深过冷铁钴基块体合金的细晶化研究
DOI: 10.3724/SP.J.1037.2012.00286, PP. 1409-1414
Keywords: 铁钴基块体合金,深过冷,Cu模吸铸,凝固组织,晶粒细化
Abstract:
采用熔融玻璃净化与循环过热相结合的深过冷技术,对比研究了深过冷凝固和过冷熔体Cu模激冷凝固Fe44Co44Nb7B4Cu1块体合金的组织特征.结果表明,随过冷度增大,深过冷和深过冷Cu模激冷凝固组织均由最初的发达树枝晶逐渐演变为细小的粒状晶,并且Cu模激冷可显著减小树枝晶向粒状晶转变的临界过冷度.在相同过冷度下,过冷熔体Cu模激冷凝固组织更加细小均匀,其根本原因在于Cu模激冷和熔体深过冷的双重作用不仅提高了熔体的形核率并抑制了晶粒长大,而合金化元素在晶界聚集并不是阻碍晶粒长大的主要原因.
| [1] | Herlach D M, Eckler K, Karma A, Schwarz M. Mater Sci Eng, 2001; A304-306: 20
|
| [2] | Liu N, Liu F, Yang G C, Chen Y Z, Yang C L, Li J S,Zhou Y H. J Alloys Compd, 2008; 455: L6
|
| [3] | Liu N, Yang G C, Chen Y Z, Zhou Y H. Prog Nat Sci,2006; 16: 120(刘宁, 杨根仓, 陈豫增, 周尧和. 自然科学进展, 2006; 16: 120)
|
| [4] | Han Y, Yang C L, Liu F, Sang G L, Jiang Y H. Foundry Technol, 2011; 32: 453(韩 野, 杨长林, 刘 峰, 桑国良, 姜伊辉. 铸造技术, 2011; 32: 453)
|
| [5] | Herlach D M. Mater Sci Eng, 1994; R12: 177
|
| [6] | Hayzelden C, Rayment J J, Cantor B. Acta Metall, 1983;31: 379
|
| [7] | Boettinger W J, Coriell S R, Trivedi R. Rapid Solidification Processing. 4th Ed., Baton Rouge La: Claitor’s Publishing Division, 1988: 13
|
| [8] | Liu N, Yang G C, Liu F, Chen Y Z, Yang C L, Zhou Y H. Acta Metall Sin, 2007; 43: 449(刘宁, 杨根仓, 刘峰, 陈豫增, 杨长林, 周尧和. 金属学报, 2007; 43: 449)
|
| [9] | Liu N, Liu F, Yang G C, Chen Y Z, Chen D, Yang C L, Zhou Y H. Physica, 2007; 387B: 151
|
| [10] | Hermann R, Loser W. J Magn Magn Mater, 2002; 242-245: 285
|
| [11] | Liu N, Yang G C, Liu F, Yang C L. Chin J Mater Res,2010; 24: 525(刘宁, 杨根仓, 刘峰, 陈豫增, 杨长林. 材料研究学报, 2010; 24: 525)
|
| [12] | Li M J, Xue Y F, Song G S, Yang G C, Zhou Y H. Acta Metall Sin, 1999; 35: 517(李明军, 薛玉芳, 宋广生, 杨根仓, 周尧和. 金属学报, 1999; 35: 517)
|
| [13] | Hayzelden C, Rayment J J, Cantor B. Acta Metall, 1983;31: 379
|
| [14] | Aziz M J. J Appl Phys, 1982; 53: 1158
|
| [15] | Burke J E. Trans Met Soc AIME, 1949; 175: 73
|
| [16] | Michels A, Krill C E, Ehrhrdt H, Birringer R, Wu D T. Acta Mater, 1999; 47: 2143
|
| [17] | Li J J, Wang J C, Yang G C. Scr Mater, 2009; 60: 945
|
| [18] | Zhu M, Wu Z F, Zeng M Q, Ouyang L Z, Gao Y. J Mater Sci, 2008; 43: 3259
|
| [19] | Natter H, Schmelzer M, Lo1ffler M S, Krill C E, Fitch A, Hempelmann R. J Phys Chem, 2000; 104B: 2467
|
| [20] | Jackson K A, Hunt J D, Uhlmann D R, Stewart T P. TMS-AIME, 1966; 236: 149
|
| [21] | Karma A. Int J Non-Equilib Process, 1998; 11: 201
|
| [22] | Liu F, Yang G C. J Cryst Growth, 2001; 231: 295
|
| [23] | Liu F, Guo X F, Yang G C. Chin J Mater Res, 2001; 15:269(刘峰, 郭学锋, 杨根仓. 材料研究学报, 2001; 15: 269)
|
| [24] | Piccone T J, Wu Y, Shiohara Y, Flemings M C. Mater Trans, 1987; 18A: 925
|
| [25] | Li M J, Lin X, Song G S, Yang C L, Zhou Y H. Mater Sci Eng, 1999; A268: 90
|
| [26] | Li M J. PhD Thesis, Northwestern Polytechnical University, Xi’an, 1999(李明军. 西北工业大学博士学位论文, 西安, 1999)
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|