连铸温度和低倍组织对轮箍钢氢致开裂的影响
, PP. 149-153
Keywords: 轮箍,低倍组织,连铸温度,氢致开裂,白点
Abstract:
研究了轮箍低倍组织和连铸温度对白点敏感性、断裂韧性和氢致开裂门槛值的影响。结果表明，连铸温度对白点敏感性有影响，尾坯（低温）的白点敏感性略高于头坯（高温）。低倍组织对白点敏感性影响显著，柱状晶区的白点敏感性最低，等轴晶区的白点敏感性最高。但是，低倍组织和连铸温度对氢扩散、条件断裂韧性KIQ以及氢致开裂门槛值KIH均没有影响。
| [1] | PPollard M G.Proc Inst Eng,1999;213F:181
|
| [2] | MMclellan R R,Xu Z R.Scr Mater,1997;36:1201
|
| [3] | CChu W Y.Hydrogen Damage and Hydrogen-Induced Delayed Fracture.Beijing:Metallurgical Industry Press,1988:146(褚武扬．氢损伤与滞后断裂．北京：冶金工业出版社，1988：148)
|
| [4] | IInterrante C G.Current Solution to Problems in Steels.Metals Park,OH:ASM,1982:2
|
| [5] | PPressourye G M.Current Solution to Problems in Steels.Metals Park,OH:ASM,1982:18
|
| [6] | SSteiner J E.Current Solution to Problems in Steels.Metals Park,OH:ASM,1982:55
|
| [7] | OOriani R A,Hirth J P,Smialowski M.Hydrogen Degradation of Ferrous Alloys,Park Ridge,N J:Noyes Pub,1985:218
|
| [8] | FFruehan R T.Iron Steel Maker,1997;24:61
|
| [9] | RRen X C,Chu WY,Li J X,Qiao L J,Jiang B,Chen G,Cui Y H.Acta Metall Sin,2006;42:273(任学冲，褚武扬，李金许，乔利杰，江波，陈刚，崔银会．金属学报，2006；42：273)
|
| [10] | Ren X C,Shan G G,Chu WY,Su Y J,Gao K W,Qiao L J,Jiang B,Chen G,Cui Y H.Chin Sci Bull,2005;50:1962
|
| [11] | Peng X,Su Y J,Gao K W,Qiao L J,Chu W Y.Mater Lett,2004;58:2073
|
| [12] | Ren X C,Chu W Y,Li J X,Qiao L J,Jiang B,Chcn G,Cui Y H.Acta Metall Sin,2006;42:153(任学冲，褚武扬，李金许，乔利杰，江波，陈刚，崔银会．金属学报，2006；42：153)
|
| [13] | Hodge J M,Orehoski M A,Steiner J E.Trans Metall Soc AIME,1964;230:1182
|
| [14] | Allen A O.Probability,Statistics and Queuing Theory,New York:Academic Press,1978:293
|
| [15] | Wu M,Chu W Y,Li J X,Jiang B,Chen G,Cui Y H.Acta Metall Sin.2006:42:815(武明，褚武扬，李金许，江波，陈刚，崔银会．金属学报，2006；42：815)
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|