氢致脆断的TEM原位拉伸观察
, PP. 248-256
Keywords: 氢致脆断,微裂纹,透射电镜原位观察,无位错区,３１０不锈钢
Abstract:
通过对预充氢３１０不锈钢薄膜在透射电镜（ＴＥＭ）下的原位拉伸观察，并和不含氢试样的结果相比较，研究了氢在韧－脆转变中的作用及氢致脆断机理．结果表明，预充氢的３１０不锈钢试样在拉伸过程中从裂尖发射大量位错，平衡后形成无位错区（ＤＦＺ）；纳米级微裂纹择优在ＤＦＺ中形核；微裂纹不钝化为空洞，而是通过多个微裂纹的形核及相互连接导致裂纹的脆性扩展．即氢使奥氏体不锈钢由韧变脆的根本原因是氢抑制了ＤＦＺ中纳米级微裂纹向空洞的转化．
| [1] | 1褚武扬著．氢损伤与滞后断裂．北京:冶金工业出版社,19882ChuWY,YaoJ,HsiaoCM．MetallTrans,1984;15A:7293ChuWY,WangHL,HsiaoCM．Corrosion,1984;40:4874QiaoLJ,ChuWY,HsiaoCM．Corrosion,1988;44:505QiaoLJ,ChuWY,HsiaoCM．Corrosion,1987;43:4796RiceJR,ThomsonR．Phil．Mag,1974;29:737ArgonAS．ActaMetall,1987;35:1858ChiaoYH,ClarkeDR．ActaMetall,1989;37:2039陈奇志,褚武扬,肖纪美．中国科学,1994;37A10张跃,王燕斌,褚武扬,肖纪美．ScriptaMetallMater,inPress11CherepanovGP．MechanicsofBrittleFracture,McGraw-HillInt．BookComp,NewYork,1979:2912FriededJ．Dislocations,PergamonPress,Oxford,1964:31213RitchieRO,ThompsonAW．MetallTrans,1985;16A:233P
|