气体保护熔炼条件下Mg-Gd-Y-Zr合金的夹杂物
DOI: 10.3724/SP.J.1037.2011.00593, PP. 63-69
Keywords: Mg-Gd-Y-Zr合金,夹杂物,气体保护
Abstract:
本文研究了气体保护条件下,常规熔铸的Mg-Gd-Y-Zr合金中夹杂物的形貌、分布及形成原因,并通过计算分析了夹杂物的沉降行为.结果表明,Mg-Gd-Y-Zr合金中有MgO或Y的氧化物为主的球状、簇状、不规则状、线状的复合夹杂物和含熔剂夹杂物,夹杂物的平均尺寸为12.7μm,平均体积分数为0.26%.夹杂物出现的频率随其尺寸增大而急剧减小,尺寸在20μm以下的夹杂物占夹杂物总体积接近85%,尺寸在45μm以下的夹杂物占96%.计算结果表明,夹杂物沉降速率与其尺寸和密度相关;夹杂物密度增大,可使镁合金中夹杂物的最大尺寸减小,计算得到的合金中最大夹杂物的尺寸与实验结果基本一致.
| [1] | Hu H, Luo A. JOM, 1996; 48(10): 47
|
| [2] | Eckert C E. Mod Cast, 1991; (4): 28
|
| [3] | Bakke P, Laulin J A, Provost A, Karlsen D O. In: Huglen R ed., Light Metals 1997. Orlando: Minerals, Metals & Materials Society, 1997: 1019
|
| [4] | Zhang S C, Wei B K, Lin H T. Foundry, 2003; 52: 488
|
| [5] | (张诗昌, 魏伯康, 林汉同. 铸造, 2003; 52: 488)
|
| [6] | Zhao Y, Liu P P, Zhou H. Foundry, 2006; 55: 1085
|
| [7] | (赵宇, 刘盼盼, 周 宏. 铸造, 2006; 55: 1085)
|
| [8] | Han Y F, Liu J R, Shen S J, Huang W D. Foundry Technol, 2006; 27: 613
|
| [9] | (韩英芬, 刘建睿, 沈淑娟, 黄卫东. 铸造技术, 2006; 27: 613)
|
| [10] | Gao L, Chen R S, Han E H. Trans Nonferrous Met Soc China, 2011; 21: 863
|
| [11] | Wang J, Meng J, Zhang D P, Tang D X. Mater Sci Eng, 2007; A456: 78
|
| [12] | He S M, Zeng X Q, Peng L M, Guo X W, Chang J W, Ding W J. Mater Sci Forum, 2007; 546-549: 101
|
| [13] | Guo X T, Li P J, Zeng D B, Liu S X. Trans Nonferrous Met Soc China, 2004; 14: 1295
|
| [14] | (郭旭涛, 李培杰, 曾大本, 刘树勋. 中国有色金属学报, 2004; 14: 1295)
|
| [15] | Zheng Y, Wu G H, Hou Z Q, Chen B, Wang Q L, Ding W J. Foundry, 2010; 59(1): 7
|
| [16] | (蒋亦元. 农业工程学报, 1996; 12(8): 12)
|
| [17] | Chen Z H, Yan H G, Chen J H, Quan Y J, Wang H M, Chen D. Magnesium Alloy. Beijing: Chemical Industry Press, 2004: 10
|
| [18] | (陈振华, 严红革, 陈吉华, 全亚杰, 王慧敏, 陈鼎 编著. 镁合金. 北京: 化学工业出版社, 2004: 10)
|
| [19] | Mi G B, He L J, Li P J, Popel P S, Abaturov I S. Trans Nonferrous Met Soc China, 2009; 19: 1372
|
| [20] | (弭光宝, 何良菊, 李培杰, Popel P S, Abaturov I S. 中国有色金属学报, 2009; 19: 1372)
|
| [21] | Cao Y Q. Master Thesis, Jilin University, Changchun, 2006
|
| [22] | (曹永强. 吉林大学硕士学位论文, 长春, 2006)
|
| [23] | Li Z B. J Mater Metall, 2002; 1: 161
|
| [24] | (李正邦. 材料与冶金学报, 2002; 1: 161)
|
| [25] | Keissling R. Non-Metallic Inclusions in Steel. London: Metals Society, 1978: 47
|
| [26] | Lee S G, Patel G R, Gokhale A M, Sreeranganathan A, Horstemeyer M F. Scr Mater, 2005; 53(7): 851
|
| [27] | Liu G J, Wang Y, Fan Z Y. Mater Sci Eng, 2008; 472A: 251
|
| [28] | Hu B, Peng L M, Yang Y L, DingWJ. Mater Des, 2010; 31: 3901
|
| [29] | Stumphy B, Mudryk Y, Russell A, Herman D, Gschneidner K Jr. J Alloy Compd, 2008; 460: 363
|
| [30] | Yim C D, Kang N E, You B S. Met Mater Int, 2010; 16: 377
|
| [31] | Wang W W, Xu J W, Cao D F. Foundry Technol, 1991; 12(6): 15
|
| [32] | (王薇薇, 徐介文, 曹达富. 铸造技术, 1991; 12(6): 15)
|
| [33] | Lu C, Wu G H, Cai C, Zeng K, Ding W J. Met Form Technol, 2002; 20(5): 5
|
| [34] | (卢晨, 吴国华, 蔡超, 曾 克, 丁文江. 金属成形工艺, 2002; 20(5): 5)
|
| [35] | Liang M J, Wu G H, Ding W J, Wang W. Trans Nonferrous Met Soc China, 2011; 21: 717
|
| [36] | Wang J, Yang Y S, Tong W H. Trans Nonferrous Met Soc China, 2011; 21: 949
|
| [37] | (郑韫, 吴国华, 侯正全, 陈 斌, 王其龙, 丁文江. 铸造, 2010; 59(1): 7)
|
| [38] | Li N, Liu J R, Wang S Q, Shen S J, Huang W D, Pang Y T. Foundry Technol, 2006; 27: 1133
|
| [39] | (李娜, 刘建睿, 王栓强, 沈淑娟, 黄卫东, 逄玉台. 铸造技术, 2006; 27: 1133)
|
| [40] | Zhang J, He L J, Li P J. Foundry, 2005; 54: 665
|
| [41] | (张军, 何良菊, 李培杰. 铸造, 2005; 54: 665)
|
| [42] | Jiang Y Y. Trans Chin Soc Agric Eng, 1996; 12(8): 12
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|