321不锈钢在酸性氯离子溶液中的应力腐蚀开裂机理
, PP. 68-73
Keywords: 应力腐蚀开裂,321不锈钢,阳极溶解
Abstract:
证明了321不锈钢在酸性氯离子溶液中处于活性阳极溶解状态.其应力腐蚀开裂(SCC)无法用钝化膜破裂-再钝化理论或氢脆理论解释,而可能是阳极溶解降低了裂纹尖端金属的开裂强度
| [1] | 1 Hoar T P, Hinse J G. J Iron Steel Inst, 1954; 177: 148
|
| [2] | 2 Rhodes P R. Corrosion, 1969: 25: 462
|
| [3] | 3 Hoar T P, Scully J C. J Electrochem Soc. 1964; 111: 348
|
| [4] | 4 Pugh E N. In: Scully J C ed., The Theory of Stress Corrosion Cracking in Alloys, Brussels: NATO, 1971: 21
|
| [5] | 5 Staehle R W. In: Sculy J C ed., The Theory of Stress Corrosion Cracking in Alloys. Brussels: NATO, 1971: 223
|
| [6] | 6 Uhlig H H. In: Rhodined T N ed., Physical Metallurgy of Stress Corrosion Fracture, New York: Interscience, 1959: 1
|
| [7] | 7 Nielsen N A. In: Rhodined T N ed., Physical Metallrugy of Stress Corrosion. Fracture. New York: Interscience, 1959: 341
|
| [8] | 8 Galvele J R. Corros Sci, 1987; 27: 1
|
| [9] | 9 Jones D A. Metall Trans. 1985; 16A: 1133
|
| [10] | 10 曹楚南.新材料研究--第二届中国材料研讨会论文集,上册,武汉,1988:238
|
| [11] | 11 Fragnani A, Trabanelli G, Zucchi F. Corros Sci, 1984; 24: 917
|
| [12] | 12 Okada F, Hosoi Y, Abe S. Trans Iron Steel Inst Jpn, 1992; 15: 121
|
| [13] | 13 曹楚南,杨乾刚,吕明,林海潮.中国腐蚀与防护学报,1992;12:109
|
| [14] | 14 Zuo J Y, Gu B X, Liu Y P. Corrosion. 1991; 47: 47
|
| [15] | 15 魏学军,周向阳,李劲,刘光磊,柯伟.金属学报,待发表
|
| [16] | 16 罗炳清,吕明,曹楚南,李启中.新材料研究--第二届中国材料研讨会论文集,下册,武汉,1988:367
|
| [17] | 17 Revie R W, Uhlig H H. Corros Sci, 1972: 12: 669
|
| [18] | 18 Revie R W, Uhlig H H. Acta Metall, 1974; 22: 619
|
| [19] | 19 Uhlig H H. J Electrochem Soc, 1976; 22: 619
|
| [20] | 20 Uhlig H H. Corros Sci, 1981; 21: 271
|
| [21] | 21 Kramer I R. Scr Metall, 1974; 8: 1231~
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|