Fe-C合金贝氏体相变热力学(LFG模型)
, PP. 33-41
Abstract:
由LFG模型计算贝氏体相变三种可能过程的相变驱动力和KRC的结果基本相近,但在高碳合金显示差别.认为对处理间隙固溶体,LFG模型似略胜一筹.但两个模型所得均以ΔG~(γ→a+Fe_3C)为最大,ΔG~(γ→a+γ_1)次之,ΔG~(γ→a′)最小,ΔG_N~(γ→a′)更远远低于ΔG_N~(γ→a+γ_1)。在Bs(或Bs附近)温度,对x_γ=0.01—0.02;LFG的ΔG~(γ→a+γ_1)为-190—-237Jmol~(-1);对x_γ=0.0235合金,LFG的ΔG~(γ→a′)和ΔG~(a′→a″+Fe_3C)之和仅-181Jmol~(-1).本文再次表明,按热力学,至少在上部温度,贝氏体不可能以切变机制形成.由形核(长大)驱动力的计算证明,亚共析钢共析反应的领先相为铁素体,而过共析钢的领先相为渗碳体.
References
[1] | 1 Hsu TY(Xu Zuyao),Mou Yiwen.In:Marder AR,Goldstein J I,eds.Proc,on Phase Transformations in Ferrous Alloys,TMS-AIME,1984,327
|
[2] | 2 Hsu TY(Xu Zuyao),Mou Yiwen.Acta Metall,1984;32:1469
|
[3] | 3 徐祖耀,牟翊文,金属学报,1985;21:A102
|
[4] | 4 Mou Yiwen,Hsu T Y(Xu Zuyao).Acta Metall,1986;34:325
|
[5] | 5 Fowler R H.Proc Cambridge Phil Soc,1936;32:144
|
[6] | 6 Lacher J R.Proc Cambridge Phil Soc,1937;33:518
|
[7] | 7 Fowler R H,Guggenheim E A.In:Statistical Thermodynamics.Cambridge University Press,1956,426-442.
|
[8] | 8 Aaronson H I,Domain H A,Pound G M.Trans Metall Soc AIME,1966;236:753
|
[9] | 9 Shiflet G J,Bradley J.R,Aaronson H I.Metall Trans,1978;9A:999
|
[10] | 10 Bhadeshia H K D H.Met Sci,1981;15:178
|
[11] | 11 Bhadeshia H K D H.Acta Metall,1980;28:1103
|
[12] | 12 Hsu TY(Xu Zuyao),Chang Hongbing.Acta Metall,1984;32:343
|
[13] | 13 Kaufman L,Clougherty E V,Weiss R J.Acta Metall,1963;11:323
|
[14] | 14 Orr R L,Chipman J.Trans Metall Soc AIME,1967;239:630
|
[15] | 15 1972;109-113
|
[16] | 16 Kanfman L,Radcliffe S V,Cohen M.In:Zackey V F,Aaronson H I,edso,New York:Interscience,1962;313
|
[17] | 17 徐祖耀,马氏体相变与马氏体,科学出版社,1980,258
|
[18] | 18 徐祖耀,金属材料热力学,科学出版社,1980;279
|
[19] | 19 Hsu T Y(Xu Zuyao).J Mater Sci,1985;20:23
|
[20] | 20 Steven W,Haynes A G.J Iorn Steel Inst,1956;183:349[
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|