.; Sauerwald, T.; Kohl, C. D.; Tiemann, M. Sens. Actuators, B 2010, 150, 788.
|
| [31] | Wu, Q.; Chen, J. X.; Zhang, F.; Xiao, P.; Lu, Y. N.; Wang, X. Z.; Hu, Z. CrystEngComm 2012, 14, 3397.
|
| [32] | Liu, J. F.; Wang, X.; Peng, Q.; Li, Y. D. Adv. Mater. 2005, 17, 764.
|
| [33] | Wang, J. X.; Sun, X. W.; Yang, Y.; Huang, H.; Lee, Y. C.; Tan, O. K.; Vayssieres, L. Nanotechnology 2006, 17, 4995.
|
| [34] | Wang, X. Z.; Liu, W.; Liu, J. R.; Wang, F. L.; Kong, J.; Qiu, S.; He, C. Z.; Luan, L. Q. ACS Appl. Mater. Interfaces 2012, 4, 817.
|
| [35] | Wang, L. W.; Kang, Y. F.; Liu, X. H.; Zhang, S. M.; Huang, W. P.; Wang, S. R. Sens. Actuators, B 2012, 20, 237.
|
| [36] | Chen, J.; Li, J.; Li, J. H.; Xiao, G. Q.; Yang, X. F. J. Alloys Compd. 2011, 509, 740.
|
| [37] | Ahn, H.; Park, J. H.; Kim, S. B.; Jee, S. H.; Yoon, Y. S.; Kim, D. J. Electrochem. Solid-State Lett. 2010, 13, J125.
|
| [38] | Zhang, Z. Y.; Li, X. H.; Wang, C. H.; Wei, L. M.; Liu, Y. C.; Shao, C. L. J. Phys. Chem. C 2009, 113, 19397.
|
| [39] | Zhang, J.; Wang, S. R.; Xu, M. J.; Wang, Y.; Zhu, B. L.; Zhang, S. M.; Huang, W. P.; Wu, S. H. Cryst. Growth Des. 2009, 9, 3532.
|
| [40] | Wan, Q.; Li, Q. H.; Chen, Y. J.; Wang, Y. H.; He, X. L.; Li, J. P.; Lin, C. L. Appl. Phys. Lett. 2004, 84, 3654.
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|