镍基单晶高温合金杂晶形成倾向性的研究

DOI: 10.3724/SP.J.1037.2012.00261, PP. 1229-1236

Keywords: 镍基高温合金,定向凝固,杂晶,过冷度

Full-Text   Cite this paper   Add to My Lib

Abstract:

采用2种不同平台尺寸的模型试样,对镍基单晶高温合金定向凝固过程中的杂晶形成倾向性进行量化研究,对不同合金的杂晶形成倾向性及杂晶在平台内的形成机制进行探索.结果表明,平台长度越长、高度越小时,杂晶越容易在平台内形核并长大;在第一、二、三代镍基单晶高温合金SRR99,DD5和DD90中,第一代合金的杂晶形成倾向性最弱,第二代次之,第三代最强;凝固时平台尖角处的过冷度大于平台内部的过冷度,且随着平台长度增加和平台高度减小,平台尖角处的过冷度增大,当平台尖角处的过冷度达到临界形核过冷度时,杂晶在平台尖角处形核并快速长大进入平台内部.

References

[1]  Yang X L, Dong H B, Wang W, Lee P D. Mater Sci Eng, 2004; A386: 129
[2]  Rappaz M, Gandin C A, Desbiolles J L, Thevoz P. Metall Mater Trans, 1996; 27A: 695
[3]  Gandin C A, Schaefer R J, Rappaz M. Acta Mater, 1996; 44: 3333
[4]  Pollock T M, Murphy W H, Goldman E H, Uram D L, Tu J S. In: Antolovich S D, Stusrud R W, MacKay R A, Anton D L, Khan T, Kissinger R D, Klarstrom D L eds.,
[5]  Superalloys 1992. Warrendale, PA: TMS, 1992: 125
[6]  Pollock T M, Murphy W H. Metall Mater Trans, 1996; 27A: 1081
[7]  Tin S, Pollock T M. Metall Mater Trans, 2003; 34A: 1953
[8]  D’Souza N, Jennings P A, Yang X L, Dong H B, Lee P D, McLean M. Metall Mater Trans, 2005; 36B: 657
[9]  D’Souza N, Ardakani M G, McLean M, Shollock B A. Metall Mater Trans, 2000; 31A: 2877
[10]  Napolitano R E, Schaefer R J. J Mater Sci, 2000; 35: 1641
[11]  Meyer ter Vehn M, Dedecke D, Paul U, Sahm P R. In: Kissinger R D, Deye D J, Anton D L, Cetel A D, Nathal M V, Pollock T M, Woodford D A, eds., Superalloys 1996.
[12]  Warrendale, PA: TMS, 1996: 471
[13]  Cockcroft S L, Rappaz M, Mitchell A, Fernihough J, Schmalz A. In: Coutsouradis D, Davidson J H, Ewald J, Greenfield P, Khan T, Malik M, Meadowcroft D B, Regis
[14]  V, Scarlin R B, Schubert F, Thornton D V. Proc Materials for Advanced Power Engineering, Liege: Kluwer Academic publishers, 1994: 1145
[15]  Kurz W, Fisher D J. Fundamentals of Solidification. Switzerland: Trans Tech Publications, 1984: 21
[16]  Ma D X, Buhrig-Polaczek A. Metall Mater Trans, 2009; 40B: 738
[17]  Paul U, Sahm P R. Mater Sci Eng, 1993; A173: 49
[18]  Reed R C. The Superalloys Fundamentals and Applications. Cambridge: Cambridge University Press, 2006: 141
[19]  Schafrik R E, Walston S. In: Reed R C, Green K A, Caron P, Gabb T P, Fahrmann M G, Huron E S, Woodard S A, eds., Superalloys 2008. Warrendale, PA: TMS, 2008: 3
[20]  McLean M. Directionally Solidified Materials for High Temperature Service. London: The Metals Society, 1983: 161
[21]  Shalin R E, Svetlov I L, Kachanov E B, Toloraiia V N, Gavrilin O S. Single Crystals of Nickel Superalloys. Moscow: Mocshinostroeniye, 1997: 336
[22]  Fullagar K P L, Broomfield R W, Hulands M, Harris K, Erickson G L, Sikkenga S L. Trans ASME, 1996; 118: 380
[23]  Goulette M J, Spilling P O, Arthey R P. In: Gill M, Kortovich C S, Briknell R H, Kent W B, Radavich J F, eds., Proc 5th International Symposium on Superalloys, Warrendale,
[24]  PA: TMS, 1984: 167
[25]  de Bussac A, Gandin C A. Mater Sci Eng, 1997; A237: 35
[26]  Goldschmidt D, Paul U, Sahm P R. In: Antolovich S D, Stusrud RW, MacKay R A, Anton D L, Khan T, Kissinger R D, Klarstrom eds., Superalloys 1992. Warrendale, PA:
[27]  TMS, 1992: 155
[28]  Napolitano R E, Schaefer R J. Mater Sci, 2000; 35: 1641
[29]  Bussac A D, Gandin C A. Mater Sci Eng, 1997; A237: 35
[30]  Gu J P, Beckermann C, Giamei A. Metall Mater Trans, 1997; 28A: 1533
[31]  Copley S M, Giamei A F, Johnson S M, Hornbecker M F. Metall Trans, 1970; 1: 2193
[32]  Zhou Y Z. Scr Mater, 2011; 65: 281
[33]  Paul U, Sahm P R, Donner A, Goldschm D, Portella P D. Proc 2nd Symposium Materialforschung. Dresden: TUV Rheinland, k¨oln, 1991: 841

Full-Text

Contact Us

service@oalib.com

QQ:3279437679

WhatsApp +8615387084133