粗晶奥氏体HTP钢中形变诱导析出的定量研究
, PP. 791-796
Keywords: 含铌钢,粗晶奥氏体,形变,析出
Abstract:
利用double-hit实验与场发射扫描电镜定量研究了低碳高铌钢(0.032%C-0.089%Nb,HTP钢)粗晶奥氏体(约800μm)中的形变诱导Nb(C,N)析出规律.结果表明,在1000—900℃温度区间变形时,随着形变温度的降低,析出开始(5%析出量)时间逐渐缩短,析出开始时间与温度关系曲线具有C曲线的特征.随着形变温度的降低,析出相颗粒密度逐渐增加而颗粒直径减小,析出动力学满足修正的Avrami方程,Avrami指数约为1.1.出相主要在位错及位错结等位置优先形核,形成条带状或网状.拟合得到的模型能够预测奥氏体低碳高铌钢中的析出开始时间及析出动力学.
| [1] | YYu H,Kang Y L,Dong H B.Acta Metall Sin(Engl Lett), 2002;15:375
|
| [2] | FFlemming G,Hensger K E.MPT Int,2000;(1):54
|
| [3] | ZZhang L,Yang W Y,Zheng W W,Sun Z Q.J Univ Sci Technol Beijing Eng Ed,2005;12:517
|
| [4] | HHumbert M,Gardiola B,Esling C.Acta Mater,2002;50: 1741
|
| [5] | LLi Y,Crowther D N,Mitchell P S.ISIJ Int,2002;42:636
|
| [6] | CCobo SJ,Sellars C M.Ironmaking Steelmaking,2001;28: 230
|
| [7] | KKopp R,Nutzmann M,Ziegelmayer O.Steel Res,2002; 73:321
|
| [8] | KKaspar R.Steel Res,2003;74:318
|
| [9] | KKaspar R,Fl(?)βP.Steel Res,1991;62:501
|
| [10] | Kamada Y,Hashimoto T,Watanabe S.ISIJ Int,1990;30: 241
|
| [11] | Liu Q Y,Dong H,Sun X J.Iron Steel,2003;38(8):16 (刘清友，董瀚，孙新军．钢铁，2003；38(8)：16)
|
| [12] | Li D G,Wang X L,Liu Q Y.Iron Steel,2004;39(5):55 (李德刚，王雪莲，刘清友．钢铁，2004；39(5)：55)
|
| [13] | Hulka K,Bordignon P,Gray M.Microalloy Technol,2006; 6(2):1
|
| [14] | Stalheim D G,Barnes K R,McCutcheon D B.Microalloy Technol,2006;6(2):15
|
| [15] | Bordignon P,Hulka K.Microalloy Technol,2006;6(2):45
|
| [16] | Kang K B,Kwon O,Lee W B,Park C G.Scr Mater,1997; 36:1303
|
| [17] | Hong S G,Kang K B,Park C G.Scr Mater,2002;46:163
|
| [18] | Zhang L,Yang W Y,Zheng W W,Sun Z Q.Iron Steel, 2005;40(6):40 (张玲，杨王玥，郑为为，孙祖庆．钢铁，2005；40(6)：40)
|
| [19] | Gladman T,Dulieu D,Mcivor I D.Proc Int Symp on High-Strength-Low-Alloy Steels,New York:Union Car- bide Corporation,1977:32
|
| [20] | Dutta B,Valdes E,Sellars C M.Acta Mater,1992;40: 653
|
| [21] | Valdes E,Sellars C M.Mater Sci Technol,1991;7:622
|
| [22] | Hansen S S,Vander Sande J B,Cohen M.Metall Trans, 1980;11A:387
|
| [23] | Zurob H S,Hutchinson C R,Brechet Y.Acta Mater,2002; 50:3075
|
| [24] | Le Bon A,Rofes-Vernis J,Rossard C.Metall Sci,1975; 19:36
|
| [25] | Pereloma E V,Crawford B R,Hodgson P D.Mater Sci Eng,2001;A299:27
|
| [26] | Dutta B,Sellars C M.Mater Sci Technol,1987;3:197
|
| [27] | Medina S F,Hernandez C A.Acta Mater,1996;44:137
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|