17%Cr铁素体不锈钢中的第二相与织构
DOI: 10.3724/SP.J.1037.2012.00173, PP. 1166-1174
Keywords: 17%Cr铁素体不锈钢,析出相,织构,再结晶
Abstract:
通过工艺控制得到了不同尺寸及分布特征的析出相,研究了其对再结晶织构的影响.结果表明降低精轧温度有利于尺寸更加细小、分布更加弥散的析出相TiC的形成,经冷轧及退火后这种析出相分布特征可遗传至冷轧退火板;粗大、稀疏析出相的样品具有较强的γ纤维再结晶织构;细小、弥散的析出相有助于随机取向再结晶晶核的形成,抑制再结晶晶粒的长大,从而弱化了γ纤维再结晶织构及恶化了冷轧退火板成形性能;析出相对随机取向晶粒形核的作用及晶界迁移的钉扎作用是控制铁素体不锈钢再结晶织构的重要因素之一.
| [1] | Barnett M R, Jonas J J. ISIJ Int, 1997; 37: 697
|
| [2] | Pandit A, Murugaiyan A, Saha Podder A, Haldar A, Bhattacharjee D, Chandra S, Ray R K. Scr Mater, 2005; 53: 1309
|
| [3] | Sun W P, Militaer M, Jonas J J. Metall Trans, 1992; 23A: 821
|
| [4] | Chang S K, Kang H J. Steel Res Int, 1995; 66: 463
|
| [5] | Liu H T. PhD Thesis, Northeastern University, Shenyang, 2009
|
| [6] | Yazawa Y, Ozaki Y, Kato Y. JSAE Rev, 2003; 24: 483
|
| [7] | Liu H T, Liu Z Y, Wang G D. ISIJ Int, 2009; 49: 890
|
| [8] | Miyamoto H, Xiao T, Uenoya T, Hatano M. ISIJ Int, 2010; 50: 1653
|
| [9] | Siqueira R P, Sandim H R Z, Oliveira T R. Mater Sci Eng, 2008; A497: 216
|
| [10] | Zhang C, Liu Z Y,Wang G D. J Mater Process Tech, 2011; 211: 1051
|
| [11] | Almagro J F, Llovet X, Heredia M A, Luna C, Sanchez R. Microchim Acta, 2008; 161: 323
|
| [12] | Raabe D, L¨ucke K. Scr Metall, 1992; 27: 1533
|
| [13] | Raabe D, H¨olscher M, Dubke M, Reher F, L¨ucke K. Steel Res, 1993; 64: 359
|
| [14] | Raabe D. J Mater Sci, 1996; 31: 3839
|
| [15] | H¨olscher M, Raabe D, L¨ucke K. Steel Res, 1991; 62: 567
|
| [16] | Raabe D, L¨ucke K. Scr Metall Mater, 1992; 26: 19
|
| [17] | Sinclair C W, Robaut F, Maniguet L, Mithieux J D, Schmitt J H, Brechet Y. Adv Eng Mater, 2003; 5: 570
|
| [18] | Sinclair C W, Mithieux J D, Schmitt J H, Brechet Y. Metall Mater Trans, 2005; 36A: 3205
|
| [19] | Zhang C. PhD Thesis, Northeastern University, Shenyang, 2011
|
| [20] | (张驰. 东北大学博士学位论文, 沈阳, 2011)
|
| [21] | (刘海涛. 东北大学博士学位论文, 沈阳, 2009)
|
| [22] | Gao F, Liu Z Y, Liu H T, Wang G D. Acta Metall Sin (Engl Lett), 2011; 24: 343
|
| [23] | Huh M Y, Engler O. Mater Sci Eng, 2001; A308: 74
|
| [24] | Uematsu Y, Yamazaki Y. Tetsu Hagane, 1992; 78: 632
|
| [25] | Park S H, Kim K Y, Lee Y D, Park C G. ISIJ Int, 2002; 42: 100
|
| [26] | Kang H G, Huh M Y, Park S H, Engler O. Steel Res Int, 2008; 79: 489
|
| [27] | Hamada J, Ono N, Inoue H. ISIJ Int, 2011; 51: 1740
|
| [28] | Liu H T, Ma D X, Liu Z Y, Wang G D. J Iron Steel Res, 2010; 22(8): 31
|
| [29] | (刘海涛, 马东旭, 刘振宇, 王国栋. 钢铁研究学报, 2010; 22(8): 31)
|
| [30] | Satoh S, Obara T, Nishida K, Irie T. Trans ISIJ, 1986; 26: 838
|
| [31] | Huh M Y, Kim H C, Engler O. Steel Res, 2000; 71: 239
|
| [32] | Kubodera H, Inagaki H. Bull Jpn Inst Met, 1986; 7: 383
|
| [33] | Satoh S, Obara T, Tsunoyama K. Trans ISIJ, 1986; 26: 737
|
| [34] | Subramaniam S V, Prikryl M, Gaulin B D, Clifford D D, Benincasa S, Reilly I O’. ISIJ Int, 1994; 34: 61
|
| [35] | Zener C, Smith S C. Trans AIME, 1984; 175: 47
|
| [36] | Verbeken K, Kestens L, Jonas J J. Scr Mater, 2003; 48: 1457
|
| [37] | Ray R K, Jonas J J, Hook R E. Int Mater Rev, 1994; 39: 129
|
| [38] | Pereloma E V, Gazder A A, Jonas J J, Miller M K, Davies C H J. ISIJ Int, 2008; 48: 1443
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|